The electrical conductivity and Seebeck coefficient of RuO2 nanosheets are enhanced by metal nanoparticle doping using Ag-acetate solutions. In this study, RuO2 monolayer and bilayer nanosheets exfoliated from layered alkali metal ruthenates are transferred to Si substrates for device fabrication, and the temperature dependence of their conductivity and Seebeck coefficients is investigated. For pristine RuO2 nanosheets, the sign of the Seebeck coefficient changes with temperature from 350-450 K. This indicates that the dominant type of charge carrier is dependent on the temperature, and the RuO2 nanosheets show ambipolar carrier transport behavior. By contrast, the sign of the Seebeck coefficient for Ag nanoparticle-doped RuO2 nanosheets does not change with temperature, indicating that the extra charge carriers from metal nanoparticles promote n-type semiconductor behavior.
RESUMO
The enhancement in electrical transport properties of exfoliated individual RuO2 NSs was systemically investigated for their application in flexible electronics and optoelectronics. Decoration of Ag NPs on the surface of the RuO2 NSs provides donor electrons and dramatically increases the electrical conductivity of the monolayer RuO2 NSs by up to 3700%. The n-type doping behavior was confirmed via Hall measurement analysis of the doped RuO2 NSs. The layer number- and temperature-dependence of the conductivity were also investigated. Moreover, carrier concentration and mobility were obtained from Hall measurements, indicating that the undoped RuO2 NSs had ambipolar transport and semi-metallic characteristics. Moreover, the Ag-doped RuO2 NS multilayer films on polycarbonate substrates were demonstrated by the Langmuir-Blodgett assembly methods, showing one-third reduction in the sheet resistance and extraordinarily high bending stability that the change in the resistance was less than 1% over 50 000 cycles.