Fabricating a high-loading smart film to monitor pork freshness via adsorption of anthocyanins on simultaneously etched, anionized and bleached wood cell wall.

In this paper, wood cell walls were simultaneously roughened, carboxylated, and bleached via NaOH/H2O2 treatment and roughened-poplar film (RPF) was obtained. Compared with the untreated film, the carboxyl group content increased 8 times to 1.92 mmol/g, and the pore growth rate reached 11.24%. Afterwards, a pH-indicator wood film (CTA-RPF) was prepared by self-adsorption of anthocyanins on RPF. It rapidly changed from purple to green within 7 s in 0.25 mL of ammonia at 53% RH and the initial color could restore in the air. When anthocyanins adsorption capacity reached 1.95 mg/g, only 0.36 cm2 of the film could accurately indicate the quality change of 300 g pork. Currently, CTA-RPF is the smallest smart film that can track the maximum mass of pork after comparing with other researches, therefore, promising to be used as a smart indicator label to track the freshness of pork in real market circulation.

Development of pH-responsive intelligent films based on κ-carrageenan/straw lignin and anthocyanin from Padus virginiana peel for real-time monitoring of chicken.

A series of intelligent films with pH-responsive properties were prepared using Padus virginiana peel extract (PVE) as a smart response factor, κ-carrageenan (κC) as a matrix, and complexed with rice straw lignin (SL). Following the addition of 5 mL PVE at a concentration of 430.99 mg/L, tensile strength and elongation at break of the films increased to a maximum value of 21.25 ± 0.75 MPa and 24.04 ± 0.69 %, respectively. The water vapour permeability of the films decreased with increasing PVE addition, and the minimum value was 5.85 ± 0.09 × 10-11 g m-1 s-1 Pa-1. All the films had favourable thermal stability, transparency, haze and antioxidant properties. PVE-containing films all exhibited excellent pH and ammonia response properties. The higher the humidity of the environment, the faster the ammonia response, and the films were capable of rapid discoloration at 75 % relative humidity. κC/SL-PVE5 can be used to monitor the freshness of chicken breast meat. When the total volatile basic nitrogen of chicken breast meat was increased to 14.27 mg/100 g, κC/SL-PVE5 changed from pink to greyish-yellow. In conclusion, κC/SL-PVE intelligent films hold great promise for real-time monitoring of meat freshness.