RESUMO
Single crystals of Cu2ZnGeSe4 and Cu2ZnGeS4 solid solutions were developed and successfully obtained using the chemical vapor transfer method, with iodine acting as a transporter. The structure, compositional dependences of lattice parameters, pycnometric and X-ray densities and microhardness were determined. The chemical composition determined by the X-ray microanalysis satisfactorily corresponds to the nominal one with a tolerance of ±5 %. The XRD analysis showed that all the obtained compounds and their solid solutions have unit cell described by tetragonal symmetry. The attice parameters were found to be а = 5.342 ± 0.005 Å, Ñ = 10.51 ± 0.01 Å for the Сu2ZnGeS4 compound and а = 5.607 ± 0.005 Å, Ñ = 11.04 ± 0.01 Å for the Cu2ZnGeSe4, respectively. Structural studies confirmed the validity of the Vegard's law in relation to the obtained samples. The pycnometric densities of â¼4.28 g/cm3 for the Cu2ZnGeS4 and â¼5.46 g/cm3 for the Cu2ZnGeSe4 were found to be slightly less than their X-ray densities of â¼4.32 g/cm3 and â¼5.52 g/cm3, respectively. The maximum microhardness of â¼398 kg/mm2 for these solid solutions corresponds to x = 0.60. The melt point of the solid solutions increases from â¼1180 °C for the Сu2ZnGeSe4 up to â¼1400 °C for the Сu2ZnGeS4. Based on X-ray fluorescence analysis and DTA data, the phase diagram of the Cu2ZnGeSe4-Cu2ZnGeS4 system was constructed. Analysis of the obtained diagram indicates its first type according to Rozbom's classification.
RESUMO
The polycrystalline SrFe12O19 samples deeply substituted up to at.67% by Al3+, Ga3+, In3+, Co3+, and Cr3+ cations with a high configurational mixing entropy were prepared by solid-phase synthesis. Phase purity and unit cell parameters were obtained from XRD and analyzed versus the average ionic radius of the iron sublattice. The crystallite size varied around â¼4.5 µm. A comprehensive study of the magnetization was realized in various fields and temperatures. The saturation magnetization was calculated using the Law of Approach to Saturation. The accompanying magnetic parameters were determined. The magnetic crystallographic anisotropy coefficient and the anisotropy field were calculated. All investigated magnetization curves turned out to be nonmonotonic. The magnetic ordering and freezing temperatures were extracted from the ZFC and FC curves. The average size of magnetic clusters varied around â¼350 nm. The high values of the configurational mixing entropy and the phenomenon of magnetic dilution were taken into account.
RESUMO
Spacecraft are exposed to a number of factors in the outer space: irradiation by electron flows, high-energy ions, solar electromagnetic radiation, plasma irradiation, and a stream of meteorite particles. All these factors initiate various physical and chemical processes in spacecraft materials, which can eventually lead to failure. To ensure reliable operation of spacecraft, it is necessary to use protective coatings and special radiation-resistant materials. TiAlCuN and TiAlCuCN coatings were formed by reactive magnetron sputtering on different substrates: single-crystal silicon and Titanium Grade 2 wafers. Nitrogen was used as a reactive gas to form nitride coatings and acetylene was used to form carbonitride coatings. The elemental composition was studied by energy-dispersive X-ray (EDX) spectroscopy. The structural-phase state of the coatings was examined by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Mechanical properties, such as hardness and Young modulus, were investigated by nanoindentation using a CSM Instruments Nanohardness Tester NHT2. The influence of deposition parameters, such as Ti and Al contents, the degree of reactivity α, and carbonitride formation on the structure and their mechanical properties were considered. It was detected that Cu addition to the coatings has effects on crystallite and growth column size refinement in comparison with the TiAlN and TiAlCN analogues due to its segregation along crystalline boundaries, and thus, imparts better mechanical characteristics. The hardness of TiAlCuN and TiAlCuCN coatings varies in the range of H = 25-36 GPa and Young modulus - E = 176-268 GPa. The impact strength index and the H/E* ratio, as well as the plastic deformation resistance index H3/E*2, were calculated. Due to their high mechanical properties, the formed nitride and carbonitride coatings are promising for use in space technologies.
RESUMO
This study announces the anomalous phase separation in CoNiP alloy electroplating. The observed phenomenon of the formation of magnetic bubbles was described for the first time for this triple CoNiP system. This study briefly covers all stages of magnetic bubble formation, starting from the formation of an amorphous phosphor-rich sublayer, followed by nucleation centers, and finally cobalt-rich bubbles. An explanation for the anomalous mechanism of bubble formation was found in the effects of additives and the phenomena of depolarization and superpolarization.
RESUMO
It is common knowledge that the O2 evolution reaction (OER) is a crucial half-reaction in the electrolysis of water. However, it is currently difficult to create inexpensive OER electrode materials in a way that is efficient, simple, and environmentally friendly. In this research, metal oxy-hydroxides with numerous oxygen defects (M-OOHv) are created at surface of Cu foam (CF) using a unique, straightforward electro-oxidation reconstitution (ER) process. Different spectroscopic and microscopy methods are used to analyse the electrode characteristics of Al2Cu-MOF@M-OOHv-ER/CF; electrochemical measurements display a lower overpotential (η) of 366 mV @ 10 mA cm-2 and a Tafel slope of 95.2 mV dec-1 in 1.0 M KOH. X-Ray diffraction (XRD), scanning electron microscopy (SEM), and Raman studies confirm the phase transition of the metal-organic framework (MOF) to the M-OOH, which acts as the active site to boost the OER activity. Through spectroscopic and microscopic investigations, it is determined that the efficiency of bimetallic electrode materials and oxygen vacancies in the M-OOHv have an impact on the electron power density. The manufactured electrode material additionally showed good durability for 50 hours. As a result, the newly developed Al2Cu-MOF@M-OOHv-ER/CF nanomaterial has greater potential for both electrolysis of water and other energy storage equipment.
RESUMO
The structural, electrical, and magneto-elastic properties of lanthanide base nitride (Ln = Dy-Lu) anti-perovskites were investigated using density functional theory (DFT). The reported structural outcomes are consistent with the experiment and decrease from Dy to Lu due to the decrease ofatomic radii of Ln atoms. According to the electronic band profile, the metallic characteristics of these compounds are due to the crossing over of Ln-f states at the Fermi level and are also supported by electrical resistivity. The resistivity of these compounds at room temperature demonstrates that they are good conductors. Their mechanical stability, anisotropic, load-bearing, and malleable nature are demonstrated by their elastic properties. Due to their metallic and load-bearing nature, in addition to their ductility, these materials are suitable as active biomaterials, especially when significant acting loads are anticipated, such as those experienced by such heavily loaded implants as hip and knee endo-prostheses, plates, screws, nails, dental implants, etc. In thesecases, appropriate bending fatigue strength is required in structural materials for skeletal reconstruction. Magnetic properties show that all compounds are G-type anti-ferromagnetic, with the Neel temperatures ranging from 24 to 48 K, except Lu3Nin, which is non-magnetic. Due to their anti-ferromagnetic structure, magnetic probes cannot read data contained in anti-ferromagnetic moments, therefore, data will be unchanged by disrupted magnetic field. As a result, these compounds can be the best candidates for magnetic cloaking devices.
RESUMO
In this study, SrFe12-xNdxO19, where x = 0, 0.1, 0.2, 0.3, 0.4, and 0.5, was prepared using high-energy ball milling. The prepared samples were characterized by X-ray diffraction (XRD). Using the XRD results, a comparative analysis of crystallite sizes of the prepared powders was carried out by different methods (models) such as the Scherrer, Williamson-Hall (W-H), Halder-Wagner (H-W), and size-strain plot (SSP) method. All the studied methods prove that the average nanocrystallite size of the prepared samples increases by increasing the Nd concentration. The H-W and SSP methods are more accurate than the Scherer or W-H methods, suggesting that these methods are more suitable for analyzing the XRD spectra obtained in this study. The specific saturation magnetization (σs), the effective anisotropy constant (Keff), the field of magnetocrystalline anisotropy (Ha), and the field of shape anisotropy (Hd) for SrFe12-xNdxO19 (0 ≤ x ≤ 0.5) powders were calculated. The coercivity (Hc) increases (about 9% at x = 0.4) with an increasing degree of substitution of Fe3+ by Nd3+, which is one of the main parameters for manufacturing permanent magnets.
RESUMO
NiFe films with a composition gradient are of particular interest from the point of view of fundamental science and practical applications. Such gradient magnetic structures may exhibit unique functional properties useful for sensory applications and beyond. The issue surrounds the anomaly concerning the compositional gradient formed near the substrate in electrolytically deposited binary and ternary iron-containing alloys, which has not previously been clearly explained. In this work, light is shed on this issue, and a clear relationship is found between the structure and surface properties of the substrate, the initially formed NiFe layers and the film composition gradient.
RESUMO
The results of studies on the wettability properties and preparation of porous anodic alumina (PAA) membranes with a 3.3 ± 0.2 µm thickness and a variety of pore sizes are presented in this article. The wettability feature results, as well as the fabrication processing characteristics and morphology, are presented. The microstructure effect of these surfaces on wettability properties is analyzed in comparison to outer PAA surfaces. The interfacial contact angle was measured for amorphous PAA membranes as-fabricated and after a modification technique (pore widening), with pore sizes ranging from 20 to 130 nm. Different surface morphologies of such alumina can be obtained by adjusting synthesis conditions, which allows the surface properties to change from hydrophilic (contact angle is approximately 13°) to hydrophobic (contact angle is 100°). This research could propose a new method for designing functional surfaces with tunable wettability. The potential applications of ordinary alumina as multifunctional films are demonstrated.
RESUMO
Nanocomposite films based on spinel ferrite (Mg0.8Zn0.2Fe1.5Al0.5O4) in a PVA matrix were obtained. An increase in the spinel concentration to 10 wt.% caused an avalanche-like rise in roughness due to the formation of nanoparticle agglomerates. The lateral mode of atomic force microscopy (AFM) allowed us to trace the agglomeration dynamics. An unexpected result was that the composite with 6 wt.% of filler had a low friction coefficient in comparison with similar composites due to the successfully combined effects of low roughness and surface energy. The friction coefficient decreased to 0.07 when the friction coefficient of pure PVA was 0.72. A specially developed method for measuring nano-objects' surface energy using AFM made it possible to explain the anomalous nature of the change in tribological characteristics.
RESUMO
The W-Cu composites with nanosized grain boundaries and high effective density were fabricated using a new fast isostatic hot pressing method. A significantly faster method was proposed for the formation of W-Cu composites in comparison to the traditional ones. The influence of both the high temperature and pressure conditions on the microstructure, structure, chemical composition, and density values were observed. It has been shown that W-Cu samples have a polycrystalline well-packed microstructure. The copper performs the function of a matrix that surrounds the tungsten grains. The W-Cu composites have mixed bcc-W (sp. gr. Im 3¯ m) and fcc-Cu (sp. gr. Fm 3¯ m) phases. The W crystallite sizes vary from 107 to 175 nm depending on the sintering conditions. The optimal sintering regimes of the W-Cu composites with the highest density value of 16.37 g/cm3 were determined. Tungsten-copper composites with thicknesses of 0.06-0.27 cm have been fabricated for the radiation protection efficiency investigation against gamma rays. It has been shown that W-Cu samples have a high shielding efficiency from gamma radiation in the 0.276-1.25 MeV range of energies, which makes them excellent candidates as materials for radiation protection.
RESUMO
Multisubstituted barium ferrites with a magnetoplumbite structure were obtained by the method of solid-phase reactions with ferritization and pre-firing. Three-charged, mainly diamagnetic cations Al3+, Cr3+, Ga3+, and In3+ were chosen as substituents for the Fe3+ iron cations, the proportion of which in solid solutions did not exceed 50%. The values of the configurational mixing entropy were calculated for all the compositions. A slight deviation of the chemical composition of the obtained solid solutions from the nominal value was established by the energy-dispersive X-ray spectroscopy method. The phase purity and values of the unit cell parameters were refined from X-ray scattering data using full-profile analysis in the Rietveld method. A non-monotonic behavior of the unit cell parameters as a function of the B-sub-lattice average ionic radius of the magnetoplumbite structure was found. A minimum unit cell volume of ~667.15 Å3 was found for the composition BaFe6.11Al1.56Cr2.17Ga2.16O19 with a B-sub-lattice average ionic radius of ~7.449 Å. The average crystallite size varied within 5.5-6.5 µm. The temperature and field dependencies of the magnetization have been measured. The values of the saturation magnetization, residual magnetization, hysteresis loop squareness, and coercivity at 50 K and 300 K were extracted from the experimental data. Using the Law of Approach to Saturation, the magnetic crystallographic anisotropy coefficient and anisotropy field were calculated. Multisubstitution leads to a significant decrease in such magnetic parameters as the magnetic ordering temperature and spontaneous magnetization at both temperatures. The maximum magnetic ordering temperature of ~297.7 K was found for the composition BaFe5.84Ga6.19O19 with a B-sub-lattice average ionic radius of ~7.586 Å in a field of 500 Oe. A maximum saturation magnetization of ~24.7 emu/g was found for the composition BaFe5.84Ga6.19O19 with a B-sub-lattice average ionic radius of ~7.586 Å at 50 K. A maximum hysteresis loop squareness of ~0.72 was found for the composition BaFe6.11Al1.56Cr2.17Ga2.16O19 with an average ionic radius of ~7.449 Å at 50 K. A maximum magnetic crystallographic anisotropy coefficient of ~2.09 × 105 Erg/g was found for the composition BaFe6.19Al1.25Cr1.57Ga1.74In1.26O19 with a B-sub-lattice average ionic radius of ~7.706 Å at 50 K. The frustrated magnetic state including the nano-sized clusters with an average diameter in the range of 50-200 nm was established from the results of measuring the ZFC and FC temperature magnetizations. The interpretation of the obtained experimental data is carried out taking into account the increased stability of high-entropy phases and regular changes in the intensity of the Fe3+(Al3+, Cr3+, Ga3+, In3+)-O2--Fe3+(Al3+, Cr3+, Ga3+, In3+) indirect superexchange interactions as a result of magnetic dilution of the iron sub-lattice in the magnetoplumbite structure.
RESUMO
The paper discusses the formation of Ta2O5 pillars with Ni tips during thin porous anodic alumina through-mask anodization on Si/SiO2 substrates. The tantalum nanopillars were formed through porous masks in electrolytes of phosphoric and oxalic acid. The Ni tips on the Ta2O5 pillars were formed via vacuum evaporation through the porous mask. The morphology, structure, and magnetic properties at 4.2 and 300 K of the Ta2O5 nanopillars with Ni tips have been studied using scanning electron microscopy, X-ray diffraction, and vibrating sample magnetometry. The main mechanism of the formation of the Ta2O5 pillars during through-mask anodization was revealed. The superparamagnetic behavior of the magnetic hysteresis loop of the Ta2O5 nanopillars with Ni tips was observed. Such nanostructures can be used to develop novel functional nanomaterials for magnetic, electronic, biomedical, and optical nano-scale devices.
RESUMO
Binary and ternary composites (CM) based on M-type hexaferrite (HF), polymer matrix (PVDF) and carbon nanomaterials (quasi-one-dimensional carbon nanotubes-CNT and quasi-two-dimensional carbon nanoflakes-CNF) were prepared and investigated for establishing the impact of the different nanosized carbon on magnetic and electrodynamic properties. The ratio between HF and PVDF in HF + PVDF composite was fixed (85 wt% HF and 15 wt% PVDF). The concentration of CNT and CNF in CM was fixed (5 wt% from total HF + PVDF weight). The phase composition and microstructural features were investigated using XRD and SEM, respectively. It was observed that CM contains single-phase HF, γ- and ß-PVDF and carbon nanomaterials. Thus, we produced composites that consist of mixed different phases (organic insulator matrix-PDVF; functional magnetic fillers-HF and highly electroconductive additives-CNT/CNF) in the required ratio. VSM data demonstrate that the main contribution in main magnetic characteristics belongs to magnetic fillers (HF). The principal difference in magnetic and electrodynamic properties was shown for CNT- and CNF-based composites. That confirms that the shape of nanosized carbon nanomaterials impact on physical properties of the ternary composited-based magnetic fillers in polymer dielectric matrix.