Influence of CAD-CAM diamond bur deterioration on surface roughness and maximum failure load of Y-TZP-based restorations.

PURPOSE: To investigate the influence of CAD-CAM diamond bur deterioration on surface roughness (Ra) and maximum failure load (Lf) of Y-TZP-based ceramic (YZ) substructures (SB) veneered with a feldspathic porcelain. METHODS: Two sets of burs (B1 and B2) were used to fabricate 30 YZ SB each in a CAD/CAM system (Cerec InLab). The SB were identified (1-30) according to the milling sequence (MS). SEM images of the burs were recorded before milling, and after milling 15 and 30 SB. The SB Ra was measured. All SB were veneered, cemented onto a fiber reinforced epoxy resin die, and loaded to failure. Specimens from B1 group were cyclic fatigued (106 cycles) before loading to failure. Fractographic analysis was performed. Data were statistically analyzed using Student's t-test, Weibull analysis, Pearson's correlation and ANOVA (α= 0.05). RESULTS: The mean Ra value of B1 specimens was statistically greater than B2. Weibull modulus of B1 and B2 were statistically similar. The correlation between MS and Lf was not statistically significant for the groups. MS and Ra had significant correlation for both groups (B1: r= -0.514, P= 0.015; B2: r= -0.462, P= 0.03). Although the visual aspect (SEM) of the burs was similar after 30 millings, the mean Ra values were significantly different after 27 millings for B1 and 24 millings for B2.

Effect of cement shade and light-curing unit on bond strength of a ceramic cemented to dentin.

PURPOSE: To evaluate the effect of cement shade, light-curing unit, and water storage on tensile bond strength (σ) of a feldspathic ceramic resin bonded to dentin. MATERIALS AND METHODS: The dentin surface of 40 molars was exposed and etched with 37% phosphoric acid, then an adhesive system was applied. Forty blocks of feldspathic ceramic (Vita VM7) were produced. The ceramic surface was etched with 10% hydrofluoric acid for 60 s, followed by the application of a silane agent and a dual-curing resin cement (Variolink II). Ceramic blocks were cemented to the treated dentin using either A3 or transparent (Tr) shade cement that was activated using either halogen or LED light for 40 s. All blocks were stored in 37°C distilled water for 24 h before cutting to obtain non-trimmed bar-shaped specimens (adhesive area = 1 mm2 ± 0.1) for the microtensile bond strength test. The specimens were randomly grouped according to the storage time: no storage or stored for 150 days in 37°C distilled water. Eight experimental groups were obtained (n = 30). The specimens were submitted to the tensile bond strength test using a universal testing machine at a crosshead speed of 1 mm/min. The data were statistically analyzed using ANOVA and Tukey's posthoc tests (a = 0.05). RESULTS: The mean bond strength values were significantly lower for the corresponding water stored groups, except for the specimens using A3 resin cement activated by halogen light. There was no significance difference in mean bond strength values among all groups after water storage. CONCLUSION: Water storage had a detrimental effect under most experimental conditions. For both cement shades investigated (Tr and A3) under the same storage condition, the light-curing units (QTH and LED) did not affect the mean microtensile bond strengths of resin-cemented ceramic to dentin.

Evaluation of flexural resistance of a denture base acrylic resin reinforced with glass fiber and with composite resin.

The objective of this study was to evaluate the flexural strength of denture base resin reinforced with glass fibers and with a laboratorial composite resin. Group G1 was formed with specimens made of acrylic resin. Group G2 was formed with the same acrylic resin but reinforced with a glass-fiber system, and G3 was reinforced with the composite resin. A flexural strength test was performed in all groups (n=10). The mean value for the G1 was 86.70 MPa +/- 6.48, for G2 it was 86.60 MPa +/- 15.01 and for G3 it was 108.90 + 11.03. The addition of glass fiber did not increase the flexural strength however the use of a resin-based composite produced significant reinforcement.