Edgewise Compression and Three-Point Bending Analyses of Repaired Composite Sandwich Panels.

In this work, the fracture behaviour of repaired honeycomb/carbon-epoxy sandwich panels under edgewise compression and three-point bending loading was analysed. Assuming the occurrence of damage resulting from a complete perforation leading to an open hole, the followed repair strategy consists of plug filling the core hole and considering two scarf patches with an angle of 10° in order to repair the damaged skins. Experimental tests were performed on undamaged and repaired situations in order to address the alteration in the failure modes and assess the repair efficiency. It was observed that repair recovers a large part of the mechanical properties of the corresponding undamaged case. Additionally, a three-dimensional finite element analysis incorporating a mixed-mode I + II + III cohesive zone model was performed for the repaired cases. Cohesive elements were considered in the several critical regions prone to damage development. The failure modes and the resultant load-displacement curves obtained numerically were compared with the experimental ones. It was concluded that the numerical model is suitable for estimating the fracture behaviour of sandwich panel repairs.

Osteosynthesis Metal Plate System for Bone Fixation Using Bicortical Screws: Numerical-Experimental Characterization.

This study reports the numerical and experimental characterization of a standard immobilization system currently being used to treat simple oblique bone fractures of femoral diaphyses. The procedure focuses on the assessment of the mechanical behavior of a bone stabilized with a dynamic compression plate (DCP) in a neutralization function, associated to a lag screw, fastened with surgical screws. The non-linear behavior of cortical bone tissue was revealed through four-point bending tests, from which damage initiation and propagation occurred. Since screw loosening was visible during the loading process, damage parameters were measured experimentally in independent pull-out tests. A realistic numerical model of the DCP-femur setup was constructed, combining the evaluated damage parameters and contact pairs. A mixed-mode (I+II) trapezoidal damage law was employed to mimic the mechanical behavior of both the screw-bone interface and bone fractures. The numerical model replicated the global behavior observed experimentally, which was visible by the initial stiffness and the ability to preview the first loading peak, and bone crack satisfactorily.