RESUMO
In this work, extremely thin silicon-on-insulator field effective transistors (ETSOI FETs) are fabricated with an ultra-thin 3 nm ferroelectric (FE) hafnium zirconium oxides (Hf0.5Zr0.5O2) layer. Furthermore, the subthreshold characteristics of the devices with double gate modulation are investigated extensively. Contributing to the advantages of the back-gate voltage coupling effects, the minimum subthreshold swing (SS) value of a 40 nm ETSOI device could be adjusted from the initial 80.8-50 mV/dec, which shows ultra-steep SS characteristics. To illustrate this electrical character, a simple analytical model based on the transient Miller model is demonstrated. This work shows the feasibility of FE ETSOI FET for ultra-low-power applications with dynamic threshold adjustment.
RESUMO
Ultrathin Hf-Ti-O higher k gate dielectric films (~2.55 nm) have been prepared by atomic layer deposition. Their electrical properties and application in ETSOI (fully depleted extremely thin SOI) PMOSFETs were studied. It is found that at the Ti concentration of Ti/(Ti + Hf) ~9.4%, low equivalent gate oxide thickness (EOT) of ~0.69 nm and acceptable gate leakage current density of 0.61 A/cm2 @ (V fb - 1)V could be obtained. The conduction mechanism through the gate dielectric is dominated by the F-N tunneling in the gate voltage range of -0.5 to -2 V. Under the same physical thickness and process flow, lower EOT and higher I on/I off ratio could be obtained while using Hf-Ti-O as gate dielectric compared with HfO2. With Hf-Ti-O as gate dielectric, two ETSOI PMOSFETs with gate width/gate length (W/L) of 0.5 µm/25 nm and 3 µm/40 nm show good performances such as high I on, I on/I off ratio in the magnitude of 105, and peak transconductance, as well as suitable threshold voltage (-0.3~-0.2 V). Particularly, ETSOI PMOSFETs show superior short-channel control capacity with DIBL <82 mV/V and subthreshold swing <70 mV/decade.