(Bio)degradable Biochar Composites of PLA/P(3HB-co-4HB) Commercial Blend for Sustainable Future-Study on Degradation and Electrostatic Properties.

Interesting alternatives to expensive biodegradable polymers are their composites with natural fillers. The addition of biochar to a blend of poly(lactic acid) (PLA) and poly(3-hydroxybutyrate-co-4-hydroxybutyrate) was studied, and the resulting materials were evaluated for their properties and changes during degradation. Introducing biochar as a filler brought a noticeable improvement in electrostatic properties. Surface resistivity decreased from 3.80 × 1012 for the sample without biochar to 1.32 × 1012 for the sample with 30% filler content. Degradation tests revealed distinct differences in the degradation profile for composites due to the presence of filler. Composites with a lower biochar content displayed curling crack edges during hydrolytic degradation, and when the filler content reached 20 wt%, PLA loss accelerated. This study suggests that biochar-based composites have potential to be used as sustainable materials with improved properties.

Development and physiochemical assessment of graphene-bioactive glass-P(3HB-co-4HB) composite scaffold as prospect biomaterial for wound healing.

The clinical management of wounds presents a considerable challenge because dressing selection must prioritise the provision of appropriate barrier and the healing properties, consider patient's compliance factors such as comfort, functionality and practicality. This study primarily aimed to develop a composite scaffold patch for potential application in wound healing. Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) [P(3HB-co-4HB)] is a biopolymer that originated from bacteria. It is well-recognised owing to its distinctive mechanical and physical characteristics suitable for biomedical applications. Graphene (G) and bioactive glass (BG) are biocompatible towards humans, and enhanced properties are achievable by adding biopolymer. In this study, composite scaffolds were developed by combining P(3HB-co-4HB) at a distinct proportion of 4HB monomer reinforced with G (3.0 wt.%) and BG (2.5 wt.%) by using solvent casting, resulting in two types of composite scaffolds: P(3HB-co-25%4HB)/G/BG and P(3HB-co-37%4HB)/G/BG. A successful composite scaffold as a unified structure was achieved based on chemical assessments of organic and inorganic elements within the composites. The pure polymer displayed a smooth surface, and the BG and G addition into the composite scaffolds increased surface roughness, forming irregular pores and protuberances. The wettability and hydrophilicity of the composites significantly improved up to 40% in terms of water uptake. An increment in crystallisation temperature diminished the flexibility of the composite's scaffolds. Evaluation of Presto Blue biocompatibility demonstrated nontoxic behaviour with a dosage of less than 25.00 mg ml-1of composite scaffold-conditioned media. The L929 fibroblast cells displayed excellent adhesion to both types of composite scaffolds, as evidenced by the increased percentage of cell viability observed throughout 14 d of exposure. These findings demonstrate the importance of optimising each component within the composite scaffolds and their interrelation, paving the way for excellent material properties and enhancing the potential for wound healing applications.

Effects of Differing Monomer Compositions on Properties of P(3HB-co-4HB) Synthesized by Aneurinibacillus sp. H1 for Various Applications.

Films prepared from poly(3-hydroxybutyrate-co-4-hydroxybutyrate) copolymers produced by Aneurinibacillus sp. H1 using an automatic film applicator were homogeneous and had a defined thickness, which allowed a detailed study of physicochemical properties. Their properties were compared with those of a poly (3-hydroxybutyrate) homopolymer film prepared by the same procedure, which proved to be significantly more crystalline by DSC and XRD. Structural differences between samples had a major impact on their properties. With increasing 4-hydroxybutyrate content, the ductility and release rate of the model hydrophilic active ingredient increased significantly. Other observed properties, such as the release of the hydrophobic active substance, the contact angle with water and ethylene glycol, or the surface morphology and roughness, were also affected by the composition. The identified properties predetermine these copolymers for wide use in areas such as biomedicine or smart biodegradable packaging for food or cosmetics. The big advantage is the possibility of fine-tuning properties simply by changing the fermentation conditions.

Supercritical CO2 Foaming of Poly(3-hydroxybutyrate-co-4-hydroxybutyrate).

The supercritical carbon dioxide foaming characteristics of the biodegradable polymer poly(3-hydroxybutyrate-co-4-hydroxybutyrate) (P(3HB-co-4HB)) are studied for environmentally friendly packaging materials. The effect of the 4HB composition of the P(3HB-co-4HB) copolymers on the foaming conditions such as pressure and temperature is studied and the density and the expansion ratio of the resulting P(3HB-co-4HB) foam are together evaluated. The increase in the 4HB content reduces the crystallinity and tan δ value of P(3HB-co-4HB) required for the growth of the foam cells. Therefore, the foaming temperature needs to be lower to retain a suitable tan δ value of P(3HB-co-4HB) for foaming. It was found that P(3HB-co-4HB) with less crystallinity showed better formability and cell uniformity. However, foaming is not possible regardless of the foaming temperature when the 4HB content of P(3HB-co-4HB) is over 50%, due to the high tan δ value. A lower foam density and higher expansion ratio can be obtained with crystalline P(3HB-co-4HB) of low 4HB content, compared with non-crystalline P(3HB-co-4HB) of high 4HB content. The expansion ratio of P(3HB-co-4HB) foams can be increased slightly by using a chain extender, due to the lowing of crystallinity and tan δ. This is most effective in the case of P(3HB-co-4HB), whose 4HB content is 16%.

Surface Modification of Sponge-like Porous Poly(3-hydroxybutyrate-co-4-hydroxybutyrate)/Gelatine Blend Scaffolds for Potential Biomedical Applications.

In this study, we described the preparation of sponge-like porous scaffolds that are feasible for medical applications. A porous structure provides a good microenvironment for cell attachment and proliferation. In this study, a biocompatible PHA, poly(3-hydroxybutyrate-co-4-hydroxybutyrate) was blended with gelatine to improve the copolymer's hydrophilicity, while structural porosity was introduced into the scaffold via a combination of solvent casting and freeze-drying techniques. Scanning electron microscopy results revealed that the blended scaffolds exhibited higher porosity when the 4HB compositions of P(3HB-co-4HB) ranged from 27 mol% to 50 mol%, but porosity decreased with a high 4HB monomer composition of 82 mol%. The pore size, water absorption capacity, and cell proliferation assay results showed significant improvement after the final weight of blend scaffolds was reduced by half from the initial 0.79 g to 0.4 g. The pore size of 0.79g-(P27mol%G10) increased three-fold while the water absorption capacity of 0.4g-(P50mol%G10) increased to 325%. Meanwhile, the cell proliferation and attachment of 0.4g-(P50mol%G10) and 0.4g-(P82mol%G7.5) increased as compared to the initial seeding number. Based on the overall data obtained, we can conclude that the introduction of a small amount of gelatine into P(3HB-co-4HB) improved the physical and biological properties of blend scaffolds, and the 0.4g-(P50mol%G10) shows great potential for medical applications considering its unique structure and properties.

The Modification of Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) by Melt Blending.

Crystalline and noncrystalline poly(3-hyroxybutylate-co-4-hyroxybutylate) (P(3HB-co-4HB)) were melt blended to obtain mixtures of P(3HB-co-4HB) copolymers. The mixtures and P(3HB-co-4HB) copolymers of different 4HB contents were compared to study the effect of 4HB content on the properties of the copolymers and mixtures. P(3HB-co-4HB) copolymer mixtures, having various 4HB content, have been successfully made by melt blending instead of bacterial biosynthesis. In the case of copolymers, they were noncrystalline when the 4HB content was over 16%, while the P(3HB-co-4HB) mixtures at the same 4HB content were crystalline. The mixtures had a higher glass transition temperature, suggesting that their chain mobility is relatively low compared with the copolymer having the same 4HB content. Due to this effect, the mixture is expected to have a higher melt viscosity and a lower loss tangent to exhibit better melt processing properties. The mechanical properties of the mixtures show a similar behavior to the copolymers in that the tensile strength and the modulus decreases and elongation at the break increases with an increase in the 4HB content.

Surface Characterization and Physiochemical Evaluation of P(3HB-co-4HB)-Collagen Peptide Scaffolds with Silver Sulfadiazine as Antimicrobial Agent for Potential Infection-Resistance Biomaterial.

Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) [P(3HB-co-4HB)] is a bacterial derived biopolymer widely known for its unique physical and mechanical properties to be used in biomedical application. In this study, antimicrobial agent silver sulfadiazine (SSD) coat/collagen peptide coat-P(3HB-co-4HB) (SCCC) and SSD blend/collagen peptide coat-P(3HB-co-4HB) scaffolds (SBCC) were fabricated using a green salt leaching technique combined with freeze-drying. This was then followed by the incorporation of collagen peptides at various concentrations (2.5-12.5 wt.%) to P(3HB-co-4HB) using collagen-coating. As a result, two types of P(3HB-co-4HB) scaffolds were fabricated, including SCCC and SBCC scaffolds. The increasing concentrations of collagen peptides from 2.5 wt.% to 12.5 wt.% exhibited a decline in their porosity. The wettability and hydrophilicity increased as the concentration of collagen peptides in the scaffolds increased. In terms of the cytotoxic results, MTS assay demonstrated the L929 fibroblast scaffolds adhered well to the fabricated scaffolds. The 10 wt.% collagen peptides coated SCCC and SBCC scaffolds displayed highest cell proliferation rate. The antimicrobial analysis of the fabricated scaffolds exhibited 100% inhibition towards various pathogenic microorganisms. However, the SCCC scaffold exhibited 100% inhibition between 12 and 24 h, but the SBCC scaffolds with SSD impregnated in the scaffold had controlled release of the antimicrobial agent. Thus, this study will elucidate the surface interface-cell interactions of the SSD-P(3HB-co-4HB)-collagen peptide scaffolds and controlled release of SSD, antimicrobial agent.

In Vivo Characterization and Application of the PHA Synthase from Azotobacter vinelandii for the Biosynthesis of Polyhydroxyalkanoate Containing 4-Hydroxybutyrate.

Polyhydroxyalkanoate (PHA) is a biodegradable thermoplastic naturally synthesized by many microorganisms, and the PHA synthase (PhaC) is known to be the key enzyme involved in determining the material properties and monomer composition of the produced PHA. The ability to exploit widely distributed, commonly found soil microorganisms such as Azotobacter vinelandii to synthesize PHA containing the lipase-degradable 4-hydroxybutyrate (4HB) monomer will allow for convenient production of biocompatible and flexible PHA. Comparisons between the A. vinelandii wild type and mutant strains, with and without a surface layer (S-layer), respectively, in terms of gene or amino acid sequences, synthase activity, granule morphology, and PHA productivity, revealed that the S-layer is the sole factor affecting PHA biosynthesis by A. vinelandii. Based on PHA biosynthesis using different carbon sources, the PhaC of A. vinelandii showed specificity for short-chain-length PHA monomers, making it a member of the Class I PHA synthases. In addition, it was proven that the PhaC of A. vinelandii has the inherent ability to polymerize 4-hydroxybutyrate (4HB) and the mediated accumulation of PHA with 4HB fractions ranging from 10 mol% to as high as 22 mol%. The synthesis of biocompatible PHA containing tailorable amounts of 4HB with an expanded range of elasticity and lipase-degradability will enable a wider range of applications in the biomedical field.

P(3HB-co-4HB) as high value polyhydroxyalkanoate: its development over recent decades and current advances.

Polyhydroxyalkanoate (PHA) is a biogenic polymer that has the potential to substitute synthetic plastic in numerous applications. This is due to its unique attribute of being a biodegradable and biocompatible thermoplastic, achievable through microbial fermentation from a broad utilizable range of renewable resources. Among all the PHAs discovered, poly(3-hydroxybutyrate-co-4-hydroxybutyrate) [P(3HB-co-4HB)] stands out as a next generation healthcare biomaterial for having high biopharmaceutical and medical value since it is highly compatible to mammalian tissue. This review provides a critical assessment and complete overview of the development and trend of P(3HB-co-4HB) research over the last few decades, highlighting aspects from the microbial strain discovery to metabolic engineering and bioprocess cultivation strategies. The article also outlines the relevance of P(3HB-co-4HB) as a material for high value-added products in numerous healthcare-related applications.

Elucidating the Surface Functionality of Biomimetic RGD Peptides Immobilized on Nano-P(3HB-co-4HB) for H9c2 Myoblast Cell Proliferation.

Biomaterial scaffolds play crucial role to promote cell proliferation and foster the regeneration of new tissues. The progress in material science has paved the way for the generation of ingenious biomaterials. However, these biomaterials require further optimization to be effectively used in existing clinical treatments. It is crucial to develop biomaterials which mimics structure that can be actively involved in delivering signals to cells for the formation of the regenerated tissue. In this research we nanoengineered a functional scaffold to support the proliferation of myoblast cells. Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) [P(3HB-co-4HB)] copolymer is chosen as scaffold material owing to its desirable mechanical and physical properties combined with good biocompatibility, thus eliciting appropriate host tissue responses. In this study P(3HB-co-4HB) copolymer was biosynthesized using Cupriavidus malaysiensis USMAA1020 transformant harboring additional PHA synthase gene, and the viability of a novel P(3HB-co-4HB) electrospun nanofiber scaffold, surface functionalized with RGD peptides, was explored. In order to immobilize RGD peptides molecules onto the P(3HB-co-4HB) nanofibers surface, an aminolysis reaction was performed. The nanoengineered scaffolds were characterized using SEM, organic elemental analysis (CHN analysis), FTIR, surface wettability and their in vitro degradation behavior was evaluated. The cell culture study using H9c2 myoblast cells was conducted to assess the in vitro cellular response of the engineered scaffold. Our results demonstrated that nano-P(3HB-co-4HB)-RGD scaffold possessed an average fiber diameter distribution between 200 and 300 nm, closely biomimicking, from a morphological point of view, the structural ECM components, thus acting as potential ECM analogs. This study indicates that the surface conjugation of biomimetic RGD peptide to the nano-P(3HB-co-4HB) fibers increased the surface wettability (15 ± 2°) and enhanced H9c2 myoblast cells attachment and proliferation. In summary, the study reveals that nano-P(3HB-co-4HB)-RGD scaffold can be considered a promising candidate to be further explored as cardiac construct for building cardiac construct.

Introducing the Newly Isolated Bacterium Aneurinibacillus sp. H1 as an Auspicious Thermophilic Producer of Various Polyhydroxyalkanoates (PHA) Copolymers-1. Isolation and Characterization of the Bacterium.

Extremophilic microorganisms are considered being very promising candidates for biotechnological production of various products including polyhydroxyalkanoates (PHA). The aim of this work was to evaluate the PHA production potential of a novel PHA-producing thermophilic Gram-positive isolate Aneurinibacillus sp. H1. This organism was capable of efficient conversion of glycerol into poly(3-hydroxybutyrate) (P3HB), the homopolyester of 3-hydroxybutyrate (3HB). In flasks experiment, under optimal cultivation temperature of 45 °C, the P3HB content in biomass and P3HB titers reached 55.31% of cell dry mass and 2.03 g/L, respectively. Further, the isolate was capable of biosynthesis of PHA copolymers and terpolymers containing high molar fractions of 3-hydroxyvalerate (3HV) and 4-hydroxybutyrate (4HB). Especially 4HB contents in PHA were very high (up to 91 mol %) when 1,4-butanediol was used as a substrate. Based on these results, it can be stated that Aneurinibacillus sp. H1 is a very promising candidate for production of PHA with tailored material properties.

Introducing the Newly Isolated Bacterium Aneurinibacillus sp. H1 as an Auspicious Thermophilic Producer of Various Polyhydroxyalkanoates (PHA) Copolymers-2. Material Study on the Produced Copolymers.

Aneurinibacillus sp. H1 is a promising, moderately thermophilic, novel Gram-positive bacterium capable of the biosynthesis of polyhydroxyalkanoates (PHA) with tunable monomer composition. In particular, the strain is able to synthesize copolymers of 3-hydroxybutyrate (3HB), 4-hydroxybutyrate (4HB) and 3-hydroxyvalerate (3HV) with remarkably high 4HB and 3HV fractions. In this study we performed an in-depth material analysis of PHA polymers produced by Aneurinibacillus sp. H1 in order to describe how the monomer composition affects fundamental structural and physicochemical parameters of the materials in the form of solvent-casted films. Results of infrared spectroscopy, X-ray diffractometry and thermal analysis clearly show that controlling the monomer composition enables optimization of PHA crystallinity both qualitatively (the type of the crystalline lattice) and quantitatively (the overall degree of crystallinity). Furthermore, resistance of the films against thermal and/or enzymatic degradation can also be manipulated by the monomer composition. Results of this study hence confirm Aneurinibacillus sp. H1 as an auspicious candidate for thermophilic production of PHA polymers with material properties that can be tuned together with their chemical composition by the corresponding adjustment of the cultivation process.

Electrospun poly(3-hydroxybutyrate-co-4-hydroxybutyrate) /Octacalcium phosphate Nanofibrous membranes for effective guided bone regeneration.

Membranes used in guided bone regeneration (GBR) are required to exhibit high mechanical strength, biocompatibility, biodegradation, osteogenic and osteoinductive potential. In our study, poly(3-hydroxybutyrate-co-4-hydroxybutyrate)(P(3HB-co-4HB))/octacalcium phosphate (OCP) (P(3HB-co-4HB)/OCP) nanofibrous membranes were fabricated by electrospinning with two different P(3HB-co-4HB) to OCP ratios (P(3HB-co-4HB):OCP = 95:5 wt% and 90:10 wt%, termed P(3HB-co-4HB)/OCP(5)and P(3HB-co-4HB)/OCP (10), respectively) for GBR. The developed P(3HB-co-4HB)/OCP nanofibrous membranes were analysed for their osteogenic and osteoinductive properties using mesenchymal stem cells (MSCs) in vitro and in a calvarial bone defect rat model. The composite P(3HB-co-4HB)/OCP nanofibrous membranes showed decreased fibre size and enhanced tensile strength compared with those of P(3HB-co-4HB) nanofibrous membranes. In the in vitro studies, the P(3HB-co-4HB)/OCP membranes facilitated cell growth and osteoblastic differentiation of MSCs and were superior to P(3HB-co-4HB) membranes. After covered on the calvarial bone defects, P(3HB-co-4HB)/OCP membranes facilitated greater neobone formation than P(3HB-co-4HB) membranes did, as the result of histological evaluation and micro-CT analysis with higher bone volume/total volume (BV/TV) ratio and bone mineral density (BMD). P(3HB-co-4HB)/OCP(10) membranes with higher OCP content showed greater stiffness and osteoinductivity than P(3HB-co-4HB)/OCP (5)membranes, demonstrating the role of OCP in the composite membranes. These results indicated that electrospun P(3HB-co-4HB)/OCP nanofibrous membranes hold promise for the clinical application of GBR.

Data on the effect of electrospinning parameters on the morphology of the nanofibrous poly(3-hydroxybutyrate-co-4-hydroxybutyrate) scaffolds.

Electrospinning is a promising approach to fabricate desirable electropsun nanofibrous scaffold that could be applied in the medical fields. In this study, bacterial copolymer poly(3-hydroxybutyrate-co-68 mol% 4-hydroxybutyrate) [P(3HB-co-68mol% 4HB)] copolymer produced was fabricated into electrospun nanofibers using various combination of electrospinning parameters including the polymer solution, applied voltage and injection speed. The morphology of the fabricated scaffolds were observed using scanning electron microscope (SEM). The SEM images were analysed for the fibre diameter distribution of the scaffolds using Image Analyser. The results revealed that the 8 wt% of polymer solution, 25 kV/cm of the applied voltage and 1.5 mL/h of the injection speed was the most suitable combination. This electrospinning parameters combination fabricated nanofibrous P(3HB-co-4HB) scaffold with smooth, beadles and uniform nanofibers with small fibre diameter distribution.

High PHA density fed-batch cultivation strategies for 4HB-rich P(3HB-co-4HB) copolymer production by transformant Cupriavidus malaysiensis USMAA1020.

P(3HB-co-4HB) with a high 4HB monomer composition was previously successfully produced using the transformant Cupriavidus malaysiensis USMAA1020 containing an additional copy of the PHA synthase gene. In this study, high PHA density fed-batch cultivation strategies were developed for such 4HB-rich P(3HB-co-4HB). The pulse, constant and mixed feeding strategies resulted in high PHA accumulation, with a PHA content of 74-92 wt% and 4HB monomer composition of 92-99 mol%. The pulse-feed of carbon and nitrogen resulted in higher PHA concentration (30.7 g/L) than carbon alone (22.3 g/L), suggesting that a trace amount of nitrogen is essential to support cell density for PHA accumulation. Constant feeding was found to be a more feasible strategy than mixed feeding, since the latter caused a drastic fluctuation in the C/N ratio, as evidenced by higher biomass formation indicating more carbon flux towards the competitive TCA pathway. A two-times carbon and nitrogen pulse feeding was the most optimal strategy achieving 92 wt% accommodation of the total biomass, with the highest PHA concentration (46 g/L) and yield (Yp/x) of 11.5 g/g. The strategy has kept the C/N at optimal ratio during the active PHA-producing phase. This is the first report of the production of high PHA density for 4HB-rich P(3HB-co-4HB).

Production of high molecular weight poly(3-hydroxybutyrate-co-4-hydroxybutyrate) copolymer by Cupriavidus malaysiensis USMAA1020 utilising substrate with longer carbon chain.

Long carbon chain alkanediols are used in the production of poly(3-hydroxybutyrate-co-4-hydroxybutyrate) [P(3HB-co-4HB)], however these substrates possess high toxicity towards bacterial cells. This study demonstrated the effective utilisation of a long carbon chain alkanediol, namely 1,8-octanediol, to enhance the yield and production of a copolymer with a high molecular weight of over 1000 kDa, which is desirable for novel applications in medical and biopharmaceuticals. The increased PHA content (47-61 wt%) and concentration (1.7-4.5 g/L) was achieved by additional feeding of a combination of C4 substrates at C/N 10, with 1,8-octanediol + γ-butyrolactone producing P(3HB-co-22 mol% 4HB) with a high molecular weight (1060 kDa) and elongation at break of 970%. The DO-stat feeding strategy of C/N 10 has shown an increment of PHA concentration for both carbon combination, 0.45-4.27 g/L and 0.32-3.36 g/L for 1,8-octanediol + sodium 4-hydroxybutyrate (4HB-Na) and 1,8-octanediol + γ-butyrolactone, but with a slight reduction on molecular weight and mechanical strength. Nonetheless, further study revealed that a nitrogen-absence feeding strategy could retain the high molecular weight and elongation at break of the copolymer, and simultaneously improving the overall P(3HB-co-4HB) production.

Acute and repeated dose 28-day oral toxicity of poly(3-hydroxybutyrate-co-4-hydroxybutyrate) nanoparticles in Sprague-Dawley rats.

This study aimed to investigate the oral acute and subacute toxicity of Poly [3-hydroxybutyrate-co-4-hydroxybutyrate], P(3HB-co-4HB) in the form of nanoparticles in Sprague-Dawley rats. Acute oral administration of P(3HB-co-4HB) nanoparticles was performed as a single dose up to 2000 mg/kg in six female rats for 14 days. Subacute toxicity study via oral administration for 28 days at doses of 0 (control), 500, 1000 and 2000 mg/kg in rats (10 rats in each group, female:male = 1:1) was conducted. The estimated lethal dose (LD50) of P(3HB-co-4HB) nanoparticles was >2000 mg/kg. No mortality, unusual changes in behaviour, adverse clinical signs, abnormal changes in body weights or food consumption were observed on all animals treated with P(3HB-co-4HB) nanoparticles during 14 days of the acute toxicity study. In the subacute test, there was no mortality and toxicologically significant changes in clinical signs, body weights, food consumption, hematology, clinical biochemistry, urinalysis, macroscopic findings, organ weights as well as histopathological examination were observed.

Cupriavidus malaysiensis sp. nov., a novel poly(3-hydroxybutyrate-co-4-hydroxybutyrate) accumulating bacterium isolated from the Malaysian environment.

Bacterial classification on the basis of a polyphasic approach was conducted on three poly(3 hydroxybutyrate-co-4-hydroxybutyrate) [P(3HB-co-4HB)] accumulating bacterial strains that were isolated from samples collected from Malaysian environments; Kulim Lake, Sg. Pinang river and Sg. Manik paddy field. The Gram-negative, rod-shaped, motile, non-sporulating and non-fermenting bacteria were shown to belong to the genus Cupriavidus of the Betaproteobacteria on the basis of their 16S rRNA gene sequence analyses. The sequence similarity value with their near phylogenetic neighbour, Cupriavidus pauculus LMG3413T, was 98.5%. However, the DNA-DNA hybridization values (8-58%) and ribotyping analysis both enabled these strains to be differentiated from related Cupriavidus species with validly published names. The RiboPrint patterns of the three strains also revealed that the strains were genetically related even though they displayed a clonal diversity. The major cellular fatty acids detected in these strains included C15:0 ISO 2OH/C16:1 ω7c, hexadecanoic (16:0) and cis-11-octadecenoic (C18:1 ω7c). Their G+C contents ranged from 68.0  to 68.6 mol%, and their major isoprenoid quinone was Ubiquinone Q-8. Of these three strains, only strain USMAHM13 (= DSM 25816 = KCTC 32390) was discovered to exhibit yellow pigmentation that is characteristic of the carotenoid family. Their assembled genomes also showed that the three strains were not identical in terms of their genome sizes that were 7.82, 7.95 and 8.70 Mb for strains USMAHM13, USMAA1020 and USMAA2-4, respectively, which are slightly larger than that of Cupriavidus necator H16 (7.42 Mb). The average nucleotide identity (ANI) results indicated that the strains were genetically related and the genome pairs belong to the same species. On the basis of the results obtained in this study, the three strains are considered to represent a novel species for which the name Cupriavidus malaysiensis sp. nov. is proposed. The type strain of the species is USMAA1020T (= DSM 19416T = KCTC 32390T).

Pilot scale production of poly(3-hydroxybutyrate-co-4-hydroxybutyrate) biopolymers with high molecular weight and elastomeric properties.

Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) [(P(3HB-co-4HB)] copolymer receives attention as next generation biomaterial in medical application. However, the exploitation of the copolymer is still constrained since such copolymer has not yet successfully been performed in industrial scale production. In this work, we intended to establish pilot production system of the copolymer retaining the copolymer quality which has recently discovered to have novel characteristic from lab scale fermentation. An increase of agitation speed has significantly improved the copolymer accumulation efficiency by minimizing the utilization of substrates towards cell growth components. This is evidenced by a drastic increase of PHA content from 28 wt% to 63 wt% and PHA concentration from 3.1 g/L to 6.5 g/L but accompanied by the reduction of residual biomass from 8.0 g/L to 3.8 g/L. Besides, fermentations at lower agitation and aeration have resulted in reduced molecular weight and mechanical strength of the copolymer, suggesting the role of sufficient oxygen supply efficiency in improving the properties of the resulting copolymers. The KLa-based scale-up fermentation was performed successfully in maintaining the yield and the quality of the copolymers produced without a drastic fluctuation. This suggests that the scale-up based on the KLa values supported the fermentation system of P(3HB-co-4HB) copolymer production in single-stage using mixed-substrate cultivation strategy.

Enhanced degradation of polyhydroxyalkanoates (PHAs) by newly isolated Burkholderia cepacia DP1 with high depolymerase activity.

The contribution of microbial depolymerase has received much attention because of its potential in biopolymer degradation. In this study, the P(3HB) depolymerase enzyme of a newly isolated Burkholderia cepacia DP1 from soil in Penang, Malaysia, was optimized using response surface methodology (RSM). The factors affecting P(3HB) depolymerase enzyme production were studied using one-variable-at-a-time approach prior to optimization. Preliminary experiments revealed that the concentration of nitrogen source, concentration of carbon source, initial pH and incubation time were among the main factors influencing the enzyme productivity. An increase of 9.4 folds in enzyme production with an activity of 5.66 U/mL was obtained using optimal medium containing 0.028% N of di-ammonium hydrogen phosphate and 0.31% P(3HB-co-21%4HB) as carbon source at the initial pH of 6.8 for 38 h of incubation. Moreover, the RSM model showed great similarity between predicted and actual enzyme production indicating a successful model validation. This study warrants the ability of P(3HB) degradation by B. cepacia DP1 in producing higher enzyme activity as compared to other P(3HB) degraders being reported. Interestingly, the production of P(3HB) depolymerase was rarely reported within genus Burkholderia. Therefore, this is considered to be a new discovery in the field of P(3HB) depolymerase production.