Crystalline Si Surface Passivation with Nafion for Bulk Defects Detection with Electron Paramagnetic Resonance.

In monocrystalline Si (c-Si) solar cells, identification and mitigation of bulk defects are crucial to achieving a high photoconversion efficiency. To spectroscopically detect defects in the c-Si bulk, it is desirable to passivate the surface defects. Passivation of the c-Si surface with dielectrics such as Al2O3 and SiNx requires deposition at elevated temperatures, which can influence defects in the bulk. Herein, we report on the passivation of different Czochralski (Cz) Si wafer surfaces by an organic copolymer, Nafion. We test the efficacy of the surface passivation at temperatures ranging from 6 to 473 K to detect bulk defects using electron paramagnetic resonance (EPR) spectroscopy. By comparing with state-of-the-art passivation layers, including Al2O3 and liquid HF/HCl, we found that at room temperature, Nafion can provide comparable passivation of n-type Cz Si with an implied open-circuit voltage (iVoc) of 713 mV and a recombination current prefactor J0 of 5 fA/cm2. For p-type Cz Si, we obtained an iVoc of 682 mV with a J0 of 22.4 fA/cm2. Scanning electron microscopy and photoluminescence reveal that Nafion can also be used to passivate the surface of c-Si solar cell fragments scribed from a solar cell module by using a laser. Consistent with previous studies, analysis of the EPR spectroscopy data confirms that the H-terminated surface is necessary, and fixed negative charge in Nafion is responsible for the field-effect passivation. While the surface passivation quality was maintained for almost 24 h, which is sufficient for spectroscopic measurements, the passivation degraded over longer durations, which can be attributed to surface SiOx growth. These results show that Nafion is a promising room-temperature surface passivation technique to study bulk defects in c-Si.

Clean-Room Lithographical Processes for the Fabrication of Graphene Biosensors.

This work is on developing clean-room processes for the fabrication of electrolyte-gate graphene field-effect transistors at the wafer scale for biosensing applications. Our fabrication process overcomes two main issues: removing surface residues after graphene patterning and the dielectric passivation of metallic contacts. A graphene residue-free transfer process is achieved by using a pre-transfer, sacrificial metallic mask that protects the entire wafer except the areas around the channel, source, and drain, onto which the graphene film is transferred and later patterned. After the dissolution of the mask, clean gate electrodes are obtained. The multilayer SiO2/SiNx dielectric passivation takes advantage of the excellent adhesion of SiO2 to graphene and the substrate materials and the superior impermeability of SiNx. It hinders native nucleation centers and breaks the propagation of defects through the layers, protecting from prolonged exposition to all common solvents found in biochemistry work, contrary to commonly used polymeric passivation. Since wet etch does not allow the required level of control over the lithographic process, a reactive ion etching process using a sacrificial metallic stopping layer is developed and used for patterning the passivation layer. The process achieves devices with high reproducibility at the wafer scale.