Phosphine Sulfide-Based Bipolar Host Materials for Blue Phosphorescent Organic Light-Emitting Diodes.

Three phosphine sulfide-based bipolar host materials, vizCzPhPS, DCzPhPS, and TCzPhPS, were facilely prepared through a one-pot synthesis in excellent yields. The developed hosts exhibit superior thermal stabilities with the decomposition temperatures (Td) all exceeding 350 °C and the melting temperatures (Tm) over 200 °C. In addition, their triplet energy (ET) levels are estimated to be higher than 3.0 eV, illustrating that they are applicable to serve as hosts for blue phosphorescent organic light-emitting diodes (PhOLEDs). The maxima luminance, current efficiency (CE), power efficiency (PE), and external quantum efficiency (EQE) of 17,223 cd m-2, 36.7 cd A-1, 37.5 lm W-1, and 17.5% are achieved for the blue PhOLEDs hosted by CzPhPS. The PhOLEDs based on DCzPhPS and TCzPhPS show inferior device performance than that of CzPhPS, which might be ascribed to the deteriorated charge transporting balance as the increased number of the constructed carbazole units in DCzPhPS and TCzPhPS molecules would enhance the hole-transporting ability of the devices to a large extent. Our study demonstrates that the bipolar hosts derived from phosphine sulfide have enormous potential applications in blue PhOLEDs, and the quantity of donors should be well controlled to exploit highly efficient phosphine sulfide-based hosts.

High Triplet Energy Level Achieved by Tuning the Arrangement of Building Blocks in Phosphorescent Polymer Backbones for Furnishing High Electroluminescent Performances in Both Blue and White Organic Light-Emitting Devices.

A high triplet energy level (ET) of ca. 2.83 eV has been achieved in a novel polymer backbone through tuning the arrangement of two kinds of building blocks, showing enhanced hole injection/transporting capacity. Based on this new polymer backbone with high ET, both blue and white phosphorescent polymers were successfully developed with a trade-off between high ET and enhanced charge-carrier transporting ability. In addition, their photophysical features, electrochemical behaviors, and electroluminescent (EL) properties have been characterized in detail. Benefitting from the advantages associated with the novel polymer backbone, the blue phosphorescent polymers show top-ranking EL performances with a maximum luminance efficiency (ηL) of 15.22 cd A-1, corresponding to a power efficiency (ηP) of 12.64 lm W-1, and external quantum efficiency (ηext) of 6.22% and the stable Commission Internationale de L'Eclairage (CIE) coordinates of (0.19, 0.38). Furthermore, blue-orange (B-O) complementary-colored white phosphorescent polymers based on this novel polymer backbone were also obtained showing encouraging EL efficiencies of 12.34 cd A-1, 9.59 lm W-1, and 4.10% in the optimized WOLED together with exceptionally stable CIE coordinates of (Δx = 0.014, Δy = 0.010) in a wide driving voltage range from 4 to 16 V. All of these attractive EL results achieved by these novel phosphorescent polymers show the great potential of this new polymer backbone in developing highly efficient phosphorescent polymers.