Effect of water glass treatment for zirconia and silane coupling on bond strength of resin cement.

OBJECTIVE: To evaluate the ability of the water glass treatment to penetrate zirconia and improve the bond strength of resin cement. MATERIAL AND METHODS: Water glass was applied to zirconia specimens, which were then sintered. The specimens were divided into water-glass-treated and untreated zirconia (control) groups. The surface properties of the water-glass-treated specimens were evaluated using surface roughness and electron probe micro-analyser (EPMA) analysis. A resin cement was used to evaluate the tensile bond strength, with2 and without a silane-containing primer. After 24 h in water storage at 37 °C and thermal cycling, the bond strengths were statistically evaluated with t-test, and the fracture surfaces were observed using SEM. RESULTS: The water glass treatment slightly increased the surface roughness of the zirconia specimens, and the EPMA analysis detected the water glass penetration to be 50 µm below the zirconia surface. The application of primer improved the tensile bond strength in all groups. After 24 h, the water-glass-treated zirconia exhibited a tensile strength of 24.8 ± 5.5 MPa, which was significantly higher than that of the control zirconia (17.6 ± 3.5 MPa) (p < 0.05). After thermal cycling, the water-glass-treated zirconia showed significantly higher tensile strength than the control zirconia. The fracture surface morphology was mainly an adhesive pattern, whereas resin cement residue was occasionally detected on the water-glass-treated zirconia surfaces. CONCLUSION: The water glass treatment resulted in the formation of a stable silica phase on the zirconia surface. This process enabled silane coupling to the zirconia and improved the adhesion of the resin cement.

The influence of Zircos-E® etchant, silica coating, and alumina air-particle abrasion on the debonding resistance of endocrowns with three different preparation designs.

OBJECTIVES: The study aimed to evaluate the debonding resistance of three different endocrown designs on molar teeth, using three different zirconia surface pretreatments. MATERIAL AND METHOD: Ninety human mandibular first molars were divided into three main groups: endocrowns without ferrule, with 1 mm ferrule, and with 2 mm ferrule. The subgroups were defined by their surface pretreatment method used (n = 15): 50 µm alumina air-particle abrasion, silica coating using 30 µm Cojet™ particles, and Zircos-E® etching. The endocrowns were fabricated using multilayer zirconia ceramic, cemented with self-adhesive resin cement, and subjected to 5000 thermocycles (5-55°C) before debonding. The data obtained were analyzed using a two-way ANOVA. RESULTS: All test specimens survived the thermocyclic aging. The results indicated that both the preparation design and the surface treatment had a significant impact on the resistance to debonding of the endocrowns (p < .001). The 2 mm ferrule followed by the 1 mm ferrule designs exhibited the highest debonding resistance, both were superior to the endocrown without ferrule. Zircos-E® etching and silica coating yielded comparable debonding resistance, which were significantly higher than alumina air-particle abrasion. All endocrowns demonstrated a favorable failure mode. CONCLUSIONS: All designs and surface treatments showed high debonding resistance for a single restoration. However, ferrule designs with Zircos-E® etching or silica coating may represent better clinical options compared to the nonferrule design or alumina airborne-particle abrasion. Nonetheless, further research, including fatigue testing and evaluations with different luting agents is recommended.

Adhesive Cementation of CAD/CAM Silica-based Ceramics: Effect of Adhesive Type and Long-term Aging on the Bond Strength to Composite Cement.

PURPOSE: To investigate the effect of adhesive type and long-term aging on the shear bond strength (SBS) between silica-based ceramics and composite cement (CC). MATERIALS AND METHODS: Lithium-silicate (LS), feldspathic (FD) and polymer-infiltrated ceramic (PIC) blocks were sectioned (10 x 12 x 2 mm) and divided into 24 groups considering the factors: "ceramics" (LS, FD, and PIC), "adhesive" (Ctrl: without adhesive; 2SC: 2-step conventional; 3SC: 3-step conventional; 1SU: 1-step universal), and "aging" (non-aged or aged [A]). After the surface treatments, CC cylinders (n = 15, Ø = 2 mm; height = 2 mm) were made and half of the samples were subjected to thermocycling (10,000) and stored in water at 37°C for 18 months. The samples were submitted to SBS testing (100 kgf, 1 mm/min) and failure analysis. Extra samples were prepared for microscopic analysis of the adhesive interface. SBS (MPa) data was analyzed by 3-way ANOVA and Tukey's test (5%). Weibull analysis was performed on the SBS data. RESULTS: All factors and interactions were significant for SBS (p<0.05). Before aging, there was no significant difference between the tested groups and the respective control groups. After aging, the LS_1SU (22.18 ± 7.74) and LS_2SC (17.32 ± 5.86) groups exhibited significantly lower SBS than did the LS_Ctrl (30.30 ± 6.11). Only the LS_1SU group showed a significant decrease in SBS after aging vs without aging. The LS_1SU (12.20) group showed the highest Weibull modulus, which was significantly higher than LS_2SC_A (2.82) and LS_1SU_A (3.15) groups. CONCLUSION: No type of adhesive applied after silane benefitted the long-term adhesion of silica-based ceramics to CC in comparison to the groups without adhesive.

Bonding of Composite Cements Containing 10-MDP to Zirconia Ceramics Without Dedicated Ceramic Primer.

PURPOSE: To measure zirconia-to-zirconia microtensile bond strength (µTBS) using composite cements with and without primer. MATERIALS AND METHODS: Two Initial Zirconia UHT (GC) sticks (1.8x1.8x5.0 mm) were bonded using four cements with and without their respective manufacturer's primer/adhesive (G-CEM ONE [GOne] and G-Multi Primer, GC; Panavia V5 [Pv5]), and Panavia SA Cement Universal [PSAu], and Clearfil Ceramic Plus, Kuraray Noritake; RelyX Universal (RXu) and Scotchbond Universal Plus [SBUp], 3M Oral Care). Specimens were trimmed to an hour-glass shaped specimen whose isthmus is circular in cross-section. After 1-week water storage, the specimens were either tested immediately (1-week µTBS) or first subjected to 50,000 thermocycles (50kTC-aged µTBS). The fracture mode was categorized as either adhesive interfacial failure, cohesive failure in composite cement, or mixed failure, followed by SEM fracture analysis of selected specimens. Data were analyzed using linear mixed-effects statistics (α = 0.05; variables: composite cement, primer/adhesive application, aging). RESULTS: The statistical analysis revealed no significant differences with aging (p = 0.3662). No significant difference in µTBS with/without primer and aging was recorded for GOne and PSAu. A significantly higher µTBS was recorded for Pv5 and RXu when applied with their respective primer/adhesive. Comparing the four composite cements when they were applied in the manner that resulted in their best performance, a significant difference in 50kTC-aged µTBS was found for PSAu compared to Pv5 and RXu. A significant decrease in µTBS upon 50kTC aging was only recorded for RXu in combination with SBUp. CONCLUSION: Adequate bonding to zirconia requires the functional monomer 10-MDP either contained in the composite cement, in which case a separate 10-MDP primer is no longer needed, or in the separately applied primer/adhesive.

The effect of freezing on the fracture pattern of adhesive on debonding: an in-vitro study.

The purpose of this study was to quantitatively evaluate adhesive remnants on the enamel surface following bracket debonding using a freezing element. Thirty-six sound premolars were used in this study. In each case, a bracket was bonded onto each tooth with conventional light-cured composite resin and de-bonded after one week. Freezing of the underlying composite through the bracket was performed immediately before debonding with a portable cryosurgical system (-55 °C). Specimens were divided into three groups according to the duration of freezing: a control group without freezing was used as a reference and two interventional groups with different durations of freezing (15 or 40 s). Brackets were removed by using debonding pliers to squeeze the wings of the bracket in an occluso-gingival manner. Adhesive remnants on the tooth were then quantitatively evaluated by stereo-microscopy. Pearson's Chi-squared test was used to investigate the relationship between the proportion of remaining resin and the group of teeth. In the control group, 100% of the composite remained on the enamel surface of all specimens. Significantly less adhesive remnants were found in the intervention groups (p = 0.001 for the 15 s group and p = 0.043 for the 40 s group). There was no significant difference between the two interventions (p = 0.165) in terms of the proportion of remaining adhesive remnants. Freezing of the bracket and the underlying adhesive resin prior to bracket debonding may favorably alter the behavioral pattern of composite fracture, thus reducing the extent of adhesive remnants on the enamel. Increasing the freezing time from 15 to 40 s did not exert significant effects on adhesive remnants following debonding. Further research now needs to investigate the effect of freezing on the mechanical properties of the adhesive remnants and its in-vivo effect on pulp vitality over both short- and long-terms.

Efficacy of seventh generation bonding agents as desensitizers in patients with dentin hypersensitivity: a randomized clinical trial.

BACKGROUND: Dentin hypersensitivity (DH) is one of the most challenging and persistent dental complaints characterized by transient, intense pain triggered by various stimuli. It affects a significant portion of the global population, predominantly those aged 20-40. This study aims to evaluate the desensitizing efficacy of seventh-generation dentin bonding agents (Single Bond Universal by 3 M ESPE and Xeno-V + by Dentsply) against a control group using Bifluorid 12 by Voco in mitigating DH within a month of the follow-up period. METHODS: This was a single-center, parallel-group, double-blind, controlled randomized clinical trial conducted at Dow University of Health Sciences, Karachi, Pakistan. A total of 105 patients with DH were allocated into three groups for this study. The patients were divided into three groups (Single Bond Universal by 3 M ESPE and Xeno-V + by Dentsply) and the control group containing fluoride varnish (Bifluorid 12 by Voco). Discomfort Interval Scale scores and Schiff Cold Air Sensitivity Scale scores were recorded at baseline, immediately after the intervention, after 01 weeks, and after 01 month. RESULTS: All the materials demonstrated a statistically significant reduction in discomfort and sensitivity (DIS scores p-value 0.01) immediately after 01 week and over a period of 01 month after treatment compared with the baseline scores before application, with no single material proving superior over the one-month observation period. The study also provided insights into dental hygiene practices, with a significant majority using a toothbrush and sensitivity patterns, with cold stimuli being the most common cause of sensitivity. CONCLUSION: The study demonstrates that Single Bond Universal, Xeno V+, and Bifluorid 12 are equally effective in reducing dentin hypersensitivity, with no distinct superiority observed over a one-month period. The findings highlight the potential of fluoride varnishes as a less technique-sensitive and cost-effective option for treating DH, offering valuable insights for future research and clinical practice. TRIAL REGISTRATION: NCT04225247 ( https://clinicaltrials.gov/study/NCT04225247 ), Date of Registration: 13/01/2020. (Retrospectively registered).

Effect of light-, chemical-, and dual-cured universal adhesives on the internal adaptation of resin composites to pulpal and gingival internal walls.

PURPOSE: To compare the internal adaptation of restorative systems bonded to mid-coronal and gingival dentin using light-cured, chemical-cured, and dual-cured adhesives, both immediately and after aging. METHODS: 60 molars were selected and received occluso-mesial preparations with dentin gingival margins. Restorations were performed using different restorative systems with light-cured, chemical-cured, and dual-cured adhesives. Internal adaptation was assessed by examining the percentage of continuous margin (%CM) at the pulpal and gingival dentin under a scanning electron microscope at x200 magnification. Half of the teeth were stored in sterile water for 24 hours, while the other half underwent 10,000 thermal cycles. Micro-morphological analysis was conducted on representative samples at x1,000 magnification. RESULTS: The restorative system with light-cured adhesive exhibited significantly lower %CM values at the gingival dentin, particularly after aging. Aging had a negative impact on the %CM values of the pulpal and gingival dentin in restorative systems with light-cured and dual-cured adhesives. Regional dentin variations influenced the %CM values, especially after aging, regardless of the restorative system used. The tested restorative system with chemical-cured adhesive is preferable for achieving improved internal adaptation when bonding to both mid-coronal and gingival dentin, compared to the other tested systems. CLINICAL SIGNIFICANCE: The study highlights the variations in adhesive performance between different regional dentin areas using the tested restorative systems.

Effect of surface treatment and resin cement type on the bond strength of polyetheretherketone to lithium disilicate ceramic.

BACKGROUND: This study aims to evaluate the effect of surface treatment and resin cement on the shear bond strength (SBS) and mode of failure of polyetheretherketone (PEEK) to lithium disilicate ceramic (LDC). This is suggested to study alternative veneering of PEEK frameworks with a ceramic material. METHODS: eighty discs were prepared from PEEK blank and from lithium disilicate ceramic. Samples were divided into four groups according to surface treatment: Group (A) air abraded with 110 µm Al2O3, Group (AP) air abrasion and primer application, Group (S) 98% sulfuric acid etching for 60 s, Group (SP) Sulfuric acid and primer. Each group was subdivided into two subgroups based on resin cement type used for bonding LDC:1) subgroup (L) self- adhesive resin cement and 2) subgroup (B) conventional resin cement (n = 10). Thermocycling was done for all samples. The bond strength was assessed using the shear bond strength test (SBS). Failure mode analysis was done at 50X magnification with a stereomicroscope. Samples were chosen from each group for scanning electron microscope (SEM). The three-way nested ANOVA followed by Tukey's post hoc test were used for statistical analysis of results. Comparisons of effects were done utilizing one way ANOVA and (p < 0.05). RESULTS: The highest mean of shear bond strength values was demonstrated in Group of air abrasion with primer application using conventional resin cement (APB) (12.21 ± 2.14 MPa). Sulfuric acid groups showed lower shear bond strength values and the majority failed in thermocycling especially when no primer was applied. The failure mode analysis showed that the predominant failure type was adhesive failure between cement and PEEK, while the remaining was mixed failure between cement and PEEK. CONCLUSION: The air abrasion followed by primer application and conventional resin cement used for bonding Lithium Disilicate to PEEK achieved the best bond strength. Primer application did not have an effect when self-adhesive resin cement was used in air-abraded groups. Priming step is mandatory whenever sulfuric acid etching surface treatment is utilized for PEEK.

Full-ceramic resin-bonded fixed dental prostheses: A systematic review.

Despite the development of implant-supported prostheses, there are still patients for whom conservative treatments such as resin-bonded fixed dental prostheses (RBFDPs) are more appropriate. This study's objective was to analyze the available research on full-ceramic RBFDPs. In this study, Web of Science, MEDLINE/PubMed, Scopus, Embase, Cochrane Library, and Google Scholar databases were searched for articles published in English between 2010 and 2020. A total of 14 studies were reviewed based on the eligibility criteria. The results showed that using a cantilever design with one abutment had an advantage over two abutments. Additionally, it was proposed that preparations designed with retentive aids, such as a proximal box, groove, and pinhole, could improve RBFDP survival rates. IPS e.max ZirCAD, In-Ceram alumina, and zirconia CAD/CAM were the most commonly used framework materials. Most studies used air abrasion, salinization, or hydrofluoric acid for surface treatment. Adhesive resin cements were the most frequently used type of cement. The survival rate of In-Ceram ceramics (85.3%-94.8%) was lower than that of In-Ceram zirconia and IPS e.max ZirCAD. Debonding, followed by framework fracture, was the leading cause of failure. Following 3-10 years follow-up, the survival percentage of all-ceramic RBFDPs ranged from 76% to 100%. Although RBFDPs have demonstrated satisfactory success as a conservative treatment, long-term follow-ups and higher sample sizes in clinical research are required to gain more reliable outcomes on the clinical success rate of various RBFDP designs.

The multi-luting concept: a new approach to facilitate the adhesive luting of multiple indirect restorations.

Bonded indirect restorations can be difficult to lute in an accurate position due to the lack of preparation geometry. Furthermore, while the use of a rubberdam has been proven to be the best technique for providing the most efficient conditions for adhesive luting, its use often requires the use of secondary clamps, which do not allow the operator to lute more than two prosthetic pieces at the same time. The multi-luting concept is a pragmatic approach that of- fers the possibility to deliver several, if not all restorations, to be bonded at the same time, thus ensuring their correct positioning.

Does surface priming increase the bond strength of orthodontic brackets? An experimental study.

OBJECTIVE: To evaluate the effects of metal primer II (MP II) on the shear bond strength (SBS) of orthodontic brackets bonded to teeth and bis-acryl composite provisional material (Bis-Acryl). MATERIAL AND METHODS: Twenty extracted human premolars specimens and 20 premolar shaped Bis-Acryl specimens were obtained and randomly divided into two surface groups. The first group consisted of human premolars (T) bonded to brackets in the conventional way while in the second (T-MP) MP II was applied on the bracket base before bonding. Similarly, one group of provisional material (PM) was prepared according to conventional treatment and another with the application of MP-II metal bonder (PM-MP). In all cases Ortho-brackets (Victory Series, 3 M) were bonded employing Transbond XT resin cement. Then the brackets were debonded under shear and the results were statistically analyzed by two-way analysis of variance and Holm Sidak at α = .05. The debonded surfaces of all specimens were examined by light microscopy and the Adhesive Remnant Index (ARI) was recorded. RESULTS: The SBS results exhibited significant differences er (p < .001). For both the T and TM the application of MP-II increased the SBS compared to respective control groups (p < .001). The T-C group was found inferior compared to PM-C (p < .001) and the same is true for the comparison between T-MP and PM-MP (p < .001). ARI indexes demonstrated that the tooth groups were characterized by a predominantly adhesive failure at the resin-dentin interface. In contrast, the control group for provisional crowns (PM-C) showed a predominantly cohesive failure mode, which moved to predominantly adhesive after the application of MP II. CONCLUSION: The application of MP II enhances the SBS on both, human enamel and provisional crown materials.

Effect of Various Surface Treatments of Zirconia on its Adhesive Properties to Dentin: An In Vitro Study.

AIM: To assess the effectiveness of various surface treatments and adhesives on the bond strength of zirconia-based ceramic to dentin. MATERIALS AND METHODS: Eighty samples of zirconia were subjected to the four-surface treatment protocols (sandblasting, 48% hydrofluoric acid (HF), 48% hydrofluoric acid + 70% nitric acid (HNO3) and no treatment (control) following which the samples from each group were subdivided into two subgroups (n = 10) based on the resin cement employed for cementation (RelyX U200 and G-Cem Linkforce). The bonded specimens were subjected to shear stress to measure the bond strength using Universal testing machine. To test the difference in bond strength among the eight study groups, the Kruskal-Wallis ANOVA test was applied and for comparison between cements in each group, Mann-Whitney U test was applied. RESULTS: The highest bond strength values were observed for 48% HF group cemented with G-Cem Linkforce resin cement (16.220 ± 1.574) and lowest for control group-RelyX (4.954 ± 0.972). G-Cem cement showed higher bond strength than RelyX for all surface treatments except 48% HF + 70% nitric acid. CONCLUSION: It can be inferred that 48% HF can etch zirconia and generate a porous structure that proves to be beneficial for bonding. CLINICAL SIGNIFICANCE: The increasing demand for esthetics has led to the replacement of metal-ceramic materials with zirconia-based ceramics. However, the chemical inertness of zirconia to various conventional surface treating agents has continuously challenged researchers to discover a new surface treatment protocol that could enhance the bond strength of zirconia. How to cite this article: Yenamandra MS, Joseph A, Singh P, et al. Effect of Various Surface Treatments of Zirconia on its Adhesive Properties to Dentin: An In Vitro Study. J Contemp Dent Pract 2024;25(3):226-230.

A new method of adhesive system application improves the bond strength between fiber post and root dentin.

This study evaluated a new method of adhesive system application on the bond strength between fiber post and root dentin using two adhesive systems. The canals of sixty bovine incisors were prepared and obturated. The roots were divided into six groups (n=10) according to the adhesive system (Clearfil SE - CSE and Single Bond Universal - SBU) and the application strategy (microbrush - MB; rotary brush - RB; and ultrasonic tip - US). The glass fiber posts were cemented with resin cement (RelyX ARC). The roots were sectioned perpendicularly to their long axis, and three slices per root were obtained. Previously to the push-out test, confocal laser scanning microscopy (CLSM) was performed to illustrate the interfacial adaptation of the cement to the root canal walls. Failure patterns were analyzed with 40x magnification. Shapiro-Wilk indicated a normal distribution of the data. The bond strength values were compared using one-way ANOVA and Tukey's tests. Student's T test analyzed the differences between the adhesive systems within each third and protocol. A significance level of 5% was used. CSE with RB showed higher mean bond strength values compared to MB (conventional technique) (P < 0.05). US application resulted in intermediate bond strength values for CSE (P > 0.05). The application of SBU using RB generated higher mean bond strength values compared to MB and US (P < 0.05). Adhesive failures were predominant (65.5%). CSE and SBU application with the new rotary brush improved the bond strength of fiber posts to root dentin compared to the conventional strategy.

Evaluation of Microbiological Susceptibility and Long-term Adhesive Properties to Dentin of Primers with Terminalia catappa Linn.

PURPOSE: To investigate the antibacterial effects of Terminalia catappa Linn (TCL) leaf extracts at different concentrations and the effects of these extracts used as primers on the long-term adhesive properties of two universal adhesives. MATERIALS AND METHODS: After extract preparation, the antimicrobial and antibacterial activities of TCL against Streptococcus mutans (UA 159) were assessed in microdilution assays to provide the minimal inhibitory concentration (MIC) and minimal bactericidal concentration (MBC). Additionally, to provide quantitative data on the ability of TCL extract to reduce cell viability, colony forming units (CFU) were counted. To examine adhesive properties, 288 human molars were randomly assigned to 32 experimental conditions (n = 9) according to the following variables: (1) treatment agent: negative control (untreated surface), and primers at concentrations of 1xMIC, 5xMIC, and 10xMIC; (2) adhesives: Scotchbond Universal (SBU) and Futurabond Universal (FBU); (3) adhesive strategy: etch-and-rinse (ER) or self-etch (SE); and (4) storage time: 24 h or after 2 years. Primers were applied for 60 s, upon which the teeth were incrementally restored and sectioned into adhesive-dentin bonded sticks. These were tested for microtensile bond strength (µTBS) and nanoleakage (NL) after 24-h and 2-year water storage, as well as in-situ degree of conversion (DC) at 24 h. The chemical profile of the hybrid layer was determined via micro-Raman spectroscopy. Biofilm assay data were analyzed using the Kruskal-Wallis test; the pH of culture media and the chemical profile were analyzed by one-way ANOVA. The adhesive properties (µTBS, NL, DC) were evaluated using a four-way ANOVA and Tukey's test. Significance was set at 5%. RESULTS: Similar values of MIC and MBC were observed (2 mg/ml), showing bactericidal potential. CFU analysis demonstrated that concentrations of 5xMIC and 10xMIC significantly inhibited biofilm formation (p < 0.001). The application of the TCL primer at all concentrations significantly increased the immediate µTBS and DC, and decreased the immediate NL values when compared to the control group (p < 0.05), regardless of the adhesive and adhesive strategies. Despite an increase in the NL values for all groups after 2 years (p > 0.05), in groups where the TCL primer was applied, the µTBS remained constant after 2 years for both adhesives, while a decrease in the µTBS was observed in the control groups (p < 0.05). Usually, 10xMIC showed better results than 1xMIC and 5xMIC (p < 0.05). The application of TCL promoted cross-linking; cross-linking rates increased proportionally to the concentration of TCL (p < 0.05). CONCLUSION: Primers containing TCL promoted bactericidal and bacteriostatic action, as well as cross-linking with dentin, while maintaining the adhesive properties of the adhesive-dentin interface after 2 years of water storage.

Bonding Effectiveness of Saliva-Contaminated Monolithic Zirconia Ceramics Using Different Decontamination Protocols.

Objective: This research study investigated the effect of new decontamination protocols on the bonding capacity of saliva-contaminated monolithic zirconia (MZ) ceramics cemented with two different monomer-containing self-adhesive resin cements. Materials and Methods: Standardized tooth preparations (4 mm. axial height) were performed for eighty human maxillary premolars under constant water cooling system. Eighty monolithic zirconia crowns (Whitepeaks Supreme Monolith) (n = 8/10 groups) were manufactured by CAD-CAM. Specimens were kept in the artificial saliva at pH = 7.3 for 1 minute at 37°C except control groups. The specimens have not been prealumina blasted and grouped according to cleaning methods and resin cements: control groups (C) (no saliva contamination + GPDM + 4-META (N) (CN) and 10-MDP (M) containing resin cement (CM), alumina blasted (AL) + GPDM + 4-META (ALN) and 10-MDP containing resin cement (ALM), zirconium oxide containing universal cleaning agent (IC) applied + GPDM + 4-META (N) (ICN) and 10-MDP containing resin cement (ICM), pumice (P) applied + GPDM + 4-META (PN) and 10-MDP containing resin cement (PM), and air-water spray (AW) applied + GPDM + 4-META (AWN) and 10-MDP containing resin cement (AWM)). Monobond Plus was applied to all surfaces for 40 seconds before cementation. The thermal cycle was applied at 5,000 cycles after cementation. The crowns were tested in tensile mode at a speed of 1 mm/min. The mode of failure was recorded. SEM examinations were carried out at different magnifications. Data were analyzed using rank-based Kruskal-Wallis and Mann-Whitney tests. Results: No significant differences were found between the surface treatments and between the two types of resin cements. Interaction effects between surface treatments and resin cements were found to be significant by two-way ANOVA analysis. ICM group resulted in significantly better bond strength results compared with CN. ICM was found to result in better bond strength results compared with PM. The combination of universal cleaning agent and 10-MDP containing resin cement had significantly the highest cementation bond strength values. The increasing order of mean tensile bond strength values of decontamination protocols was C < AW < P < AL < IC. The mean tensile bond strength of 10-MDP containing resin cement was slightly higher than GPDM + 4-META containing resin cement. Conclusions: Universal cleaning agents can be preferred as an efficient cleaning method with 10-MDP-containing cement after saliva contamination for better adhesive bond strength of 4 mm crown preparation height of monolithic zirconia ceramics.

Formulation of arginine-loaded mesoporous silica nanoparticles (Arg@MSNs) modified orthodontic adhesive.

OBJECTIVES: The objective of this study was to synthesize arginine loaded mesoporous silica nanoparticles (Arg@MSNs), develop a novel orthodontic adhesive using Arg@MSNs as modifiers, and investigate the adhesive performance, antibacterial activity, and biocompatibility. METHODS: Arg@MSNs were synthesized by immobilizing arginine into MSNs and characterized using transmission electron microscope (TEM), dynamic light scattering (DLS), and Fourier Transform Infrared Spectrometer (FT-IR). Arg@MSNs were incorporated into Transbond XT adhesive with different mass fraction to form functional adhesives. The degree of conversion (DC), arginine release behavior, adhesive performance, antibacterial activity against Streptococcus mutans biofilm, and cytotoxicity were comprehensively evaluated. RESULTS: TEM, DLS, and FT-IR characterizations confirmed the successful preparation of Arg@MSNs. The incorporation of Arg@MSNs did not significantly affect DC and exhibited clinically acceptable bonding strength. Compared to the commercial control, the Arg@MSNs modified adhesives greatly suppressed the metabolic activity and polysaccharide production while increased the biofilm pH values. The cell counting kit (CCK)-8 test indicated no cytotoxicity. CONCLUSIONS: The novel orthodontic adhesive containing Arg@MSNs exhibited significantly enhanced antibacterial activities and inhibitory effects on acid production compared to the commercial adhesive without compromising their bonding strength or biocompatibility. CLINICAL SIGNIFICANCE: The novel orthodontic adhesive containing Arg@MSNs exhibits potential clinical benefits in preventing demineralization of enamel surfaces around or beneath orthodontic brackets due to its enhanced antibacterial activities and acid-producing inhibitory effects.

A scoping review of the influence of clinical contaminants on bond strength in direct adhesive restorative procedures.

OBJECTIVE: Clinical contamination during direct adhesive restorative procedures can affect various adhesive interfaces differently and contribute to bulk failure of the restorations. This review aims to summarise the current knowledge on the influence of a variety of clinical contaminants on the bond strength at various adhesive interfaces during adhesive restorative procedures and identify gaps in the literature for future research. DATA AND SOURCES: An electronic database search was performed in PubMed and EMBASE to identify articles that investigated the influence of contaminants on direct restorative bonding procedures. A data-charting form was developed by two researchers to capture the key characteristics of each eligible study. STUDY SELECTION: The initial search yielded 1,428 articles. Fifty-seven articles published between 1 Jan 2007 and 25 Oct 2023 were included in the final review. Thirty-three of the articles examined the influence of saliva contamination, twelve articles examined the influence of blood contamination, and twenty-five articles examined the influence of other contaminants. CONCLUSION: Saliva contamination exerted less influence on the decrease in bond strength when self-etch systems were used, compared to when etch-and-rinse systems were used. Blood contamination adversely affected the bond strength at the interface between resin composite and dentine, and resin composite and resin-modified glass ionomer cement. Treating contaminated surfaces with water spray for 10-30 s followed by air drying could be effective in recovering bond strength following saliva and blood contamination. CLINICAL SIGNIFICANCE: This scoping review provides a valuable overview of the range of potential clinical contaminants that can influence the bond strength between different interfaces in direct adhesive restorative procedures. Additionally, it identifies potential decontamination protocols that can be followed to restore and enhance bond strength.

Differences in birch tar composition are explained by adhesive function in the central European Iron Age.

Birch bark tar is the most widely documented adhesive in prehistoric Europe. More recent periods attest to a diversification in terms of the materials used as adhesives and their application. Some studies have shown that conifer resins and beeswax were added to produce compound adhesives. For the Iron Age, no comparative large-scale studies have been conducted to provide a wider perspective on adhesive technologies. To address this issue, we identify adhesive substances from the Iron Age in north-eastern France. We applied organic residue analysis to 65 samples from 16 archaeological sites. This included residues adhering to ceramics, from vessel surface coatings, repaired ceramics, vessel contents, and adhesive lumps. Our findings show that, even during the Iron Age in north-eastern France, birch bark tar is one of the best-preserved adhesive substances, used for at least 400 years. To a lesser extent, Pinaceae resin and beeswax were also identified. Through statistical analyses, we show that molecular composition differs in samples, correlating with adhesive function. This has implications for our understanding of birch bark tar production, processing and mode of use during the Iron Age in France and beyond.

[Effect of different cleaning methods on bond strength and surface wettability of high translucency zirconia].

PURPOSE: To study the effect of different cleaning methods on the shear bond strength of self-adhesive resin cement to saliva-contaminated high translucency zirconia and surface wettability. METHODS: Eighty zirconia specimens were randomly divided into 5 groups (n=16), i.e., control group(not contaminated), 75% ethanol group,cleaning paste group,airborne-particle abrasion group, and atmospheric pressure cold plasma group. The contact angles was measured, shear bond strength were examined, and fracture types were determined. SPSS 26.0 software package was used for statistical analysis of the data. RESULTS: The atmospheric pressure cold plasma group produced the lowest contact angle(P＜0.05). The shear bond strength of the airborne-particle abrasion group, the cleaning paste group and the atmospheric pressure cold plasma group respectively were similar to the control group without significant difference(P＞0.05), while those were significantly higher than 75% ethanol group(P＜0.05). The mixed fracture mode of the atmospheric pressure cold plasma group evidently increased. CONCLUSIONS: Airborne-particle abrasion, cleaning paste and atmospheric pressure cold plasma overcome the effects of saliva contamination, producing the shear bond strength to zirconia similar to the control group. The atmospheric pressure cold plasma improves hydrophilicity of high translucency zirconia significantly.

Effects of different primers and colouring solutions on orthodontic bonding: shear bond strength and colour change.

OBJECTIVES: This in vitro study evaluated the effect of different colouring solutions and primer systems used in the bonding of brackets on enamel colour change and bond strength. MATERIALS AND METHODS: 120 premolar teeth were divided into four main groups; brackets were bonded with 37% orthophosphoric acid + Transbond XT Primer in Group 1, 3 M Single Bond Universal in Group 2, Transbond Plus SEP in Group 3, and G-Premio Bond in Group 4. Each group was divided into three subgroups, and the teeth were placed in a cup containing coffee and tea mixture, in a cup containing cola and in distilled water. A bond strength test was applied to all teeth. Colour measurements of all teeth were performed at 2 different times: before bonding and after the bond strength test. RESULTS: The average bond strength of the 37% orthophosphoric acid group was higher than that of the other groups. The effect of primer and solution groups on colour change was statistically significant (p = 0.001 and p = 0.023, respectively). CONCLUSIONS: In this study, the bond strength was clinically sufficient in all primer groups. The highest colour change was observed when the tea-coffee solution and Transbond Plus SEP primer were used. CLINICAL RELEVANCE: This study has identified enamel discoloration and bond strength from different colouring solutions and primer systems used for bonding braces, which can be used to inform clinicians and patients to achieve better treatment results.