The Influence of Surface Modification on the Photoluminescence of CdTe Quantum Dots: Realization of Bio-Imaging via Cost-Effective Polymer.

To impart biocompatibility, stability, and specificity to quantum dots (QDs)-and to reduce their toxicity-it is essential to carry out surface modification. However, most surface-modification processes are costly, complicated, and time-consuming. In addition, the modified QDs often have a large size, which leads to easy aggregation in biological environments, making it difficult to excrete them from in vivo systems. To solve these problems, three kinds of conventional polymers, namely, polyvinyl alcohol (PVA, neutral), sodium polystyrene sulfonate (PSS, negative charged), and poly(diallyl dimethyl ammonium chloride) (PDDA, positive charged) were selected to modify the surface of QDs at low cost via a simple process in which the size of the QDs was kept small after modification. The effect of polymer modification on the photoluminescence (PL) properties of the QDs was systematically investigated. High quantum yields (QYs) of 65 % were reached, which is important for the realization of bio-imaging. Then, the cytotoxicity of CdTe QD-polymer composites was systematically investigated via MTT assay using the Cal27 and HeLa cell lines, especially for high concentrations of QD-polymer composites in vitro. The experimental results showed that the cytotoxicity decreased in the order CdTe-PDDA>CdTe>CdTe-PSS>CdTe-PVA, indicating that PSS and PVA can reduce the toxicity of the QDs. An obvious cytotoxicity of CdTe-PVA and CdTe-PSS was present until 120 h for the Cal27 cell line and until 168 h for the HeLa cell line. At last, the Cal27 cell line was selected to realize bio-imaging using CdTe-PSS and CdTe-PVA composites with different emission colors under one excitation wavelength.

Scalable economic extracellular synthesis of CdS nanostructured particles by a non-pathogenic thermophile.

We report microbially facilitated synthesis of cadmium sulfide (CdS) nanostructured particles (NP) using anaerobic, metal-reducing Thermoanaerobacter sp. The extracellular CdS crystallites were <10 nm in size with yields of ~3 g/L of growth medium/month with demonstrated reproducibility and scalability up to 24 L. During synthesis, Thermoanaerobacter cultures reduced thiosulfate and sulfite salts to H2S, which reacted with Cd²âº cations to produce thermodynamically favored NP in a single step at 65 °C with catalytic nucleation on the cell surfaces. Photoluminescence (PL) analysis of dry CdS NP revealed an exciton-dominated PL peak at 440 nm, having a narrow full width at half maximum of 10 nm. A PL spectrum of CdS NP produced by dissimilatory sulfur reducing bacteria was dominated by features associated with radiative exciton relaxation at the surface. High reproducibility of CdS NP PL features important for scale-up conditions was confirmed from test tubes to 24 L batches at a small fraction of the manufacturing cost associated with conventional inorganic NP production processes.