Effect of treatment with phosphate, casein phosphopeptide and fluoride on the remineralization: in vitro study.

This study aimed to evaluate in vitro the effect protocols and anticaries agents containing casein amorphous calcium fluoride phosphopeptide-phosphate (CPP-ACPF, MI Paste Plus), sodium trimetaphosphate (TMP) and fluoride (F), in remineralization of caries lesions. Bovine enamel blocks with initial caries lesions were divided into groups (n = 12): 1) Toothpaste without F-TMP-MI Plus (Placebo); 2) Toothpaste 1100 ppm F (1100F), 3) 1100F + MI Paste Plus (1100F-MI Paste Plus), 4) Toothpaste with 1100F + Neutral gel with 4,500 ppm F + 5%TMP (1100F + Gel TMP) and 5) Toothpaste with 1100F + Neutral gel with 9,000 ppm F (1100F + Gel F). For the 4 and 5 groups the gel was applied only once for 1 minute, initially to the study. For the 3 group, after treatment with 1100F, MI Paste Plus was applied 2x/day for 3 minute. After pH cycling, the percentage of surface hardness recovery (%SHR); integrated loss of subsurface hardness (ΔKHN); profile and depth of the subsuperficial lesion (PLM); concentrations of F, calcium (Ca) and phosphorus (P) in enamel was determined. The data were analyzed by ANOVA (1-criterion) and Student-Newman-Keuls test (p < 0.001). Treatment with 1100F alone led to ~ 28% higher remineralization when compared to treatment with 1100F associated with MI Paste Plus (p < 0.001). The 1100F and 1100F + Gel F groups showed similar values for %SHR (p = 0.150). 1100F + Gel TMP treatment also remineralized the enamel surface by ~ 30% and 20% when compared to the 1100F + Gel F and 1100F groups (p < 0.001). The lower lesion depth (ΔKHN) was observed for the 1100F + Gel TMP group (p < 0.001), where it was 54% and 44% lower in comparison to the 1100F and 1100F + Gel F groups (p < 0.001). Polarized light microscopy photomicrographs showed subsurface lesions in all groups, but these lesions were present to a lower extent in the 1100F + Gel TMP group (p < 0.001). Treatment with 1100F + Gel TMP promoted an increase in the concentration of Ca in the enamel by ~ 57% and ~ 26% when compared to the 1100F and 1100F + MI Paste Plus groups (p < 0.001), respectively. There were no significant differences between the 1100F, 1100F + MI Paste Plus and 1100F + Gel F groups (p > 0.001). Similar values of P in the enamel were observed in the 1100F, 1100F + MI Paste Plus and 1100F + Gel F groups (p > 0.001), except for the 1100F + Gel TMP group, which presented a high concentration (p < 0.001). We conclude that the 1100F+TMP gel treatment/protocol led to a significant increased remineralization when compared to the other treatments/protocols and may be a promising strategy for patients with early caries lesions.

Effect of phosphate group on remineralization of early enamel caries regulated by amelogenin peptide.

OBJECTIVE: To show the effect of the phosphate group on the remineralization process of early enamel caries mediated by amelogenin peptide. METHODS: Freshly extracted, completed, and crack-free bovine teeth were used to create artificial early enamel caries, which were randomly divided into four groups: Group A: fluorination remineralized solution treatment group; Group B: pure remineralized solution treatment group. Group C: 100 g/ml recombinant Amelogenin peptide remineralized solution treatment group (with single phosphate group on N-terminus); Group D: 100 g/ml non-phosphorylated recombinant Amelogenin peptide remineralized solution treatment group (without single phosphate group on N-terminus). For 12 days, fresh remineralized solutions were replaced daily. Transverse microradiography (TMR) was used after remineralization to determine mineral loss and demineralization depth before and after each sample's remineralization. Each sample's depth of remineralization and mineral acquisition were then determined. RESULTS: The recombinant amelogenin peptide group significantly outperformed the non-phosphorylated amelogenin peptide group in terms of mineral acquisition and mineralization depth (P<0.05). CONCLUSIONS: The recombinant Amelogenin's solitary phosphate group at the N-terminus helps recombinant Amelogenin to encourage the remineralization process of early enamel caries.

Comparative evaluation of probiotic solutions on surface roughness and microhardness of different restorative materials and enamel.

This research study aimed to investigate the impact of probiotic mouthwash and kefir on the surface characteristics, specifically surface roughness and microhardness, of different restorative materials, as well as permanent and deciduous tooth enamels. Thirty disc-shaped specimens were prepared from composite resin (G-ænial Posterior (GP)), polyacid-modified composite resin (compomer) (Dyract-XP (DXP)), and resin-modified glass ionomer cement (Ionoseal (IS)). Additionally, thirty specimens of enamel were obtained from permanent teeth (PT) and thirty from deciduous teeth (DT) by embedding buccal and lingual sections, acquired through vertical sectioning of 15 permanent and 15 deciduous human tooth crowns in the mesiodistal orientation within acrylic resin blocks. The specimens were then categorized into three distinct groups and immersed for 14 days in one of the following solutions: distilled water, kefir or probiotic mouthwash. The mean surface roughness values of all specimens were assessed using an atomic force microscope, while the mean surface microhardness was measured using a Vickers hardness measuring instrument. The results revealed a statistically significant difference in mean surface roughness among the various restorative materials (p < 0.001). Among the restorative materials, the IS material exhibited notably higher mean surface roughness values than other restorative materials and tooth enamel, while no significant differences were observed between the PT and DT groups. Importantly, the main effect of the solutions under investigation was not statistically significant (p = 0.208). No significant difference was found between the surface roughness values of specimens subjected to the different solutions. When evaluating the effects of materials and solutions on microhardness, the main effects of material and solution variables and the influence of material-solution interactions were statistically significant (p < 0.001). Taken together, these results indicate that consistent use of kefir or probiotic mouthwashes may impact the surface properties of various restorative materials and tooth enamel.

Effect of fluoride or chitosan toothpaste and at-home bleaching in enamel roughness, tooth color, and staining susceptibility.

PURPOSE: To evaluate how fluoride- or chitosan-based toothpaste used during at-home bleaching affects enamel roughness, tooth color, and staining susceptibility. METHODS: Bovine enamel blocks were submitted to a 14-day cycling regime considering a factorial design (bleaching agent x toothpaste, 2 x 3), with n=10: (1) bleaching with 16% carbamide peroxide (CP) or 6% hydrogen peroxide (HP), and (2) daily exposure of a fluoride (1,450 ppm F-NaF) toothpaste (FT), chitosan-based toothpaste (CBT), or distilled water (control). Then, 24 hours after the last day of bleaching procedure the samples were exposed to a coffee solution. Color (ΔEab, ΔE00, L*, a*, b*) and roughness (Ra, µm) analyses were performed to compare the samples initially (baseline), after bleaching, and after coffee staining. The results were evaluated by linear models for repeated measures (L*, a*, b*, and Ra), 2-way ANOVA (ΔEab, ΔE00) and Tukey's test (α= 0.05). RESULTS: After the at-home bleaching procedure (toothpaste vs. time, P< 0.0001), the toothpaste groups presented a statistically lower Ra than the control (CBT 0.05). After coffee exposure, CBT presented lower ΔEab and ΔE00 values in the HP groups (toothpaste, P< 0.0001), and lower b* and a* values in the CP groups (toothpaste vs. time, P= 0.004). CLINICAL SIGNIFICANCE: Fluoride or chitosan delivered by toothpaste can reduce surface alterations of the enamel during at-home bleaching, without affecting bleaching efficacy.

Enamel remineralisation prospect of Moringa Oleifera hydrogel, eggshell hydrogel versus sodium fluoride varnish on artificially demineralised primary teeth: in vitro study.

PURPOSE: The purpose of the present in vitro study is to investigate and compare the remineralising potential of Moringa Oleifera extract, eggshell, and sodium fluoride varnish on microhardness of artificially demineralised enamel of primary teeth with biomimetic minimally invasive approach following the world paradigm shift towards natural products in paediatric dentistry. MATERIAL AND METHODS: Sample size included 44 primary molars. The mineral content and surface microhardness of all specimens were initially assessed using energy dispersive x-ray examination (EDX) and Vickers microhardness. The specimens were artificially demineralised for 96 h at a temperature of 37°C and then reassessed directly after demineralisation. The demineralised enamel specimens were randomly divided into four groups according to the remineralisation regimen utilised. Group 1: Artificial saliva (control); Group 2: Sodium fluoride varnish; Group 3: Eggshell hydrogel; and Group 4: Moringa Oleifera hydrogel. The specimens were stored for 8 days and then subsequently evaluated using EDX and microhardness assessment by Vickers microhardness test and scanning electron microscope (SEM).  Results: Regarding the microhardness test, there was a significant difference between the Moringa Oleifera group and Eggshell group compared to fluoride varnish (p < 0.05). Regarding EDX analysis, there was a statistically significant difference (p < 0.05) between Moringa Oleifera group and Eggshell group compared to fluoride varnish as the highest values were for Moringa Oleifera and Eggshell. On the other hand, there was no statistically significant difference (p > 0.05) between Moringa Oleifera and Eggshell in both the measurements. CONCLUSION: Moringa Oleifera and Eggshell might be considered as a biomimetic natural material capable of guiding enamel tissue remineralisation in early carious lesion of primary teeth. CLINICAL RELEVANCE: This research demonstrated the capability for early enamel caries to be remineralised using novel materials with a naturally counterpart implicated in biomineralisation as proved to be more effective than traditionally used fluoride varnish in primary teeth.

Does surface priming increase the bond strength of orthodontic brackets? An experimental study.

OBJECTIVE: To evaluate the effects of metal primer II (MP II) on the shear bond strength (SBS) of orthodontic brackets bonded to teeth and bis-acryl composite provisional material (Bis-Acryl). MATERIAL AND METHODS: Twenty extracted human premolars specimens and 20 premolar shaped Bis-Acryl specimens were obtained and randomly divided into two surface groups. The first group consisted of human premolars (T) bonded to brackets in the conventional way while in the second (T-MP) MP II was applied on the bracket base before bonding. Similarly, one group of provisional material (PM) was prepared according to conventional treatment and another with the application of MP-II metal bonder (PM-MP). In all cases Ortho-brackets (Victory Series, 3 M) were bonded employing Transbond XT resin cement. Then the brackets were debonded under shear and the results were statistically analyzed by two-way analysis of variance and Holm Sidak at α = .05. The debonded surfaces of all specimens were examined by light microscopy and the Adhesive Remnant Index (ARI) was recorded. RESULTS: The SBS results exhibited significant differences er (p < .001). For both the T and TM the application of MP-II increased the SBS compared to respective control groups (p < .001). The T-C group was found inferior compared to PM-C (p < .001) and the same is true for the comparison between T-MP and PM-MP (p < .001). ARI indexes demonstrated that the tooth groups were characterized by a predominantly adhesive failure at the resin-dentin interface. In contrast, the control group for provisional crowns (PM-C) showed a predominantly cohesive failure mode, which moved to predominantly adhesive after the application of MP II. CONCLUSION: The application of MP II enhances the SBS on both, human enamel and provisional crown materials.

Inhibition of incipient caries lesion progression by different fluoridated varnishes.

The aim of this in vitro study was to evaluate the potential of different fluoridated varnishes to inhibit the progression of incipient caries lesions after cariogenic challenge. Seventy-five enamel specimens of bovine teeth were prepared and selected based on the initial surface microhardness (SMH). The specimens were first subjected to artificial demineralization (in buffer solution) after which SMH was re-analyzed (SM1). They were then randomly assigned to five experimental groups: 1- CONTROL (pH cycling), 2 - MI VAR (MI Varnish with RECALDENTTM - CPP-ACP), 3 - PROFL (Profluorid®), 4 - CLIN (ClinproTM White Varnish with TCP), and 5 - DUR (Duraphat®) (n=15). The varnishes were applied in a thin layer and the specimens were then subjected to pH cycling for eight days. The SMH and cross-sectional microhardness (CSMH) were then analyzed (SM2). The fluoride and calcium ion concentrations in the solution were analyzed by the indirect method and atomic absorption spectrophotometry, respectively. Data were statistically analyzed by Student's t-test, ANOVA/Tukey-Kramer, or Kruskall-Wallis/Dunn tests for individual comparisons (p˂0.05). All varnishes led to significantly higher surface and subsurface remineralization compared with the control group but did not differ from each other. The varnishes with the highest fluoride release were: PROFL and CLIN, followed by MI VAR and DUR. The varnishes with significantly higher release of calcium were: DUR, CLIN, and PROFL. In conclusion, all commercial fluoridated varnishes tested have good potential to inhibit the progression of demineralization, regardless of the ion release mechanisms.

Arginine and sodium fluoride affect the microbial composition and reduce biofilm metabolism and enamel mineral loss in an oral microcosm model.

OBJECTIVE: To assess the effects of arginine, with or without sodium fluoride (NaF; 1,450 ppm), on saliva-derived microcosm biofilms and enamel demineralization. METHODS: Saliva-derived biofilms were grown on bovine enamel blocks in 0.2 % sucrose-containing modified McBain medium, according to six experimental groups: control (McBain 0.2 %); 2.5 % arginine; 8 % arginine; NaF; 2.5 % arginine with NaF; and 8 % arginine with NaF. After 5 days of growth, biofilm viability was assessed by colony-forming units counting, laser scanning confocal microscopy was used to determine biofilm vitality and extracellular polysaccharide (EPS) production, while biofilm metabolism was evaluated using the resazurin assay and lactic acid quantification. Demineralization was evaluated by measuring pH in the culture medium and calcium release. Data were analyzed by Kruskal-Wallis' and Dunn's tests (p < 0.05). RESULTS: 8 % arginine with NaF showed the strongest reduction in total streptococci and total microorganism counts, with no significant difference compared to arginine without NaF. Neither 2.5 % arginine alone nor NaF alone significantly reduced microbial counts compared to the control, although in combination, a reduction in all microbial groups was observed. Similar trends were found for biofilm vitality and EPS, and calcium released to the growth medium. CONCLUSIONS: 8 % Arginine, with or without NaF, exhibited the strongest antimicrobial activity and reduced enamel calcium loss. Also, NaF enhanced the effects of 2.5 % arginine, yielding similar results to 8 % arginine for most parameters analyzed. CLINICAL SIGNIFICANCE: The results provided further evidence on how arginine, with or without NaF, affects oral microcosm biofilms and enamel mineral loss.

In vitro effect of fluoride gels supplemented with nano-sized sodium trimetaphosphate on enamel erosive wear.

OBJECTIVE: To assess the protective effect of fluoride (F) gels supplemented with micrometric or nano-sized sodium trimetaphosphate (TMPmicro and TMPnano, respectively) against enamel erosion in vitro. METHODS: Bovine enamel blocks (n = 140) were selected according to their surface hardness, and randomly divided into seven groups (n = 20/group), according to the gels tested: Placebo (without F/TMP), 4,500 µg F/g (4500F), 9,000 µg F/g (9000F), 4500F plus 2.5 % TMPnano (2.5 % Nano), 4500F plus 5 % TMPnano (5 % Nano), 4500F plus 5 % TMPnano (Micro 5 %) and 12,300 µg F/g (Acid gel). Blocks were treated once during one minute with the gels, and submitted to erosive (ERO, n = 10/group) or erosive plus abrasive (ERO+ABR, n = 10/group) challenges 4 times/day, for 90 s for each challenge (under reciprocating agitation), during consecutive 5 days. Blocks were analyzed by profilometry, and by surface (SH) and cross-sectional hardness (∆KHN). Data were submitted to two-way ANOVA, and Fisher's LSD test (p < 0.05). RESULTS: For ERO, both TMPnano-containing gels promoted enamel wear significantly lower than Placebo and 4500F, reaching levels similar to both positive controls (9000F and acid gel); significantly lower softening was observed for enamel treated with 4500F+5 % Micro and 4500F+2.5 % Nano. Also, the lowest ∆KHN values were observed for 4500F+2.5 % TMPnano among the TMP-containing gels. For ERO+ABR, the lowest enamel wear was achieved by the use of 4500F+5 % Nano among all gels, including both positive controls; lower softening was observed for Placebo and 9000F groups. CONCLUSION: The addition of 5 % nano-sized TMP to a low-fluoride gel produced superior protective effects for enamel under both challenges conditions, when compared with micrometric TMP, reaching values similar to or superior than both positive controls, respectively for ERO and ERO+ABR. CLINICAL SIGNIFICANCE: The supplementation of low-F gels with TMP was shown to significantly improve their effects on enamel erosive wear, and the use of nano-sized TMP further enhances this protective action.

Preventive dental erosion with silver diamine fluoride: An in vitro study.

OBJECTIVES: To evaluate the erosion preventive effect of 38 % silver diamine fluoride (SDF) solution in enamel and dentin of human permanent teeth. METHODS: Ninety enamel and ninety dentin blocks were prepared from permanent molars and allocated into three groups. Gp-SDF received a one-off application of 38 % SDF solution. Gp-SNF received a one-off application of a solution containing 800 ppm stannous chloride and 500 ppm fluoride. Gp-DW received a one-off application of deionized water. The blocks were submitted to acid challenge at pH 3.2, 2 min, 5 times/day for 7 days. All blocks were immersed in human saliva between cycles for one hour. The crystal characteristics, percentage of surface microhardness loss (%SMHL), surface loss, and elemental analysis and surface morphology were examined by X-ray diffraction (XRD), microhardness test, non-contact profilometry, and energy-dispersive X-ray spectroscopy (EDS) and scanning electron microscopy (SEM), respectively. Data of%SMHL and surface loss were analyzed by one-way ANOVA. RESULTS: XRD spectra revealed that fluorapatite and silver compounds formed in Gp-SDF, while fluorapatite and stannous compounds formed in Gp-SNF. Gp-DW presented only hydroxyapatite. The median (interquartile range) of%SMHL in Gp-SDF, Gp-SNF and Gp-DW were 27.86(3.66), 43.41(2.45), and 46.40(3.54) in enamel (p< 0.001), and 14.21(1.57), 27.99(1.95), and 33.18(1.73) in dentin, respectively (p < 0.001). The mean (standard deviation, µm) of surface loss of Gp-SDF, Gp-SNF, and Gp-DW were 2.81(0.59), 4.28(0.67), and 4.63(0.64) in enamel (p < 0.001) and 4.13(0.69), 6.04(0.61), and 7.72(0.66) in dentin, respectively (p < 0.001). SEM images exhibited less enamel corruption and more dentinal tubular occlusion in Gp-SDF compared to Gp-SNF and Gp-DW. EDS analysis showed silver was detected in Gp-SDF while stannous was detected in the dentin block of Gp-SNF. CONCLUSION: 38 % SDF yielded superior results in protecting enamel and dentin blocks from dental erosion compared to SNF and DW. CLINICAL SIGNIFICANCE: Topical application of 38 % SDF is effective in preventing dental erosion in human enamel and dentin.

Toothpaste containing TiF4 and chitosan against erosive tooth wear in situ.

OBJECTIVE: This study compared the protective effect of an experimental TiF4/Chitosan toothpaste with a commercial toothpaste on the prevention of erosive tooth wear (ETW) in situ. METHODS: Fifteen subjects took part in this crossover and double-blind study, in which they wore a palatal appliance containing 4 bovine enamel and 4 dentin in 3 phases (5 days each). Half of the samples were subjected to erosive challenges (90 s in 0.1 % citric acid, pH 2.5, 4 times/day), and the other half to erosive plus abrasive challenges (15 s plus 45 s of contact, 2 times/day). The phases corresponded to the application of the different toothpastes: 1) TiF4 (1400 ppm F-) plus Chitosan, 2) Elmex®, Erosion Protection (1400 ppm F-, Chitosan), and 3) Placebo (negative control). Tooth wear was measured using contact profilometry (µm) and submitted to two-way RM ANOVA/Tukey test (p < 0.05). RESULTS: No significant differences were detected between the experimental and commercial toothpastes, regardless of the challenge on both tissues. Both significantly reduce ETW compared to negative control (p < 0.0006). Tooth wear was increased by brushing only on eroded enamel (p < 0.01), but not on dentin (p = 0.6085). TiF4/Chitosan [erosion 2.98 ± 1.12 µm vs. erosion and abrasion 3.12 ± 1.33 µm] and Elmex® toothpastes [erosion 2.35 ± 0.93 µm vs. erosion and abrasion 2.98 ± 1.0 µm] minimized the impact of brushing compared to placebo on enamel [erosion 4.62 ± 1.48 µm vs. erosion and abrasion 5.15 ± 1.50 µm]. CONCLUSIONS: TiF4 plus chitosan toothpastes showed to be effective in minimizing the ETW as the commercial toothpaste is in situ. CLINICAL RELEVANCE: The experimental toothpaste has similar effect against ETW compared to the commercial toothpaste. Considering the increased ETW prevalence worldwide, this result supports clinical trials and a possible application of this experimental anti-erosive toothpaste in the future.

Ingenious Architecture and Coloration Generation in Enamel of Rodent Teeth.

Teeth exemplify architectures comprising an interplay of inorganic and organic constituents, resulting in sophisticated natural composites. Rodents (Rodentia) showcase extraordinary adaptations, with their continuously growing incisors surpassing human teeth in functional and structural optimizations. In this study, employing state-of-the-art direct atomic-scale imaging and nanoscale spectroscopies, we present compelling evidence that the release of material from ameloblasts and the subsequent formation of iron-rich enamel and surface layers in the constantly growing incisors of rodents are complex orchestrated processes, intricately regulated and independent of environmental factors. The synergistic fusion of three-dimensional tomography and imaging techniques of etched rodent́s enamel unveils a direct correlation between the presence of pockets infused with ferrihydrite-like material and the acid resistant properties exhibited by the iron-rich enamel, fortifying it as an efficient protective shield. Moreover, observations using optical microscopy shed light on the role of iron-rich enamel as a microstructural element that acts as a path for color transmission, although the native color remains indistinguishable from that of regular enamel, challenging the prevailing paradigms. The redefinition of "pigmented enamel" to encompass ferrihydrite-like infusion in rodent incisors reshapes our perception of incisor microstructure and color generation. The functional significance of acid-resistant iron-rich enamel and the understanding of the underlying coloration mechanism in rodent incisors have far-reaching implications for human health, development of potentially groundbreaking dental materials, and restorative dentistry. These findings enable the creation of an entirely different class of dental biomaterials with enhanced properties, inspired by the ingenious designs found in nature.

Comparison of the effects of fluoride varnish containing silver nanoparticles and conventional fluoride varnish on the surface microhardness of tooth enamel.

BACKGROUND: Nano-silver fluoride (NSF) has been introduced to improve enamel lesions. The effective use of varnishes is important in the prevention of dental caries. OBJECTIVES: The study aimed to compare the effect of conventional sodium fluoride varnish with the same varnish containing 1% and 2% silver nanoparticles (AgNP) on the surface microhardness of enamel. MATERIAL AND METHODS: The baseline surface microhardness of 40 premolar teeth was measured using a Vickers microhardness tester. After immersing the samples in a demineralizing agent for 24 h, the microhardness was measured again. In group B, a layer of conventional fluoride varnish was applied to the tooth surfaces using a microbrush with soft bristles, following the manufacturer's instructions. Groups C and D were treated with 1% and 2% NSF varnishes, respectively, while group A received no varnish. Surface microhardness tests were conducted on all specimens, including those previously tested. RESULTS: The microhardness of the enamel surface increased significantly in all 3 test groups compared to the microhardness after demineralization (p < 0.05). CONCLUSIONS: Conventional fluoride varnish and fluoride varnishes containing 1% and 2% AgNP are equally effective in remineralizing initial caries.

Two-body wear of novel monolithic lithium-silicate ceramic materials and their corresponding different antagonists.

OBJECTIVES: Evaluation of the two-body wear of lithium-silicate ceramics against different antagonists compared to a direct resin composite and human teeth. METHODS: Initial LiSi Block [LISI], IPS e.max CAD [EMA], and CEREC Tessera [TESE] were investigated and compared with direct resin composite [FILL] and human teeth [tooth]. As antagonists were used: steatite, ceramic, and human enamel. The control group tooth was only tested with enamel antagonist. The combinations underwent thermomechanical aging using a chewing simulator. Material losses were calculated using GOM-analysis software. Kolmogorov-Smirnov test, Kruskal-Wallis H, Mann-Whitney-U-test with Bonferroni correction and Spearman-rho correlation were calculated. A fractographic analysis was performed. RESULTS: Within TESE, enamel antagonists led to lower restoration losses than steatite and ceramic antagonists. Within FILL, enamel and steatite antagonists caused lower material losses compared to ceramic antagonists. Against steatite antagonists, LISI showed lowest material losses. Against ceramic antagonists, the use of LISI led to lower material losses compared to FILL. Against tooth antagonists, TESE showed lower material losses than tooth and FILL and LISI lower than FILL. Within LISI, steatite antagonists showed lower material losses on the antagonist than ceramic. Within EMA, steatite antagonists showed higher material losses than ceramic ones. Within ceramic antagonists, LISI restoration material showed lower material losses than FILL and EMA. CONCLUSIONS: Regardless of the antagonist material, the material losses of LISI and EMA were comparable. However, the abrasion resistance of LISI tended to be higher than EMA. CLINICAL SIGNIFICANCE: LISI is a fully crystallized lithium-silicate ceramic and no longer needs to be processed after milling. In addition, the abrasion resistance is very good, regardless of the antagonist material chosen.

Effect of strontium fluoride on mechanical and remineralization properties of enamel: An in-vitro study on a modified orthodontic adhesive.

OBJECTIVES: Evaluate the ability of strontium fluoride on bond strength and enamel integrity after incorporation within orthodontic adhesive system as a delivery vehicle. METHODS: Experimental orthodontic adhesive system Transbond™ XT were modified with 1% Sr2+, 0.5% SrF2, 1% strontium, 0.5% Sr2+, 1% F-, 0.5% F-, and no additions were control. Mixing of formulation was monitored using Fourier transform infrared spectroscopy. Small-molecule drug-discovery suite was used to gain insights into Sr2+, F-, and SrF2 binding. Shear bond testing was performed after 6-months of ageing. Enamel blocks were cut, and STEM pictures were recorded. Specimens were indented to evaluate elastic modulus. Raman microscope was used to collect Raman spectra and inspected using a scanning electron microscope. Crystal structural analysis was performed using X-ray diffraction. Effect of material on cellular proliferation was determined. Confocal was performed to evaluate the effect of formulation on biofilms. RESULTS: FTIR of modified adhesives depicted peak changes within range due to various functional groups existing within samples. TEM represented structurally optimized hexagonal unit-cell of hydroxyapatite. Mean shear bond strength is recorded highest for Transbond XT with 1% SrF2. Dead bacterial percentage appeared higher in 0.5% SrF2 and 1% F- specimens. Crystal lengths showed an increase in 0.5% and 1% SrF2 specimens. Phase contrast within TEM images showed a union of 0.5% SrF2 crystal with enamel crystal with higher elastic modulus and highly mineralized crystalline hydroxyapatite. Intensity of ν1 PO43- and ν1 CO32- along with carbonate - / ν1PO43- ratio displayed good association with strontium fluoride. The formulation showed acceptable cell biocompatibility (p < 0.353). All specimens displayed characteristic diffraction maxima of different apatite angles within XRD. SIGNIFICANCE: Experimental results suggested good biocompatibility, adequate mechanical strength, and far-ranging crystallization ability. This would provide a new strategy to overcome the two major challenges of fixed orthodontics, biofilm growth, and demineralization of enamel.

The use of mouthwash containing trimetaphosphate as an adjunct therapy to fluoridated toothpaste reduces enamel demineralization.

INTRODUCTION: The decline in dental caries has been attributed to the widespread use of fluoride (F). Two forms of presentation are fluoridated toothpaste (FT) and mouthwash (MW), widely used by the population. MATERIALS AND METHODS: This study aimed to evaluate in vitro the effects of combining FT and MW, whether supplemented with sodium trimetaphosphate (TMP) or not, on dental enamel demineralization. Bovine enamel blocks (n = 60) were selected based on initial surface hardness (SHi) and divided into 5 experimental groups (n = 12 each): I) Placebo Toothpaste (without F/TMP); II) 1100 ppm F Toothpaste (FT); III) 1100F associated with a MW at 100 ppm F (FT + MW 100F); IV) 1100F associated with a MW at 225 ppm F (FT + MW 250F); and V) 1100F associated with a MW at 100 ppm F supplemented with 0.4 % TMP (FT + MW 100F-TMP). The blocks were treated twice a day, undergoing 5 pH cycles over 7 days. Thus, the percentage change in surface hardness (%SH), integrated subsurface hardness loss (ΔKHN), and the concentration of F, phosphorus (P), and calcium (Ca) in the enamel were determined. The data were submitted to ANOVA and Student-Newman-Keuls test (p < 0.001). RESULTS: The 1100F group was statistically inferior to the groups associated with MW for %SH, ΔKHN, and the concentration of P and Ca in the enamel (p < 0.001). Blocks treated with FT + MW 225F and FT + MW 100F-TMP showed significantly lower %SH compared to the other groups (p < 0.001). The FT + MW 100F - TMP group exhibited the lowest depth mineral loss (ΔKHN), and higher concentration de P in enamel (p < 0.001). CONCLUSION: The adjunct use of MW with FT produces a greater protective effect in inhibiting enamel demineralization, and the supplementation of TMP to the MW with 100F provides a superior effect compared to MW with 225F. CLINICAL SIGNIFICANCE: This combination of treatments could be regarded as one of several alternative fluoride supplements for subjects at elevated risk of caries.

Remineralizing effect of the association of nano-hydroxyapatite and fluoride in the treatment of initial lesions of the enamel: A systematic review.

OBJECTIVE: Assessed the effect of dental products containing nano-hydroxyapatite (nano-HA) + fluoride on the remineralization of white spot lesions (WSL) in vivo or in situ. METHODS: Seven databases were explored using a two-pronged approach (intervention/treatment). After screening, full-text assessment, and further exclusion, the qualitative synthesis of five studies (four clinical and one in situ) was performed. Based on the Cochrane collaboration guidelines relevant data of the studies were collected and summarized. The Cochrane risk of bias tool for randomized trials (RoB 2.0) was used to appraise the studies' methodological quality and the GRADE guidelines to assess their level of evidence. The RoB 2.0 domains were rated on their risk of bias (RoB) as low, high, or with some concerns, and an adaptation of the tool was used to the in situ study. RESULTS: The included studies assessed 151 WSL in anterior permanent teeth, on patients with varying ages. The protocol application, treatment length (7d-12 w), and control groups varied greatly between the studies making the performance of a quantitative analysis unfeasible. The general RoB of the clinical studies was classified as being of low risk (n = 2) or some concerns (n = 2). The in situ study was considered as being of low risk. The level of the evidence was moderate. Most of the studies found moderate evidence regarding the superiority of this association in clinical settings. CONCLUSION: Even with the nano-HA + fluoride promising results for the remineralization treatment of WSL, due to the restricted number of studies and types of products, its extended use cannot be recommended based on the current systematic review, especially when considering the moderate level of the evidence found. CLINICAL SIGNIFICANCE: Due to the biocompatibility and higher surface coverage of nano-HA and the remineralization capacity of fluoride formulations, the association of these elements to remineralize WSL has been positively reported. After the collection and qualitative appraise of the data, the clinical evidence of the use of these dental products is promising but limited.

Fluoride-amorphous calcium phosphate and biomimetic nano-hydroxyapatite for enamel remineralization: An in-vitro study of surface microhardness and composition.

AIM: Fluoride-Amorphous Calcium Phosphate and Biomimetic Nano-Hydroxyapatite for Enamel Remineralization; An In-Vitro Study of Surface Microhardness and Composition. MATERIAL AND METHODS: Ninety-six extracted human premolars with sound buccal surface were divided using a randomization computer-generating software into four groups; Group I (control) sound untreated enamel, Group II (demineralized) demineralized to create white spot lesions, Group III (biom-n-HA) demineralized and then treated with biomimetic nanohydroxyapatite cream, and Group IV (F-ACP) demineralized and then treated using Fluoride-Amorphous Calcium Phosphate varnish. Each group was divided into two subgroups; subgroup "A" evaluated for mineral content using energy dispersive x-ray spectroscopy (EDX) and for surface microhardness using the Vickers microhardness test and Subgroup "B" evaluated for white spot lesion depth using a polarized light microscope (PLM). RESULTS: The highest microhardness (VHN) was found in the (F-ACP) group (mean=428.61±54.43) and then in the (Biom-n-HA) group (mean=408.11±70.16) followed by the (Control) group (mean=402.13±53.40) with no significant difference between them and finally in the significantly different (Demineralized) group (mean=256.99±45.83). The weight percentage of Ca (30.29±1.04 and 33.44±1.07) and Ca/P ratio (1.87±0.06 and 2.03±0.05) were significantly different between Group III and Group IV respectively. PLM measurements in Group II (198.83µm), Group III (60.17µm), and Group IV (26.33µm) were significantly different. CONCLUSIONS: Both the (Biom-n-HA) cream and the (F-ACP) varnish showed promising results for enamel remineralization. The increased enamel surface microhardness was consistent with the mineral content and the changes in the birefringence.

Co-exposure to fluoride and sulfur dioxide induces abnormal enamel mineralization in rats via the FGF9-mediated MAPK signaling pathway.

Fluoride (F) and sulfur dioxide (SO2) contamination is recognized as a public health concern worldwide. Our previous research has shown that Co-exposure to F and SO2 can cause abnormal enamel mineralization. Ameloblastin (AMBN) plays a crucial role in the process of enamel mineralization. However, the process by which simultaneous exposure to F and SO2 influences enamel formation by regulating AMBN expression still needs to be understood. This study aimed to establish in vivo and in vitro models of F-SO2 Co-exposure and investigate the relationship between AMBN and abnormal enamel mineralization. By overexpressing/knocking out the Fibroblast Growth Factor 9 (FGF9) gene, we investigated the impact of FGF9-mediated Mitogen-Activated Protein Kinase (MAPK) signaling on AMBN synthesis to elucidate the mechanism underlying the induction of abnormal enamel mineralization by F-SO2 Co-exposure in rats. The results showed that F-SO2 exposure damaged the structure of rat enamel and ameloblasts. When exposed to F or SO2, gradual increases in the protein expression of FGF9 and phosphorylated p38 mitogen-activated protein kinase (p-P38) were observed. Conversely, the protein levels of AMBN, phosphorylated extracellular signal-regulated kinase (p-ERK), and phosphorylated c-Jun N-terminal kinase (p-JNK) were decreased. AMBN expression was significantly correlated with FGF9, p-ERK, and p-JNK expression in ameloblasts. Interestingly, FGF9 overexpression reduced the levels of p-ERK and p-JNK, worsening the inhibitory effect of F-SO2 on AMBN. Conversely, FGF9 knockout increased the phosphorylation of ERK and JNK, partially reversing the F-SO2-induced downregulation of AMBN. Taken together, these findings strongly demonstrate that FGF9 plays a critical role in F-SO2-induced abnormal enamel mineralization by regulating AMBN synthesis through the JNK and ERK pathways.

Odontología restauradora mínimamente invasiva: caso clínico / Minimally invasive restorative dentistry: a clinical case

La decoloración de las piezas dentarias puede te-ner un impacto estético y social que lleva a los pa-cientes a buscar una intervención para mejorar su sonrisa. Las manchas superficiales y las irregula-ridades del esmalte pueden deberse a hipoplasias, hipomineralización molar, fluorosis, uso de medica-mentos, manchas blancas causadas por traumatis-mos o infección en la dentición primaria, o manchas post ortodóncicas. El diagnóstico de los defectos del esmalte se realiza a través de un examen visual por transiluminación. Se han propuesto técnicas micro abrasivas con diferentes agentes para eliminar las manchas superficiales del esmalte, así también como el uso de agentes blanqueadores a baja concentra-ción para equilibrar el color de las piezas dentarias. Si las manchas son profundas se requiere de una mega abrasión y posterior restitución anatómica con resinas compuestas. Los avances tecnológicos en los materiales de restauración adhesivos permi-ten imitar las piezas dentarias naturales permitien-do la mínima destrucción de la estructura dental sin comprometer futuras opciones de restauración. El objetivo de este trabajo es mostrar una secuencia de procedimientos mínimamente invasivos para devol-ver la estética perdida en una paciente que concurre a la Cátedra de Odontología Restauradora (AU)

The discoloration of dental pieces can have an aesthetic and social impact that leads patients to seek an intervention to improve their smile. Superficial stains and enamel irregularities may be due to hypoplasia, molar hypomineralization, fluorosis, drug use, white spots caused by trauma or infection in the primary dentition, or post-orthodontic stains. The diagnosis of enamel defects is made through a visual examination by transillumination. Microabrasive techniques with different agents have been proposed to remove surface stains from the enamel, as well as the use of low-concentration whitening agents to balance the color of the teeth. If the stains are deep, a mega abrasion and subsequent anatomical restoration with composite resins are required. Technological advances in adhesive restorative materials make it possible to mimic natural teeth, allowing minimal destruction of tooth structure without compromising future restorative options. The objective of this work is to show the sequence of minimally invasive procedures to return the lost aesthetics in a patient who attends the Chair of Restorative Dentistry (AU)