Improvements in Wear and Corrosion Resistance of Ti-W-Alloyed Gray Cast Iron by Tailoring Its Microstructural Properties.
Materials (Basel)
; 17(10)2024 May 20.
Article
in En
| MEDLINE
| ID: mdl-38793534
ABSTRACT
The improved wear and corrosion resistance of gray cast iron (GCI) with enhanced mechanical properties is a proven stepping stone towards the longevity of its versatile industrial applications. In this article, we have tailored the microstructural properties of GCI by alloying it with titanium (Ti) and tungsten (W) additives, which resulted in improved mechanical, wear, and corrosion resistance. The results also show the nucleation of the B-, D-, and E-type graphite flakes with the A-type graphite flake in the alloyed GCI microstructure. Additionally, the alloyed microstructure demonstrated that the ratio of the pearlite volume percentage to the ferrite volume percentage was improved from 67/33 to 87/13, whereas a reduction in the maximum graphite length and average grain size from 356 ± 31 µm to 297 ± 16 µm and 378 ± 18 µm to 349 ± 19 µm was detected. Consequently, it improved the mechanical properties and wear and corrosion resistance of alloyed GCI. A significant improvement in Brinell hardness, yield strength, and tensile strength of the modified microstructure from 213 ± 7 BHN to 272 ± 8 BHN, 260 ± 3 MPa to 310 ± 2 MPa, and 346 ± 12 MPa to 375 ± 7 MPa was achieved, respectively. The substantial reduction in the wear rate of alloyed GCI from 8.49 × 10-3 mm3/N.m to 1.59 × 10-3 mm3/N.m resulted in the upgradation of the surface roughness quality from 297.625 nm to 192.553 nm. Due to the increase in the corrosion potential from -0.5832 V to -0.4813 V, the impedance of the alloyed GCI was increased from 1545 Ohm·cm2 to 2290 Ohm·cm2. On the basis of the achieved experimental results, it is suggested that the reliability of alloyed GCI based on experimentally validated microstructural compositions can be ensured during the operation of plants and components in a severe wear and corrosive environment. It can be predicted that the proposed alloyed GCI components are capable of preventing the premature failure of high-tech components susceptible to a wear and corrosion environment.
Full text:
1
Collection:
01-internacional
Database:
MEDLINE
Language:
En
Journal:
Materials (Basel)
Year:
2024
Document type:
Article