Nanostructured Ir-supported on Ti4O7 as a cost-effective anode for proton exchange membrane (PEM) electrolyzers.
Phys Chem Chem Phys
; 18(6): 4487-95, 2016 Feb 14.
Article
em En
| MEDLINE
| ID: mdl-26791108
ABSTRACT
PEM water electrolysis has recently emerged as one of the most promising technologies for large H2 production from a temporal surplus of renewable electricity; yet it is expensive, partly due to the use of large amounts of Ir present in the anode. Here we report the development and characterization of a cost-effective catalyst, which consists of metallic Ir nanoparticles supported on commercial Ti4O7. The catalyst is synthesized by reducing IrCl3 with NaBH4 in a suspension containing Ti4O7, cetyltrimethylammonium bromide (CTAB) and anhydrous ethanol. No thermal treatment was applied afterwards in order to preserve the high conductivity of Ti4O7 and the metallic properties of Ir. Electron microscopy images show an uniform distribution of mostly single Ir particles covering the electro-ceramic support, although some agglomerates are still present. X-ray diffraction (XRD) analysis reveals a cubic face centered structure of Ir nanoparticles with a crystallite size of ca. 1.8 nm. According to X-ray photoelectron spectroscopy (XPS), the ratio of metallic Ir and Ir-oxide, identified as Ir(3+), is 3 1 after the removal of surface contamination. Other surface properties such as primary particle size distribution and surface potential were determined by atomic force microscopy (AFM). Cyclic and linear voltammetric measurements were conducted to study the electrochemical surface and kinetics of Ir-black and Ir/Ti4O7. The developed catalyst outperforms the commercial Ir-black in terms of mass activity for the oxygen evolution reaction (OER) in acid medium by a factor of four, measured at 0.25 V overpotential and room temperature. In general, the Ir/Ti4O7 catalyst exhibits improved kinetics and higher turnover frequency (TOF) compared to Ir-black. The developed Ir/Ti4O7 catalyst allows reducing the precious metal loading in the anode of a PEM electrolyzer by taking advantage of the use of an electro-ceramic support.
Texto completo:
1
Coleções:
01-internacional
Contexto em Saúde:
1_ASSA2030
Base de dados:
MEDLINE
Tipo de estudo:
Health_economic_evaluation
/
Prognostic_studies
Idioma:
En
Revista:
Phys Chem Chem Phys
Ano de publicação:
2016
Tipo de documento:
Article