Self-assembled biobased chitosan hybrid carrying N/P/B elements for polylactide with enhanced fire safety and mechanical properties.
Int J Biol Macromol
; 236: 123947, 2023 May 01.
Article
em En
| MEDLINE
| ID: mdl-36898460
ABSTRACT
The inherent shortcomings such as flammability, brittleness, and low crystallinity limit the broad applications of poly(lactic acid) (PLA). To improve the fire resistance and mechanical properties of PLA, a chitosan-based core-shell flame retardant additive (APBA@PA@CS) was prepared for PLA via the self-assembly of interionic interactions among chitosan (CS), phytic acid (PA), and 3-aminophenyl boronic acid (APBA). The peak heat release rate (pHRR) and total heat release rate (THR) of PLA composite containing 3 wt% APBA@PA@CS decreased from 460.1 kW/m2 and 75.8 MJ/m2 to 419.0 kW/m2 and 53.1 MJ/m2, respectively. The presence of APBA@PA@CS contributed to the formation of a high-quality char layer rich in phosphorus and boron in the condensed phase and released non-flammable gases in the gas phase to hinder the exchange of heat and O2, thereby having a synergistic flame retardant effect. Meanwhile, the tensile strength, elongation at break, impact strength, and crystallinity of PLA/APBA@PA@CS were increased by 3.7 %, 17.4 %, 5.3 %, and 55.2 %, respectively. This study provides a feasible route to construct a chitosan-based N/B/P tri-element hybrid to improve the fire safety performance and mechanical properties of PLA biocomposites.
Palavras-chave
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Assunto principal:
Quitosana
/
Retardadores de Chama
Idioma:
En
Revista:
Int J Biol Macromol
Ano de publicação:
2023
Tipo de documento:
Article