Design of cationic surfactant reinforced carrageenan waterproof composite films and applied as water induced electricity generator.
Int J Biol Macromol
; 253(Pt 2): 126713, 2023 Dec 31.
Article
em En
| MEDLINE
| ID: mdl-37673149
ABSTRACT
Carrageenan (CR) is a renewable polysaccharide material for packaging application due to its good film-forming property, but its use can be limited by the water solubility. In this research, CR hydrogels were modified by quaternary ammonium surfactants with different length of hydrocarbon tails (n, 8â¦nâ¦16) by adsorption method and waterproof films were obtained after drying. The composition and charge interaction of composite films was confirmed by FTIR. Both thermogravimetric analysis and energy dispersive spectrometer indicated that the surfactant ions replaced K+ to form complexes with CR. The X-ray diffraction revealed the decreased amorphous nature of composite films compared to neat CR film. Water-related physical properties, such as water content, weight percentage change after contact with water, water vapor transmission, and water contact angle were intimately related to n. When 8â¦nâ¦14, the waterproof properties were enhanced with the increase of n. Meanwhile, the waterproof property of composite film was ascertained by the no leakage result in the boiling water packaging experiment. When n = 16, sandwich structure was found in the sectional micromorphology images, and water bag structure formed after immersed into water. By comparing the mechanical properties of the composite films in different condition, we found that quaternary ammonium surfactants improved significantly the tensile strength in water and increased elongation at break in dry state. The composite films can be used as water induced voltage generator for their polyelectrolyte nature. Benefiting from the high stability of the composite films in water, their water-induced voltage generation process had good recyclability. Due to the antimicrobial activity of the quaternary ammonium salts and the waterproof property, composite films were more stable and degraded more slowly than neat CR film in nature environment.
Palavras-chave
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Assunto principal:
Tensoativos
/
Compostos de Amônio
Idioma:
En
Revista:
Int J Biol Macromol
Ano de publicação:
2023
Tipo de documento:
Article