Boosting the Electrochemical Performance of Primary and Secondary Lithium Batteries with Mn-Doped All-Fluoride Cathodes.

ABSTRACT

Transition metal fluorides are potentially high specific energy cathode materials of next-generation lithium batteries, and strategies to address their low conductivity typically involve a large amount of carbon coating, which reduces the specific energy of the electrode. In this study, MnyFe1-yF3@CFx was generated by the all-fluoride strategy, converting most of the carbon in MnyFe1-yF3@C into electrochemical active CFx through a controllable NF3 gas phase fluorination method, while still retaining a tightly bound graphite layer to provide initial conductivity, which greatly improved the energy density of the composite. This synergistic effect of nonfluorinated residual carbon (∼11%) and Mn doping ensures the electrochemical kinetics of the composite. The loading mass of the active substance had been increased to 86%. The theoretical and actual discharge capacity of MnyFe1-yF3@CFx composite was up to 765 mAh g-1 (pure FeF3 is 712 mAh g-1) and 728 mAh g-1, respectively. The discharge capacity at the high-voltage (3.0 V) platform was more than three times higher than that of the non-Mn-doped composite (FeF3@CFx).