Resumo
This work aimed to evaluate the physical and mechanical properties based panels made of barley industrial waste and particles Pinus spp. The company Bonet Woods and Papers Ltda. in the municipality of Santa Cecilia - Santa Catarina, provided the particles Pinus spp. The barley residue was provided by AMBEV in Lages, SC. For the production of panels used were five treatments, being composed of different barley residue content and particle Pinus spp.: 100:0 (T1), 75:25 (T2), 50:50 (T3), 25:75 (T4) and 0:100 (T5), to the residue and timber respectively. Three panels were produced per treatment, totaling 15 panels. The nominal density of 650 Kg.m-3, 12% of urea formaldehyde resin, 1% paraffin, eight minutes press cycle were used in the production of panels, with a temperature of 160 °C and a maximum pressure of 40 Kgf.cm-2. For the physical properties, moisture content, density, compression ratio, thickness swelling and water absorption (2h and 24h) were determined. The mechanical properties determined were static bending, internal connection, top and surface screw pulling. With the results found it can be concluded that increasing the percentage of barley residue decreases the resistance of the panels to the physical and mechanical properties.(AU)
Neste trabalho objetivou-se avaliar as propriedades físicas e mecânicas de painéis aglomerados constituídos por resíduos de cevada industrial e partículas de Pinus spp. As partículas de Pinus spp. foram fornecidas pela empresa Bonet Madeiras e Papéis Ltda. localizada em Santa Cecília, Santa Catarina. O resíduo de cevada foi fornecido pela AMBEV, Lages, SC. Para a produção dos painéis foram utilizados cinco tratamentos, sendo compostos por diferentes teores de resíduo de cevada e de partículas de Pinus spp., respectivamente: 100:0 (T1), 75:25 (T2), 50:50 (T3), 25:75 (T4) e 0:100 (T5). Foram produzidos três painéis por tratamento, totalizando 15 painéis. Na produção dos painéis, utilizou-se a densidade nominal de 650 Kg.m-3, 12% de resina ureia formaldeído, 1% de parafina e ciclo de prensagem de oito minutos, com 160 ºC de temperatura e pressão máxima de 40 Kgf.cm-2. Para as propriedades físicas determinou-se o teor de umidade, densidade, razão de compactação, inchamento em espessura e absorção de água (2h e 24h). As propriedades mecânicas determinadas foram resistência a flexão estática, ligação interna, arrancamento de parafuso de topo e superfície. Com os resultados encontrados pode-se concluir que o aumento da porcentagem de resíduo de cevada diminui a resistência dos painéis para as propriedades físicas e mecânicas.(AU)
Assuntos
Resíduos Industriais/análise , Hordeum/química , Hordeum/classificaçãoResumo
This work aimed to evaluate the physical and mechanical properties based panels made of barley industrial waste and particles Pinus spp. The company Bonet Woods and Papers Ltda. in the municipality of Santa Cecilia - Santa Catarina, provided the particles Pinus spp. The barley residue was provided by AMBEV in Lages, SC. For the production of panels used were five treatments, being composed of different barley residue content and particle Pinus spp.: 100:0 (T1), 75:25 (T2), 50:50 (T3), 25:75 (T4) and 0:100 (T5), to the residue and timber respectively. Three panels were produced per treatment, totaling 15 panels. The nominal density of 650 Kg.m-3, 12% of urea formaldehyde resin, 1% paraffin, eight minutes press cycle were used in the production of panels, with a temperature of 160 °C and a maximum pressure of 40 Kgf.cm-2. For the physical properties, moisture content, density, compression ratio, thickness swelling and water absorption (2h and 24h) were determined. The mechanical properties determined were static bending, internal connection, top and surface screw pulling. With the results found it can be concluded that increasing the percentage of barley residue decreases the resistance of the panels to the physical and mechanical properties.
Neste trabalho objetivou-se avaliar as propriedades físicas e mecânicas de painéis aglomerados constituídos por resíduos de cevada industrial e partículas de Pinus spp. As partículas de Pinus spp. foram fornecidas pela empresa Bonet Madeiras e Papéis Ltda. localizada em Santa Cecília, Santa Catarina. O resíduo de cevada foi fornecido pela AMBEV, Lages, SC. Para a produção dos painéis foram utilizados cinco tratamentos, sendo compostos por diferentes teores de resíduo de cevada e de partículas de Pinus spp., respectivamente: 100:0 (T1), 75:25 (T2), 50:50 (T3), 25:75 (T4) e 0:100 (T5). Foram produzidos três painéis por tratamento, totalizando 15 painéis. Na produção dos painéis, utilizou-se a densidade nominal de 650 Kg.m-3, 12% de resina ureia formaldeído, 1% de parafina e ciclo de prensagem de oito minutos, com 160 ºC de temperatura e pressão máxima de 40 Kgf.cm-2. Para as propriedades físicas determinou-se o teor de umidade, densidade, razão de compactação, inchamento em espessura e absorção de água (2h e 24h). As propriedades mecânicas determinadas foram resistência a flexão estática, ligação interna, arrancamento de parafuso de topo e superfície. Com os resultados encontrados pode-se concluir que o aumento da porcentagem de resíduo de cevada diminui a resistência dos painéis para as propriedades físicas e mecânicas.