Rev. Ciênc. Agrovet. (Online) ; 14(3): 217-223, 2015. tab
Artigo em Português | VETINDEX | ID: biblio-1488093

Resumo

The study aimed to determine the technological properties of cement-wood panels produced with the particle Eucalyptus benthamii Maiden et Cambage. The experiment plan consisted of four compositions with different treatments of the particles (cold water, hot water, sodium hidroxyde (NaOH) and calcium hidroxyde (Ca(OH)2), and a control composition. The panels were produced with nominal specific gravity of 1.20 g cm-³, with the ratios wood:concrete 1:2.75 and water:cement 0.40. The panels were evaluated for their physical and mechanical properties through the European standard EN. Analyses were performed to verify the occurrence of outliers, data normality and homogeneity of variances, and subsequently submitted to analysis of variance and Tukey test. The results of physical and mechanical properties of the panels indicated that the best method of treating particles is through the use of Ca(OH)2. With the exception of the modulus of rupture, the thickness swelling, modulus of elasticity and tensile perpendicular, they met the specifications of commercial panels produced by the BISON process. Therefore, the feasibility of use of Eucalyptus benthamii for wood-cement panels production was discovered.


O estudo teve como objetivo determinar as propriedades tecnológicas de painéis cimento-madeira produzidos com partículas de Eucalyptus benthamii Maiden et Cambage. O plano experimental foi formado por quatro composições com diferentes tratamentos das partículas (água fria, água quente, hidróxido de sódio (NaOH) e hidróxido de cálcio (Ca(OH)2), e uma composição testemunha. Os painéis foram produzidos com massa específica nominal de 1,20 g/cm³, com relação madeira:cimento de 1:2,75 e água:cimento de 0,40. Os painéis foram avaliados quanto as suas propriedades físicas e mecânicas por meio da norma europeia EN. Foram realizadas análises para verificar a ocorrência de outliers, normalidade dos dados e homogeneidade das variâncias, sendo posteriormente submetidas à análise da variância e teste de Tukey. Os resultados das propriedades físicas e mecânicas dos painéis indicaram que o melhor método de tratamento de partículas foi com o uso de Ca(OH)2. Com exceção do módulo de ruptura, o inchamento em espessura, módulo de elasticidade e tração perpendicular, atenderam às especificações de painéis comerciais produzidos pelo processo BISON. Dessa forma, verificou-se a viabilidade de uso da madeira de Eucalyptus benthamii para produção de painéis cimento-madeira.


Assuntos
Biotecnologia , Eucalyptus , Materiais de Construção
2.
R. Ci. agrovet. ; 14(3): 217-223, 2015. tab
Artigo em Português | VETINDEX | ID: vti-27888

Resumo

The study aimed to determine the technological properties of cement-wood panels produced with the particle Eucalyptus benthamii Maiden et Cambage. The experiment plan consisted of four compositions with different treatments of the particles (cold water, hot water, sodium hidroxyde (NaOH) and calcium hidroxyde (Ca(OH)2), and a control composition. The panels were produced with nominal specific gravity of 1.20 g cm-³, with the ratios wood:concrete 1:2.75 and water:cement 0.40. The panels were evaluated for their physical and mechanical properties through the European standard EN. Analyses were performed to verify the occurrence of outliers, data normality and homogeneity of variances, and subsequently submitted to analysis of variance and Tukey test. The results of physical and mechanical properties of the panels indicated that the best method of treating particles is through the use of Ca(OH)2. With the exception of the modulus of rupture, the thickness swelling, modulus of elasticity and tensile perpendicular, they met the specifications of commercial panels produced by the BISON process. Therefore, the feasibility of use of Eucalyptus benthamii for wood-cement panels production was discovered.(AU)


O estudo teve como objetivo determinar as propriedades tecnológicas de painéis cimento-madeira produzidos com partículas de Eucalyptus benthamii Maiden et Cambage. O plano experimental foi formado por quatro composições com diferentes tratamentos das partículas (água fria, água quente, hidróxido de sódio (NaOH) e hidróxido de cálcio (Ca(OH)2), e uma composição testemunha. Os painéis foram produzidos com massa específica nominal de 1,20 g/cm³, com relação madeira:cimento de 1:2,75 e água:cimento de 0,40. Os painéis foram avaliados quanto as suas propriedades físicas e mecânicas por meio da norma europeia EN. Foram realizadas análises para verificar a ocorrência de outliers, normalidade dos dados e homogeneidade das variâncias, sendo posteriormente submetidas à análise da variância e teste de Tukey. Os resultados das propriedades físicas e mecânicas dos painéis indicaram que o melhor método de tratamento de partículas foi com o uso de Ca(OH)2. Com exceção do módulo de ruptura, o inchamento em espessura, módulo de elasticidade e tração perpendicular, atenderam às especificações de painéis comerciais produzidos pelo processo BISON. Dessa forma, verificou-se a viabilidade de uso da madeira de Eucalyptus benthamii para produção de painéis cimento-madeira.(AU)