Resumo
Wood-cement composite (WCC) is a potential construction material for tropical regions, due to its physico-mechanical properties and resistance to decay and fungi attack. However it is important to test alternative production methods and wood materials that are easier and cheaper than those traditionally used, in order to create a higher demand for this product. The aim of this work was to evaluate the use of wood from four Amazonian species (Eschweilera coriaceae, Swartzia recurva, Manilkara amazonica and Pouteria guianensis) in the production of wood-cement composites through a vibro-dynamic compression process, an alternative method to the use of a hydraulic press. The inhibition degree caused by the wood to the cement cure, measured by the factor CA, indicated that all species were compatible with Portland cement (CP II-Z). WCC with densities higher than 1,100 kg m-3 (produced with E. coriaceae and S. recurva particles) showed compressive strength values higher than 10 MPa, which fulfills the minimum requirement for lightweitgh reinforced concrete blocks for structural use.(AU)
Compósito madeira-cimento é um potencial material de construção para regiões tropicais, devido a suas propriedades físico-mecânicas e resistência ao ataque de fungos e podridão. Contudo, é importante testar métodos alternativos de produção e madeiras que sejam mais simples e baratos do que os tradicionalmente usados, para que se alcance uma maior demanda para esse produto. O objetivo deste estudo foi avaliar o uso de madeira de quatro espécies amazônicas (Eschweilera coriaceae, Swartzia recurva, Manilkara amazonica e Pouteria guianensis) na produção de compósitos de madeira-cimento (WCC) pelo processo de compactação vibro-dinâmica, um método alternativo que dispensa o uso de prensas hidráulicas. O grau de inibição à pega do cimento causado pela presença da madeira foi medido pelo fator CA e indicou que todas as quatro espécies foram compatíveis com o cimento Portland (CP II-Z). Compósitos com massa específica superior a 1.100 kg m-3 (produzidas com partículas de E. coriaceae e S. recurva) apresentaram valores de compressão axial acima de 10 MPa, requisito mínimo para classificar como blocos de concreto reforçados leves de uso estrutural.(AU)
Resumo
Wood-cement composite (WCC) is a potential construction material for tropical regions, due to its physico-mechanical properties and resistance to decay and fungi attack. However it is important to test alternative production methods and wood materials that are easier and cheaper than those traditionally used, in order to create a higher demand for this product. The aim of this work was to evaluate the use of wood from four Amazonian species (Eschweilera coriaceae, Swartzia recurva, Manilkara amazonica and Pouteria guianensis) in the production of wood-cement composites through a vibro-dynamic compression process, an alternative method to the use of a hydraulic press. The inhibition degree caused by the wood to the cement cure, measured by the factor CA, indicated that all species were compatible with Portland cement (CP II-Z). WCC with densities higher than 1,100 kg m-3 (produced with E. coriaceae and S. recurva particles) showed compressive strength values higher than 10 MPa, which fulfills the minimum requirement for lightweitgh reinforced concrete blocks for structural use. (AU)
Compósito madeira-cimento é um potencial material de construção para regiões tropicais, devido a suas propriedades físico-mecânicas e resistência ao ataque de fungos e podridão. Contudo, é importante testar métodos alternativos de produção e madeiras que sejam mais simples e baratos do que os tradicionalmente usados, para que se alcance uma maior demanda para esse produto. O objetivo deste estudo foi avaliar o uso de madeira de quatro espécies amazônicas (Eschweilera coriaceae, Swartzia recurva, Manilkara amazonica e Pouteria guianensis) na produção de compósitos de madeira-cimento (WCC) pelo processo de compactação vibro-dinâmica, um método alternativo que dispensa o uso de prensas hidráulicas. O grau de inibição à pega do cimento causado pela presença da madeira foi medido pelo fator CA e indicou que todas as quatro espécies foram compatíveis com o cimento Portland (CP II-Z). Compósitos com massa específica superior a 1.100 kg m-3 (produzidas com partículas de E. coriaceae e S. recurva) apresentaram valores de compressão axial acima de 10 MPa, requisito mínimo para classificar como blocos de concreto reforçados leves de uso estrutural.(AU)