Resistance of acetylated Jacaranda copaia wood to termites and decaying fungi attack / Resistência da madeira acetilada de Jacaranda copaia ao ataque de cupins e fungos apodrecedores

The natural durability of the wood is essential for the definition of its use, and this property can be enhanced with the proper chemical treatment of the wood. Thus, the objective of this study was to evaluate the resistance to termites and decay fungi of Jacaranda copaia wood chemically modified through acetylation. Five experimental treatments were assessed: acetylation for 2, 4, 6 and 8 hours and a control (non-acetylated). The acetylation was carried out by immersing wood samples in acetic anhydride at 90 °C. Acetylated and control samples were subjected to the action of xylophagous termites (Nasutitermes sp.) and decaying fungi (Gloeophyllum trabeum and Trametes versicolor). The acetylation process significantly increased the resistance of Jacaranda copaia wood to the attack of the xylophagous organisms. There was no mass loss after exposure to termites of the wood in any of the acetylation treatments, while in the control wood, mass loss was 9.5%. Regarding the decaying fungi, mass loss occurred in all treatments. Acetylation for 6 and 8 hours were the most efficient chemical treatments, increasing the resistance class of the Jacaranda copaia wood to highly resistant.(AU)

A durabilidade natural da madeira é essencial para a definição de seu uso, e essa propriedade pode ser potencializada com o tratamento químico adequado da madeira. Assim, o objetivo deste trabalho foi avaliar a resistência da madeira de Jacaranda copaia modificada quimicamente por acetilação a cupins e fungos apodrecedores. Cinco tratamentos experimentais foram avaliados: acetilação por 2, 4, 6 e 8 horas e um controle (não acetilado). A acetilação foi realizada por imersão das amostras de madeira em anidrido acético a 90°C. Amostras acetiladas e controle foram submetidas à ação de cupins xilófagos (Nasutitermes sp.) e fungos apodrecedores (Gloeophyllum trabeum e Trametes versicolor). O processo de acetilação aumentou significativamente a resistência da madeira de Jacaranda copaia ao ataque dos organismos xilófagos. Não houve perda de massa após exposição aos cupins da madeira em nenhum dos tratamentos de acetilação, enquanto na madeira controle a perda de massa foi de 9,5%. Em relação aos fungos em decomposição, ocorreu perda de massa em todos os tratamentos. Os tratamentos químicos mais eficientes foram os de acetilação por 6 e 8 horas, elevando a classe de resistência da madeira de Jacaranda copaia para altamente resistente.(AU)

Dureza Rockwell da madeira de três espécies amazônicas submetidas a ensaios de apodrecimento acelerado

This study aimed to evaluate the use of Rockwell hardness in the characterization of the biodeterioration of Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru) woods, which were submitted to decay fungi Trametes versicolor (white rot) and Gloeophyllum trabeum (brown rot). For this purpose, specimens of each Amazon species were submitted to decay fungi, according to ASTM D2017 (2005). The characterization of the Rockwell hardness was performed weekly until the fourth week, and then every two weeks until the twentieth week. Additionally, it was determined the mass loss, according to criteria established by ASTM D2017 (2005). The results indicated that the Rockwell hardness can be used as a primary tool in the characterization of the biodeterioration of wood, being sensitive in predicting the early stages. Among the Amazon woods, cumaru wood showed a greater natural resistance to decay fungi. With respect to decay fungi, brown rot more intensely attacked the three Amazon woods.

Objetivou-se avaliar o emprego de ensaios de dureza Rockwell na caracterização da biodeterioração das madeiras de Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru), submetidas ao ataque dos fungos apodrecedores Trametes versicolor (podridão branca) e Gloeophyllum trabeum (podridão parda). Para tanto, corpos de prova de cada espécie amazônica foram submetidos a ensaios de apodrecimento acelerado, de acordo com a ASTM D2017 (2005), durante 20 semanas. A caracterização da dureza Rockwell foi realizada semanalmente até a 4ª semana e, posteriormente, a cada duas semanas, até a 20ª semana. Adicionalmente, foram determinadas as perdas de massa, conforme critérios estabelecidos pela ASTM D2017 (2005). Quanto aos resultados, destaca-se que a dureza Rockwell pode ser empregada como ferramenta principal na caracterização da biodeterioração da madeira, sendo sensível na predição dos estágios iniciais. Dentre as madeiras amazônicas, o cumaru apresentou a maior resistência natural aos fungos apodrecedores. Com relação aos fungos, a podridão parda atacou mais intensamente as três madeiras amazônicas.

Dureza Rockwell da madeira de três espécies amazônicas submetidas a ensaios de apodrecimento acelerado

This study aimed to evaluate the use of Rockwell hardness in the characterization of the biodeterioration of Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru) woods, which were submitted to decay fungi Trametes versicolor (white rot) and Gloeophyllum trabeum (brown rot). For this purpose, specimens of each Amazon species were submitted to decay fungi, according to ASTM D2017 (2005). The characterization of the Rockwell hardness was performed weekly until the fourth week, and then every two weeks until the twentieth week. Additionally, it was determined the mass loss, according to criteria established by ASTM D2017 (2005). The results indicated that the Rockwell hardness can be used as a primary tool in the characterization of the biodeterioration of wood, being sensitive in predicting the early stages. Among the Amazon woods, cumaru wood showed a greater natural resistance to decay fungi. With respect to decay fungi, brown rot more intensely attacked the three Amazon woods.

Objetivou-se avaliar o emprego de ensaios de dureza Rockwell na caracterização da biodeterioração das madeiras de Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru), submetidas ao ataque dos fungos apodrecedores Trametes versicolor (podridão branca) e Gloeophyllum trabeum (podridão parda). Para tanto, corpos de prova de cada espécie amazônica foram submetidos a ensaios de apodrecimento acelerado, de acordo com a ASTM D2017 (2005), durante 20 semanas. A caracterização da dureza Rockwell foi realizada semanalmente até a 4ª semana e, posteriormente, a cada duas semanas, até a 20ª semana. Adicionalmente, foram determinadas as perdas de massa, conforme critérios estabelecidos pela ASTM D2017 (2005). Quanto aos resultados, destaca-se que a dureza Rockwell pode ser empregada como ferramenta principal na caracterização da biodeterioração da madeira, sendo sensível na predição dos estágios iniciais. Dentre as madeiras amazônicas, o cumaru apresentou a maior resistência natural aos fungos apodrecedores. Com relação aos fungos, a podridão parda atacou mais intensamente as três madeiras amazônicas.

Dureza Rockwell da madeira de três espécies amazônicas submetidas a ensaios de apodrecimento acelerado

This study aimed to evaluate the use of Rockwell hardness in the characterization of the biodeterioration of Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru) woods, which were submitted to decay fungi Trametes versicolor (white rot) and Gloeophyllum trabeum (brown rot). For this purpose, specimens of each Amazon species were submitted to decay fungi, according to ASTM D2017 (2005). The characterization of the Rockwell hardness was performed weekly until the fourth week, and then every two weeks until the twentieth week. Additionally, it was determined the mass loss, according to criteria established by ASTM D2017 (2005). The results indicated that the Rockwell hardness can be used as a primary tool in the characterization of the biodeterioration of wood, being sensitive in predicting the early stages. Among the Amazon woods, cumaru wood showed a greater natural resistance to decay fungi. With respect to decay fungi, brown rot more intensely attacked the three Amazon woods.

Objetivou-se avaliar o emprego de ensaios de dureza Rockwell na caracterização da biodeterioração das madeiras de Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru), submetidas ao ataque dos fungos apodrecedores Trametes versicolor (podridão branca) e Gloeophyllum trabeum (podridão parda). Para tanto, corpos de prova de cada espécie amazônica foram submetidos a ensaios de apodrecimento acelerado, de acordo com a ASTM D2017 (2005), durante 20 semanas. A caracterização da dureza Rockwell foi realizada semanalmente até a 4ª semana e, posteriormente, a cada duas semanas, até a 20ª semana. Adicionalmente, foram determinadas as perdas de massa, conforme critérios estabelecidos pela ASTM D2017 (2005). Quanto aos resultados, destaca-se que a dureza Rockwell pode ser empregada como ferramenta principal na caracterização da biodeterioração da madeira, sendo sensível na predição dos estágios iniciais. Dentre as madeiras amazônicas, o cumaru apresentou a maior resistência natural aos fungos apodrecedores. Com relação aos fungos, a podridão parda atacou mais intensamente as três madeiras amazônicas.

Durabilidade natural de painéis aglomerados confeccionados com Eucalyptus grandis e Bambusa vulgaris em ensaio de apodrecimento acelerado

The knowledge about lignocellulosic compounds strength to the attack of microorganisms is essential for preventing deterioration and also for knowing the correct usage of the material. Accordingly it was evaluated the natural resistance of wood panels made of particles of wood (Eucalyptus grandis) and/or bamboo (Bambusa vulgaris) to decay fungi. Particleboards were produced in laboratory, each of them with dimensions 50x50x0.95cm and density pre-set at 0.70g cm-3, in proportions of 100:0, 75:25, 50:50, 25:75 and 0:100 of wood and bamboo, respectively. The particles mass represented 91% of the dry mass of each panel while the remainder was formed by the urea-formaldehyde adhesive (8%) and paraffin (1%). The panels were tested in the laboratory and Gloeophyllum trabeum (brown rot) and Trametes versicolor (white rot) were used to determine the natural resistance to attack by wood decay fungi. It was observed that panels which were made with a mixture of particles of wood and bamboo were less resistant to attack by decay fungi. Panels that were made from bamboo or wood only showed similar biological resistance. Among fungi, T. versicolor was the one that attacked panels more severely.

O conhecimento acerca da resistência dos compostos ligno-celulósicos ao ataque de microrganismos é primordial para servir de base à prevenção da deterioração e a correta destinação de emprego do material. Nesse sentido, avaliou-se a resistência natural a fungos apodrecedores de painéis aglomerados confeccionados com partículas de madeira (Eucalyptus grandis) e/ou bambu (Bambusa vulgaris). Foram produzidas, em laboratório, chapas aglomeradas nas dimensões 50x50x0,95cm e massa específica pré-estabelecida em 0,70g cm-3, nas proporções de 100:0, 75:25, 50:50, 25:75 e 0:100 de madeira e bambu, respectivamente. A massa de partículas representou 91% da massa seca de cada painel, sendo, o restante, formado pelo adesivo ureia-formaldeído (8%) e parafina (1%). Para determinação da resistência natural ao ataque de fungos xilófagos, os painéis foram testados em laboratório e utilizados os fungos Gloeophyllum trabeum (podridão parda) e Trametes versicolor (podridão branca), de acordo com a ASTM D 2017 (2005). Quanto aos resultados, foi observado que os painéis confeccionados com mistura de partículas de madeira e bambu apresentaram menor resistência ao ataque dos fungos apodrecedores. Painéis que utilizaram apenas bambu ou madeira apresentaram resistência biológica semelhante. Dentre os fungos, T. versicolor atacou mais severamente os painéis.

Durabilidade natural de painéis aglomerados confeccionados com Eucalyptus grandis e Bambusa vulgaris em ensaio de apodrecimento acelerado

The knowledge about lignocellulosic compounds strength to the attack of microorganisms is essential for preventing deterioration and also for knowing the correct usage of the material. Accordingly it was evaluated the natural resistance of wood panels made of particles of wood (Eucalyptus grandis) and/or bamboo (Bambusa vulgaris) to decay fungi. Particleboards were produced in laboratory, each of them with dimensions 50x50x0.95cm and density pre-set at 0.70g cm-3, in proportions of 100:0, 75:25, 50:50, 25:75 and 0:100 of wood and bamboo, respectively. The particles mass represented 91% of the dry mass of each panel while the remainder was formed by the urea-formaldehyde adhesive (8%) and paraffin (1%). The panels were tested in the laboratory and Gloeophyllum trabeum (brown rot) and Trametes versicolor (white rot) were used to determine the natural resistance to attack by wood decay fungi. It was observed that panels which were made with a mixture of particles of wood and bamboo were less resistant to attack by decay fungi. Panels that were made from bamboo or wood only showed similar biological resistance. Among fungi, T. versicolor was the one that attacked panels more severely.

O conhecimento acerca da resistência dos compostos ligno-celulósicos ao ataque de microrganismos é primordial para servir de base à prevenção da deterioração e a correta destinação de emprego do material. Nesse sentido, avaliou-se a resistência natural a fungos apodrecedores de painéis aglomerados confeccionados com partículas de madeira (Eucalyptus grandis) e/ou bambu (Bambusa vulgaris). Foram produzidas, em laboratório, chapas aglomeradas nas dimensões 50x50x0,95cm e massa específica pré-estabelecida em 0,70g cm-3, nas proporções de 100:0, 75:25, 50:50, 25:75 e 0:100 de madeira e bambu, respectivamente. A massa de partículas representou 91% da massa seca de cada painel, sendo, o restante, formado pelo adesivo ureia-formaldeído (8%) e parafina (1%). Para determinação da resistência natural ao ataque de fungos xilófagos, os painéis foram testados em laboratório e utilizados os fungos Gloeophyllum trabeum (podridão parda) e Trametes versicolor (podridão branca), de acordo com a ASTM D 2017 (2005). Quanto aos resultados, foi observado que os painéis confeccionados com mistura de partículas de madeira e bambu apresentaram menor resistência ao ataque dos fungos apodrecedores. Painéis que utilizaram apenas bambu ou madeira apresentaram resistência biológica semelhante. Dentre os fungos, T. versicolor atacou mais severamente os painéis.

Durabilidade natural do estipe de pupunha (Bactris gasipaes Kunth, Arecaceae) II: insetos

The durability of the stipe of Bactris gasipaes Kunth (Peach palm) when under attack by xylophage insects, is evaluated in the present paper, through forest and urban environment field tests. Five palms with spines and five without spines from the Tabatinga population (Putumayo landrace) were used in the experiment. Disks approximately 30 cm thick were taken from the butt, middle and top portions of each palm and distributed at random in a forest area near the INPA Peach Palm Germoplasm Bane (2º38'S 60º03'W). The time of permanence of the samples was 18 months, and in this period the disks were checked every three months to evaluate the degree of deterioration and collection of insects. In the urban condition, the same procedure was adopted, however each disk was halved to remove the centre and each half was distributed at random, one in a concave and the other in a convex position, on a wooden framework situated in the INPA's campus, Manaus, and checked bimonthly for one year. The results in the forest condition indicated that most of the disks were deteriorated by termites, and useful life of the butt portions varied around 18 months, the middle and the top around 15. The main species of termites were: Heterotermes tenuis (Hagen) (Rhinotermitidae) attacked the butt, middle and the top parts; Nasutitermes similis Emerson (Termitidae) that infested the area of the base and of the middle; Anoplotermes sp. (Termitidae) and Nasutitermes tatarandae (Holmgren) (Termitidae) attacked the medium part of the stipe. In the urban condition, the beetle Dinoderus bifoveolatus Wollston (Bostrichidae), was the most responsible for the deterioration of the samples, followed by the termite N. similis.

Neste trabalho estão apresentados os resultados da durabilidade natural do estipe (madeira) de Bactris gasipaes Kunth (pupunha), quando submetido ao ataque de insetos xilófagos, em ensaios em ambiente florestal e urbano. Foram utilizados dez palmeiras, cinco com espinhos e cinco sem espinhos, de plantios da Fazenda Experimental da Universidade Federal do Amazonas, localizada no km 40 da rodovia Manaus-Boa Vista (BR 174). De cada uma das palmeiras foram cortados três discos de aproximadamente 30 cm de espessura, retirados da base, do meio e do topo. No ambiente florestal, os discos foram distribuídos aleatoriamente, em área próxima ao plantio, no espaçamento de 0,5m, permanecendo durante 18 meses, período no qual foram efetuadas seis inspeções trimestrais para avaliar o grau de deterioração e coleta de insetos. Para o ensaio em condição urbana, os discos foram secionados axialmente para a retirada da medula e distribuídos aleatoriamente, nas posições côncava e convexa, sobre uma estrutura de madeira, localizada no Campus do INPA em Manaus, e inspecionados bimestralmente por um ano. Os resultados do ensaio no ambiente florestal indicaram que a maioria dos discos foi deteriorada por térmitas e a vida útil da base foi em torno de 18 meses, a do meio e do topo em torno de 15. As principais espécies de cupins foram: Heterotermes tenuis (Hagen) (Rhinotermitidae) responsável pela deterioração da parte basal, mediana e o topo; Nasutitermes similis Emerson (Termitidae) que infestou a região da base e do meio; Anoplotermes sp.(Termitidae) e Nasutitermes tatarandae (Holmgren) (Termitidae) responsáveis pela infestação da parte mediana do estipe. No ambiente urbano, o principal responsável pela deterioração das amostras foi o besouro Dinoderus bifoveolatus Wollston (Bostrichidae), e em seguida, o térmita N. similis.