Monitoramento da biodeterioração da madeira de três espécies amazônicas pela técnica da colorimetria / Monitoring of biodeterioration of three Amazonian wood species by the colorimetry technique

This work aimed to evaluate the use of colorimetry in the characterization of biodeterioration marupá, jequitibá and cumaru wood, submitted to white and brown rot. For this purpose, specimens of each Amazonian species were submitted to accelerated decay tests, according to American Society for Testing and Materials - ASTM D2017, during 20 weeks. With a colorimeter, the colorimetric parameters L* (lightness), a* (green-red coordinate), b* (blue-yellow coordinate) and total color change (ΔE) were determined weekly until the fourth week, and then every two weeks until the twentieth week. Additionally, it was determined the mass loss. The results indicated that the colorimetry was effective in monitoring of biodeterioration of wood, as well as to differentiate white and brown rot. The best predictions of natural resistance to white and brown rot were obtained with the parameters b* and L*, respectively. We also emphasizes the use of ΔE to estimate the biodeterioration of wood, because of their significant correlations with weight loss.

Objetivou-se avaliar o emprego da colorimetria na caracterização da biodeterioração das madeiras de marupá, jequitibá e cumaru submetidas ao ataque de fungos de podridão branca e parda. Para tanto, corpos de prova de cada espécie amazônica foram submetidos a ensaios de apodrecimento acelerado, de acordo com a American Society for Testing and Materials - ASTM D2017, durante 20 semanas. Os parâmetros colorimétricos L* (luminosidade), a* (coordenada verde-vermelho), b* (coordenada amarelo-azul) e a variação total da cor (ΔE) foram determinados semanalmente até a quarta semana, e posteriormente a cada duas semanas até a vigésima semana, com auxílio de um espectrofotocolorímetro. Adicionalmente, foram determinadas as perdas de massa dos corpos de prova. Os resultados permitiram destacar que a colorimetria foi eficaz no monitoramento da biodeterioração da madeira, bem como para diferenciação da podridão branca e parda. As melhores predições da resistência natural aos fungos de podridão branca e parda foram obtidas com os parâmetros b* e L*, respectivamente. Enfatiza-se também, o emprego da ΔE como parâmetro auxiliar na estimativa da biodeterioração da madeira, em razão de suas correlações significativas com a perda de massa.

Monitoramento da biodeterioração da madeira de três espécies amazônicas pela técnica da colorimetria / Monitoring of biodeterioration of three Amazonian wood species by the colorimetry technique

This work aimed to evaluate the use of colorimetry in the characterization of biodeterioration marupá, jequitibá and cumaru wood, submitted to white and brown rot. For this purpose, specimens of each Amazonian species were submitted to accelerated decay tests, according to American Society for Testing and Materials - ASTM D2017, during 20 weeks. With a colorimeter, the colorimetric parameters L* (lightness), a* (green-red coordinate), b* (blue-yellow coordinate) and total color change (ΔE) were determined weekly until the fourth week, and then every two weeks until the twentieth week. Additionally, it was determined the mass loss. The results indicated that the colorimetry was effective in monitoring of biodeterioration of wood, as well as to differentiate white and brown rot. The best predictions of natural resistance to white and brown rot were obtained with the parameters b* and L*, respectively. We also emphasizes the use of ΔE to estimate the biodeterioration of wood, because of their significant correlations with weight loss.(AU)

Objetivou-se avaliar o emprego da colorimetria na caracterização da biodeterioração das madeiras de marupá, jequitibá e cumaru submetidas ao ataque de fungos de podridão branca e parda. Para tanto, corpos de prova de cada espécie amazônica foram submetidos a ensaios de apodrecimento acelerado, de acordo com a American Society for Testing and Materials - ASTM D2017, durante 20 semanas. Os parâmetros colorimétricos L* (luminosidade), a* (coordenada verde-vermelho), b* (coordenada amarelo-azul) e a variação total da cor (ΔE) foram determinados semanalmente até a quarta semana, e posteriormente a cada duas semanas até a vigésima semana, com auxílio de um espectrofotocolorímetro. Adicionalmente, foram determinadas as perdas de massa dos corpos de prova. Os resultados permitiram destacar que a colorimetria foi eficaz no monitoramento da biodeterioração da madeira, bem como para diferenciação da podridão branca e parda. As melhores predições da resistência natural aos fungos de podridão branca e parda foram obtidas com os parâmetros b* e L*, respectivamente. Enfatiza-se também, o emprego da ΔE como parâmetro auxiliar na estimativa da biodeterioração da madeira, em razão de suas correlações significativas com a perda de massa.(AU)

Qualidade de rosas de corte tratadas com produtos naturais

Use of natural products like floral preservative has contributed to reduce indiscriminate use of chemical products. Therefore, this research tested solutions to keep quality and to increase commercial durability of 'Vega' cv. cut roses. It was used a casual design in a factorial schema composed by six post harvest treatments and four evaluation dates. The following treatments were conducted: 1) Distilled water; 2) Metil jasmonate (350µM) application in pulsing form for four hours; 3) Metil jasmonate (500µM) spraying; 4) Mint oil (100ppm); 5) Ginger oil (100ppm); and 6) Propolis (0.05%) used as a maintenance solution. Flowers stayed in an environment at 20±2°C and 67±3% RH. Physiological and qualitative evaluations were conducted. Generally speaking, natural products presented a beneficial action over the shelf life of flowers. However, metil jasmonate spraying was, in all evaluated parameters, the most efficient product to maintain floral quality, providing a lower fresh mass loss and a lower respiratory rate of flowers. It also permitted improvement in coloration maintenance, water relative content and reducing sugars.

O uso de produtos naturais como conservantes florais vem contribuir para a redução do uso indiscriminado de produtos químicos potencialmente tóxicos. Assim, objetivou-se neste trabalho testar soluções para manter a qualidade e aumentar a durabilidade comercial de rosas vermelhas cortadas da cv. 'Vega'. Foi empregado o delineamento inteiramente casualizado, em esquema fatorial composto por seis tratamentos pós-colheita e quatro datas de avaliação. Os tratamentos realizados foram os seguintes: 1) Água destilada; 2) Metil jasmonato (350µM); aplicado na forma de pulsing, por quatro horas; 3) Pulverização de Metil jasmonato (500µM); 4) Óleo de menta (100ppm); 5) Óleo de gengibre (100ppm); e 6) Própolis (0,05%), utilizados na forma de solução de manutenção. As flores foram mantidas em ambiente com temperatura de 20±2°C e umidade relativa de 67±3%. Procedeu-se a avaliações fisiológicas e qualitativas. De modo geral, os produtos naturais apresentaram ação benéfica sobre a vida de vaso das flores, entretanto, o uso do metil jasmonato em pulverização mostrou, em todos os parâmetros avaliados, ser o produto mais eficiente para manutenção da qualidade floral, promovendo menor perda de massa fresca e menor taxa respiratória das flores, além de permitir melhoria na manutenção da coloração, do conteúdo relativo de água e de carboidratos redutores.

Qualidade de rosas de corte tratadas com produtos naturais

Use of natural products like floral preservative has contributed to reduce indiscriminate use of chemical products. Therefore, this research tested solutions to keep quality and to increase commercial durability of 'Vega' cv. cut roses. It was used a casual design in a factorial schema composed by six post harvest treatments and four evaluation dates. The following treatments were conducted: 1) Distilled water; 2) Metil jasmonate (350µM) application in pulsing form for four hours; 3) Metil jasmonate (500µM) spraying; 4) Mint oil (100ppm); 5) Ginger oil (100ppm); and 6) Propolis (0.05%) used as a maintenance solution. Flowers stayed in an environment at 20±2°C and 67±3% RH. Physiological and qualitative evaluations were conducted. Generally speaking, natural products presented a beneficial action over the shelf life of flowers. However, metil jasmonate spraying was, in all evaluated parameters, the most efficient product to maintain floral quality, providing a lower fresh mass loss and a lower respiratory rate of flowers. It also permitted improvement in coloration maintenance, water relative content and reducing sugars.

O uso de produtos naturais como conservantes florais vem contribuir para a redução do uso indiscriminado de produtos químicos potencialmente tóxicos. Assim, objetivou-se neste trabalho testar soluções para manter a qualidade e aumentar a durabilidade comercial de rosas vermelhas cortadas da cv. 'Vega'. Foi empregado o delineamento inteiramente casualizado, em esquema fatorial composto por seis tratamentos pós-colheita e quatro datas de avaliação. Os tratamentos realizados foram os seguintes: 1) Água destilada; 2) Metil jasmonato (350µM); aplicado na forma de pulsing, por quatro horas; 3) Pulverização de Metil jasmonato (500µM); 4) Óleo de menta (100ppm); 5) Óleo de gengibre (100ppm); e 6) Própolis (0,05%), utilizados na forma de solução de manutenção. As flores foram mantidas em ambiente com temperatura de 20±2°C e umidade relativa de 67±3%. Procedeu-se a avaliações fisiológicas e qualitativas. De modo geral, os produtos naturais apresentaram ação benéfica sobre a vida de vaso das flores, entretanto, o uso do metil jasmonato em pulverização mostrou, em todos os parâmetros avaliados, ser o produto mais eficiente para manutenção da qualidade floral, promovendo menor perda de massa fresca e menor taxa respiratória das flores, além de permitir melhoria na manutenção da coloração, do conteúdo relativo de água e de carboidratos redutores.

Qualidade de rosas de corte tratadas com produtos naturais

Use of natural products like floral preservative has contributed to reduce indiscriminate use of chemical products. Therefore, this research tested solutions to keep quality and to increase commercial durability of 'Vega' cv. cut roses. It was used a casual design in a factorial schema composed by six post harvest treatments and four evaluation dates. The following treatments were conducted: 1) Distilled water; 2) Metil jasmonate (350µM) application in pulsing form for four hours; 3) Metil jasmonate (500µM) spraying; 4) Mint oil (100ppm); 5) Ginger oil (100ppm); and 6) Propolis (0.05%) used as a maintenance solution. Flowers stayed in an environment at 20±2°C and 67±3% RH. Physiological and qualitative evaluations were conducted. Generally speaking, natural products presented a beneficial action over the shelf life of flowers. However, metil jasmonate spraying was, in all evaluated parameters, the most efficient product to maintain floral quality, providing a lower fresh mass loss and a lower respiratory rate of flowers. It also permitted improvement in coloration maintenance, water relative content and reducing sugars.

O uso de produtos naturais como conservantes florais vem contribuir para a redução do uso indiscriminado de produtos químicos potencialmente tóxicos. Assim, objetivou-se neste trabalho testar soluções para manter a qualidade e aumentar a durabilidade comercial de rosas vermelhas cortadas da cv. 'Vega'. Foi empregado o delineamento inteiramente casualizado, em esquema fatorial composto por seis tratamentos pós-colheita e quatro datas de avaliação. Os tratamentos realizados foram os seguintes: 1) Água destilada; 2) Metil jasmonato (350µM); aplicado na forma de pulsing, por quatro horas; 3) Pulverização de Metil jasmonato (500µM); 4) Óleo de menta (100ppm); 5) Óleo de gengibre (100ppm); e 6) Própolis (0,05%), utilizados na forma de solução de manutenção. As flores foram mantidas em ambiente com temperatura de 20±2°C e umidade relativa de 67±3%. Procedeu-se a avaliações fisiológicas e qualitativas. De modo geral, os produtos naturais apresentaram ação benéfica sobre a vida de vaso das flores, entretanto, o uso do metil jasmonato em pulverização mostrou, em todos os parâmetros avaliados, ser o produto mais eficiente para manutenção da qualidade floral, promovendo menor perda de massa fresca e menor taxa respiratória das flores, além de permitir melhoria na manutenção da coloração, do conteúdo relativo de água e de carboidratos redutores.

Produção de celulose nanofibrilada a partir de polpa organossolve de bambu para nanoreforço de compósitos cimentícios

Fibras vegetais de baixo módulo de elasticidade são conhecidas pela sua capacidade de aumentar a energia absorvida durante o carregamento dos materiais cimentícios, especialmente no estágio pós-fissurado. A utilização de nanofibras celulósicas pode contribuir para a tenacificação de matrizes frágeis, tanto por melhorar o empacotamento das partículas, com o refinamento de poros, quanto pela interceptação de fissuras na escala nanométrica, com a respectiva absorção de energia. A celulose nanofibrilada provém de um recurso natural, abundante e renovável, possui bom desempenho mecânico e superfície específica elevada, o que contribui para melhorar a adesão entre as partículas de cimento. Estes fatores justificam o uso da celulose nanofibrilada e a tornam uma boa alternativa como nanoreforço de materiais cimentícios. Com isso, o objetivo deste trabalho foi a produção de celulose nanofibrilada a partir de polpa organossolve de bambu, definindo a melhor condição para sua produção e posterior utilização como reforço em compósitos híbridos (reforçados na nano e micro escalas) em comparação a compósitos reforçados somente com microfibras (polpa) pelos processos de produção por sucção e prensagem, e extrusão. A celulose nanofibrilada foi produzida utilizando-se polpa não-branqueada e branqueada, por meio de 5, 10, 15 e 20 ciclos de nanofibrilação pelo processo grinding. Foram realizados testes químicos, físicos e mecânicos para definição da condição ótima de nanofibrilação. A celulose nanofibrilada não-branqueada produzida mediante 10 ciclos foi definida como a melhor opção para utilização nos compósitos híbridos, por possuírem maior módulo de elasticidade e, em razão da sua maior estabilidade estrutural, apresentam maior resistência à degradação em meio alcalino. Os compósitos foram submetidos à cura por carbonatação acelerada para mitigação da degradação da fibra pela diminuição do pH da matriz e também para refinamento dos poros. Os compósitos foram submetidos ao teste de envelhecimento acelerado por meio de 200 ciclos de imersão e secagem para análise da sua degradação. Os compósitos híbridos e reforçados somente com polpa aos 28 dias de cura e após o envelhecimento acelerado foram submetidos aos ensaios físicos, mecânicos e microestruturais para acompanhamento do efeito da celulose nanofibrilada nas suas propriedades. Nos compósitos produzidos pelos dois processos aos 28 dias não houve diferença estatística para as propriedades físicas testadas, comparando-se os compósitos híbridos e os reforçados somente com polpa. No processo de sucção e prensagem, embora útil para ajustes na formulação e na cura do compósito híbrido, não se percebeu contribuição estatisticamente significativa da celulose nanofibrilada na formação de pontes de transferência de tensões, e, portanto sem o correspondente aumento na resistência mecânica dos compósitos. Nos compósitos extrudados, a celulose nanofibrilada atuou de modo a melhorar o comportamento mecânico do compósito híbrido em comparação ao compósito sem nanofibras. Esta melhoria pode estar associada à maior adesão entre as nanofibrilas e a matriz cimentícia, o que foi atestado pela análise microestrutural (MEV) dos compósitos. Após o envelhecimento acelerado os compósitos com e sem nanofibras produzidos pelos dois processos não apresentaram redução do desempenho mecânico, o que se atribui à menor alcalinidade provida pela carbonatação acelerada.

Low elastic modulus vegetable fibers are known for their ability to increase the energy absorbed by cement based materials while they are loaded, especially during the post-crack stage. The use of cellulose nanofibers may contribute for toughening of brittle matrices and improving particle packing by both pore refining and crack intercepting at nanoscale, with the corresponding energy absorption. Nanofibrillated cellulose comes from a natural, abundant and renewable resources, it has good mechanical peformance and high specific surface, which contributes to improve the adhesion between the cement particles. These factors justify the use of nanofibrillated cellulose and give rise to an alternative nanoreinforcement for cement based materials. Thus, the aim of this work was the production of the nanofibrillated cellulose from bamboo organosolv pulp, establishing the best condition for its production and subsequent use as reinforcement in hybrid composites (both nano and micro-scale reinforcement) compared to composites reinforced with only microfibers (pulp), produced by the slurry vacuum dewatering followed by pressing and extrusion methods. The nanofibrillated cellulose was produced submitting unbleached and bleached pulps to 5, 10, 15 and 20 nanofibrillated cycles by the grinding method. Chemical, physical and mechanical tests were carried out to define the optimal condition to nanofibrillation. The unbleached nanofibrillated cellulose produced by 10 cycles was defined as the best option to be used in hybrid composites, since their greater modulus of elasticity and, because of their greater structural chemical stability, higher resistance to degradation in alkaline environments. The composites were subjected to accelerated carbonation curing process to mitigate the degradation of fiber by reducing the matrix pH and also to refine the pores. The composites were subjected to accelerated aging process by means of 200 wet and dry cycles to assess their degradation. The hybrid composites and the composites reinforced only with pulp at 28 days and after accelerated aging were subjected to physico-mechanical and microstructural tests to study the effect of the nanofibrillated cellulose on their properties. There was no difference in the physical properties of the hybrid composites and composites reinforced with only pulp, produced by the two processes at 28 days. For the slurry vacuum dewatering followed by pressing process, although useful for adjustments in the formulation and cure hybrid composite, there was no statistically significant contribution of the nanofibrillated cellulose in the formation of stress transfer bridges, and therefore without a corresponding increase in the mechanical strength of the composites. For the extruded composites, the nanofibrillated cellulose improved the mechanical behavior of the hybrid composite compared to the composite without nanofiber. This improvement may be associated with greater adherence between the nanofibrils and the cement matrix, which was confirmed by microstructural analysis (SEM) of the composites. After accelerated aging, the composites with and without nanofibers produced by the two processes showed no reduction in mechanical performance, which is attributed to the lower alkalinity provided by the accelerated carbonation.