Exploring the electrochemical performance of layered Bi2Se3 hexagonal platelets as the anode material for lithium-ion batteries.

The escalating need for lithium-ion batteries (LIBs), driven by their expanding range of applications in our daily lives, has led to a surge in interest in metal selenides as potential anode materials. Among them, Bi2Se3 stands out as a promising anode material for LIBs due to its unique layered structure. Herein, we explored hexagonally structured layered Bi2Se3 platelets synthesized using the solvothermal method. The electrochemical performance of these platelets in LIBs was thoroughly examined, revealing an impressive initial discharge specific capacity of 556 mA h g-1 at a current density of 100 mA g-1 and a coulombic efficiency of 66.5%. Improved cycling stability, rate performance, and discharge voltage profile at various current densities were observed. The plateaus observed during the charge/discharge profile were clearly illustrated by the CV results. The reaction kinetics indicated that both ion diffusion and pseudo-capacitance behavior are crucial for the observed high electrochemical performance. Moreover, the hexagonal Bi2Se3 platelets exhibited a high ion-diffusion coefficient of 1.8 × 10-13 cm2 s-1 and a charge transfer impedance of 23 Ω post-cycling. Furthermore, the crystal structure, lattice vibrational bonding, and surface morphology of Bi2Se3 were explored using X-ray diffraction, Raman spectroscopy, scanning electron microscopy, and transmission electron microscopy. FTIR spectroscopy was utilized for identifying the functional groups, while X-ray photoelectron spectroscopy (XPS) was used to identify the elemental composition and oxidation states of Bi2Se3.

Starch-Assisted Synthesis of Bi2S3 Nanoparticles for Enhanced Dielectric and Antibacterial Applications.

Starch [(C6H10O5) n ]-stabilized bismuth sulfide (Bi2S3) nanoparticles (NPs) were synthesized in a single-pot reaction using bismuth nitrate pentahydrate (Bi(NO3)3·5H2O) and sodium sulfide (Na2S) as precursors. Bi2S3 NPs were stable over time and a wide band gap of 2.86 eV was observed. The capping of starch on the Bi2S3 NPs prevents them from agglomeration and provides regular uniform shapes. The synthesized Bi2S3 NPs were quasispherical, and the measured average particle size was ∼11 nm. The NPs are crystalline with an orthorhombic structure as determined by powder X-ray diffraction and transmission electron microscopy. The existence and interaction of starch on the NP's surface were analyzed using circular dichroism. Impedance spectroscopy was used to measure the electronic behavior of Bi2S3 NPs at various temperatures and frequencies. The dielectric measurements on the NPs show high dielectric polarizations. Furthermore, it was observed that the synthesized Bi2S3 NPs inhibited bacterial strains (Bacillus subtilis, Escherichia coli, Pseudomonas aeruginosa, and Staphylococcus aureus) and demonstrated substantial antibacterial activity.