Evaluation of structural coloration of experimental flowable resin composites.

OBJECTIVE: To examine the effect of filler contentTo examine the effect of filler content on structural coloration of experimental flowable resin composites. OVERVIEW: Experimental composites containing spherical fillers and different filler contents (30, 40, 50, 60 and 70 wt%), a structural colored resin composite (Omnichroma), and a nanohybrid flowable resin composite (Gracefil LoFlo) were used. The optical characteristics of the specimens were measured on standard black and white backgrounds using a spectrophotometer under CIE D65 illuminant and the L*a*b* values were determined. The color matching abilities to artificial teeth were evaluated using the ΔE*ab and ΔE00 color difference formulas. One-way analysis of variance and Tukey's post hoc test were used. The spectral reflectance of experimental composites showed different trends in different backgrounds, plate thickness, and filler contents. In particular, higher spectral reflectance was observed on the white background at wavelengths ranging from 450 to 700 nm in both 1.5 and 3.0 mm plates when compared to the black background. The percent reflectivity tended to decrease with a decrease of the filler contents. The color matching abilities of the experimental composites improved with the increase in the filler contents. CONCLUSIONS: Structural coloration of the flowable resin composites were affected by the filler contents. CLINICAL SIGNIFICANCE: Clinical Significance: Higher filler contents might be needed to achieve the optimal color properties of structural colored flowable resin composites, thereby improving the restoration esthetics.

Influence of different curing modes on the bonding effectiveness of self-adhesive resin luting cements in combination with universal adhesives.

OBJECTIVES: This study aimed to investigate the immediate dentin bond performance and bond durability of self-adhesive resin luting cements (RLCs) in combination with universal adhesives in different curing modes. METHODS: Two self-adhesive RLCs were used with universal adhesives as primers. They were also used alone as self-adhesive RLCs. Two multiple-step RLC systems were used as comparison materials. To measure the shear bond strength (SBS) in different curing modes, 12 specimens were prepared for each group. Stainless-steel rods were bonded to bovine dentin, and the bonded specimens were assigned to the baseline group (stored for 24 h) and artificially aged group (thermal cycling [TC], 10,000 cycles). After each storage period, the SBS of the bonded specimens was measured. The Knoop hardness number (KHN) of the cured RLCs was measured with or without primer application in different curing modes at 24 h and after 10,000 TC. The representative RLC/dentin interfaces were observed using scanning electron microscopy (SEM). RESULTS: Dentin SBS was significantly influenced by the RLC system but not by the curing mode. Self-adhesive RLCs alone showed significantly lower SBS values than self-adhesive RLCs with primer regardless of the curing mode or storage period. The storage period, curing mode, and RLC system significantly influenced the KHN. SIGNIFICANCE: The use of universal adhesives as a primer may help enhance the immediate dentin bond performance and bond durability of self-adhesive RLCs.