Pyrometric-Based Melt Pool Monitoring Study of CuCr1Zr Processed Using L-PBF.

The potential of in situ melt pool monitoring (MPM) for parameter development and furthering the process understanding in Laser Powder Bed Fusion (LPBF) of CuCr1Zr was investigated. Commercial MPM systems are currently being developed as a quality monitoring tool with the aim of detecting faulty parts already in the build process and, thus, reducing costs in LPBF. A detailed analysis of coupon specimens allowed two processing windows to be established for a suitably dense material at layer thicknesses of 30 µm and 50 µm, which were subsequently evaluated with two complex thermomechanical-fatigue (TMF) panels. Variations due to the location on the build platform were taken into account for the parameter development. Importantly, integrally averaged MPM intensities showed no direct correlation with total porosities, while the robustness of the melting process, impacted strongly by balling, affected the scattering of the MPM response and can thus be assessed. However, the MPM results, similar to material properties such as porosity, cannot be directly transferred from coupon specimens to components due to the influence of the local part geometry and heat transport on the build platform. Different MPM intensity ranges are obtained on cuboids and TMF panels despite similar LPBF parameters. Nonetheless, besides identifying LPBF parameter windows with a stable process, MPM allowed the successful detection of individual defects on the surface and in the bulk of the large demonstrators and appears to be a suitable tool for quality monitoring during fabrication and non-destructive evaluation of the LPBF process.

Pandora's Box-Influence of Contour Parameters on Roughness and Subsurface Residual Stresses in Laser Powder Bed Fusion of Ti-6Al-4V.

The contour scan strategies in laser powder bed fusion (LPBF) of Ti-6Al-4V were studied at the coupon level. These scan strategies determined the surface qualities and subsurface residual stresses. The correlations to these properties were identified for an optimization of the LPBF processing. The surface roughness and the residual stresses in build direction were linked: combining high laser power and high scan velocities with at least two contour lines substantially reduced the surface roughness, expressed by the arithmetic mean height, from values as high as 30 µm to 13 µm, while the residual stresses rose from ~340 to about 800 MPa. At this stress level, manufactured rocket fuel injector components evidenced macroscopic cracking. A scan strategy completing the contour region at 100 W and 1050 mm/s is recommended as a compromise between residual stresses (625 MPa) and surface quality (14.2 µm). The LPBF builds were monitored with an in-line twin-photodiode-based melt pool monitoring (MPM) system, which revealed a correlation between the intensity quotient I2/I1, the surface roughness, and the residual stresses. Thus, this MPM system can provide a predictive estimate of the surface quality of the samples and resulting residual stresses in the material generated during LPBF.

An Assessment of Subsurface Residual Stress Analysis in SLM Ti-6Al-4V.

Ti-6Al-4V bridges were additively fabricated by selective laser melting (SLM) under different scanning speed conditions, to compare the effect of process energy density on the residual stress state. Subsurface lattice strain characterization was conducted by means of synchrotron diffraction in energy dispersive mode. High tensile strain gradients were found at the frontal surface for samples in an as-built condition. The geometry of the samples promotes increasing strains towards the pillar of the bridges. We observed that the higher the laser energy density during fabrication, the lower the lattice strains. A relief of lattice strains takes place after heat treatment.