Ettringite is a naturally occurring mineral found in cementitious matrices that is known for its ability to incorporate environmentally mobile oxyanion contaminants. To better assess this immobilization mechanism for contaminants within cementitious waste forms intended for nuclear waste storage, this work explores how mixed oxyanion contaminants compete for ettringite incorporation and influence the evolving mineralogy. Ettringite was precipitated in the presence of TcO4-, IO3-, and/or CrO42-, known contaminants of concern to nuclear waste treatment, over pre-determined precipitation periods. Solution analyses quantified contaminant removal, and the collected solid was characterized using bulk and microprobe X-ray diffraction coupled with pair distribution function and microprobe X-ray fluorescence analyses. Results suggest that ≥96% IO3- is removed from solution, regardless of ettringite precipitation time or the presence of TcO4- or CrO42-. However, TcO4- removal remained <20%, was not significantly improved with longer ettringite precipitation times, and decreased to zero in the presence of IO3-. When IO3- is co-mingled with CrO42-, calcite and gypsum are formed as secondary mineral phases, which allows for oxyanion partitioning, e.g., IO3- incorporation into ettringite, and CrO42- incorporation into calcite. Results from this work exemplify the importance of competitive immobilization when assessing waste form performance and environmental risk of contaminant release.
Assuntos
Minerais , Resíduos Radioativos , Difração de Raios XRESUMO
Technetium-99 immobilization in low-temperature nuclear waste forms often relies on additives that reduce environmentally mobile pertechnetate (TcO4-) to insoluble Tc(IV) species. However, this is a short-lived solution unless reducing conditions are maintained over the hazardous life cycle of radioactive wastes (some â¼10,000 years). Considering recent experimental observations, this work explores how rapid formation of ettringite [Ca6Al2(SO4)3(OH)12·26(H2O)], a common mineral formed in cementitious waste forms, may be used to directly immobilize TcO4-. Results from ab initio molecular dynamics (AIMD) simulations and solid-phase characterization techniques, including synchrotron X-ray absorption, fluorescence, and diffraction methods, support successful incorporation of TcO4- into the ettringite crystal structure via sulfate substitution when synthesized by aqueous precipitation methods. One sulfate and one water are replaced with one TcO4- and one OH- during substitution, where Ca2+-coordinated water near the substitution site is deprotonated to form OH- for charge compensation upon TcO4- substitution. Furthermore, AIMD calculations support favorable TcO4- substitution at the SO42- site in ettringite rather than gypsum (CaSO4·2H2O, formed as a secondary mineral phase) by at least 0.76 eV at 298 K. These results are the first of their kind to suggest that ettringite may contribute to TcO4- immobilization and the overall lifetime performance of cementitious waste forms.
Assuntos
Resíduos Radioativos , Pertecnetato Tc 99m de Sódio , Minerais , SulfatosRESUMO
Borosilicate glasses are widely used for radioactive waste disposal due to their ability to incorporate a variety of contaminants and radionuclides while exhibiting high durability in various disposal scenarios. This research evaluated the dissolution of borosilicate glass using both single-pass-flow-through (ASTM C1662-18) and product consistency test (ASTM C1285-21) methods with different solutions, including a cementitious-contacted water (called grout-contacted, GC, from this point) and solutions with varying levels of dissolved cementitious species such as Si, Ca, Al. The results indicated that the presence of Ca plays a crucial role in suppressing glass corrosion, as evidenced by the slower normalized dissolution rates, which were one order of magnitude lower for boron and two orders of magnitude lower for rhenium, observed in both Ca-amended and GC solutions compared to the pH 12 buffer solution. This effect is attributed to the formation of a dense, low-porosity, and strongly bonded calcium silicate hydrate (CSH) layer on the glass surface, which implies that a glass corrosion process is influenced by ion exchange involving alkali ions Na+, K+, Ca2+, and hydrogen-containing species. A small number of glass particles treated in the GC solution showed minor corrosion pits in the form of shallow craters with an average diameter of approximately 500 µm. This observation is correlated with a significant reduction, 2000 to 3000 times lower, in the cumulative volume of glass pores, indicating that smaller pore voids were "sealed" in the presence of Ca2+ ions, likely attributed to the formation of CSH precipitation or other corrosion products such as calcium carbonate saturated from the grout solution. These findings suggest that the presence of dissolved Ca in the GC solution can slow down the dissolution of borosilicate glass, contrary to the expected trend of higher dissolution rates resulting from exposure to high alkaline and thus higher pH solutions.
RESUMO
Radioiodine capture and immobilization is not only important to consider during the operation of reactors (i.e., I-131), during nuclear accidents (i.e., I-131 and I-129) or nuclear fuel reprocessing (i.e., I-131 and I-129), but also during disposal of nuclear wastes (i.e., I-129). Most disposal plans for I-129-containing waste forms (including spent nuclear fuel) propose to store them in underground repositories. Here, iodine can be highly mobile and, given its radiotoxicity, needs to be carefully managed to minimize long-term environmental impacts arising from disposal. Typically, any process that has been used to capture iodine from reprocessing or in a reactor is not suitable for direct disposal, rather conversion into a wasteform for disposal is required. The objectives of these materials are to use either chemical immobilization or physical encapsulation to reduce the leaching of iodine by groundwaters. Some of the more recent ideas have been to design capture materials that better align with disposal concepts, making the industrial processing requirements easier. Research on iodine capture materials and wasteforms has been extensive. This review will act as both an update on the state of the research since the last time it was comprehensively summarized, and an evaluation of the industrial techniques required to create the proposed iodine wasteforms in terms of resulting material chemistry and applicability.
RESUMO
The interaction between radionuclides and cementitious material phases is crucial in the prediction of the long-term disposal behavior of cementitious waste forms. This work focuses on the behavior of technetium-99 (Tc) within a hydrated-lime based waste form developed as a candidate to immobilize high-sulphate containing liquid wastes known to inhibit cement solidification when using a fly ash based formulation. In leach testing, the hydrated-lime based formulation demonstrated improvement in Tc retention over a fly ash containing formulation beginning after 14 d leaching. The mineralogical evolution of the hydrated-lime samples during leach testing showed a decrease in portlandite content and reduction capacity at the onset of the Tc retention improvement. Leach testing upwards of 400 days showed the improved Tc retention was sustained. Samples cured for different lengths of time (28 days vs 60 days) confirmed that the improved Tc retention and mineralogic change was caused by cement - leachant interactions and not the sample curing time. The Tc observed diffusivities in the hydrated-lime samples are amongst the lowest measured in a cement waste form tested for development at the US Department of Energy Hanford site, leading to a possible pathway to improved cement conditioning where contaminants can be retained for long disposal times.
Assuntos
Cinza de Carvão , Tecnécio , Compostos de Cálcio , Materiais de Construção , ÓxidosRESUMO
Both granular activated carbon (GAC) and silver mordenite (AgM) are utilized for the removal of contaminants and radionuclides (e.g., radioiodine) from off-gas streams in nuclear fuel reprocessing and high temperature immobilization of nuclear waste. Following their service lifetimes, the GAC and AgM contain an inventory of contaminants and radionuclides and require stabilization in a matrix for disposal. GAC and AgM are referred to as solid secondary waste (SSW) materials. Cementitious waste forms can be used as the stabilization matrix for SSW, however, for successful stabilization, the inclusion of GAC and AgM should not negatively impact the physical behavior of the cementitious waste form or increase release of the contaminants/radionuclides compared to the baseline case without stabilization. The present work focuses on evaluation of cement formulations, with and without slag, for the stabilization of iodine-loaded GAC or AgM. The results showed that both a slag-containing and slag-free formulations were able to stabilize GAC and AgM, up to 30 vol%, without deleterious impacts on the bulk physical properties of the encapsulating matrix. When monolithic samples of the GAC or AgM containing cement formulations were subjected to leach tests, it was observed that iodide leached from the SSW) had limited sorption to either of the cement matrices. Nonetheless, the iodine can interact with the SSW materials themselves. Specifically, iodine retention within monolithic samples containing the iodine-loaded GAC or AgM was improved for AgM containing waste forms while no improvement was observed for the GAC containing waste forms. The improvement for the AgM containing waste forms was likely due to an enrichment of Ag at the interface between the AgM particles and the cement matrix that can impede iodine migration out from the waste form. The results are significant in highlighting the potential for long-term retention of iodine in specific cementitious waste forms.
Assuntos
Iodo , Monitoramento de Radiação , Silicatos de Alumínio , Carvão Vegetal , Iodetos , Radioisótopos do Iodo , PrataRESUMO
The objective of this review is to evaluate materials for use as a barrier or other deployed technology to treat technetium-99 (Tc) in the subsurface. To achieve this, Tc interactions with different materials are considered within the context of remediation strategies. Several naturally occurring materials are considered for Tc immobilization, including iron oxides and low solubility sulfide phases. Synthetic materials are also considered, and include tin-based materials, sorbents (resins, activated carbon, modified clays), layered double hydroxides, metal organic frameworks, cationic polymeric networks and aerogels. All of the materials were evaluated for their potential in-situ and ex-situ performance with respect to long-term Tc uptake and immobilization, environmental impacts and deployability. Other factors such as the technology maturity, cost and availability were also considered. Given the difficulty of evaluating materials under different experimental conditions (e.g., solution chemistry, redox conditions, solution to solid ratio, Tc concentration etc.), a subset of these materials will be selected, on the basis of this review, for subsequent standardized batch loading tests.
RESUMO
One of the key challenges for radioactive waste management is the efficient capture and immobilization of radioiodine, because of its radiotoxicity, high mobility in the environment, and long half-life (t1/2â¯=â¯1.57â¯×â¯107 years). Silver-functionalized silica aerogel (AgAero) represents a strong candidate for safe sequestration of radioiodine from various nuclear waste streams and subsurface environments. Batch sorption experiments up to 10 days long were carried out in oxic and anoxic conditions in both deionized water (DIW) and various Hanford Site Waste Treatment Plant (WTP) off-gas condensate simulants containing from 5 to 10â¯ppm of iodide (I-) or iodate (IO3-). Also tested was the selectivity of AgAero towards I- in the presence of other halide anions. AgAero exhibited fast and complete removal of I- from DIW, slower but complete removal of I- from WTP off-gas simulants, preferred removal of I- over Br- and Cl-, and it demonstrated ability to remove IO3- through reduction to I-.
RESUMO
To prevent the release of radioiodine during the reprocessing of used nuclear fuel or in the management of other wastes, many technologies have been developed for iodine capture. The capture is only part of the challenge as a durable waste form is required to ensure safe disposal of the radioiodine. This work presents the first durability studies in dilute conditions of two AgI-containing waste forms: hot-isostatically pressed silver mordenite (AgZ) and spark plasma sintered silver-functionalized silica aerogel (SFA) iodine waste forms (IWF). Using the single-pass flow-through (SPFT) test method, the dissolution rates respective to Si, Al, Ag and I were measured for variants of the IWFs. By combining solution and solid analysis information on the corrosion mechanism neutral-to-alkaline conditions was elucidated. The AgZ samples were observed to have corrosion preferentially occur at secondary phases with higher Al and alkali content. These phases contained a lower proportion of I compared with the matrix. The SFA samples experienced a higher extent of corrosion at Si-rich particles, but an increased addition of Si to the waste led to an improvement in corrosion resistance. The dissolution rates for the IWF types are of similar magnitude to other Si-based waste form materials measured using SPFT.
RESUMO
Despite the numerous studies on changes within the reservoir following CO2 injection and the effects of CO2 release into overlying aquifers, little or no literature is available on the effect of CO2 release on rock between the storage reservoirs and subsurface. This is important, because the interactions that occur in this zone between the CO2 storage reservoir and the subsurface may have a significant impact on risk analysis for CO2 storage projects. To address this knowledge gap, relevant rock materials, temperatures and pressures were used to study mineralogical and elemental changes in this intermediate zone. After rocks reacted with CO2-acidified 0.01â¯M NaCl, liquid analysis showed an increase of major elements (e.g., Ca and Mg) and variable concentrations of potential contaminants (e.g., Sr and Ba); lower aqueous concentrations of these elements were observed in N2 control experiments, likely due to differences in pH between the CO2 and N2 experiments. In experiments with As/Cd and/or organic spikes, representing potential contaminants in the CO2 plume originating in the storage reservoir, most or all of these contaminants were removed from the aqueous phase. SEM and Mössbauer spectroscopy results showed the formation of new minerals and Fe oxides in some CO2-reacted samples, indicating potential for contaminant removal through mineral incorporation or adsorption onto Fe oxides. These experiments show the interactions between the CO2-laden plume and the rock between storage reservoirs and overlying aquifers have the potential to affect the level of risk to overlying groundwater, and should be considered during site selection and risk evaluation.
Assuntos
Dióxido de Carbono/química , Sequestro de Carbono , Carbonatos/química , Minerais/química , Adsorção , Água Subterrânea/químicaRESUMO
A cementitious waste form, Cast Stone, is a possible candidate technology for the immobilization of low activity nuclear waste (LAW) at the Hanford site. This work focuses on the addition of getter materials to Cast Stone that can sequester Tc from the LAW, and in turn, lower Tc release from the Cast Stone. Two getters which produce different products upon sequestering Tc from LAW were tested: Sn(II) apatite (Sn-A) that removes Tc as a Tc(IV)-oxide and potassium metal sulfide (KMS-2) that removes Tc as a Tc(IV)-sulfide species, allowing for a comparison of stability of the form of Tc upon entering the waste form. The Cast Stone with KMS-2 getter had the best performance with addition equivalent to â¼0.08wt% of the total waste form mass. The observed diffusion (Dobs) of Tc decreased from 4.6±0.2×10-12cm2/s for Cast Stone that did not contain a getter to 5.4±0.4×10-13cm2/s for KMS-2 containing Cast Stone. It was found that Tc-sulfide species are more stable against re-oxidation within getter containing Cast Stone compared with Tc-oxide and is the origin of the decrease in Tc Dobs when using the KMS-2.