1.
Nanotechnology ; 32(14): 145703, 2021 Apr 02.
Artigo em Inglês | MEDLINE | ID: mdl-33333498

RESUMO

This study reports on the synthesis of highly oriented chromium triiodide (CrI3) magnetic inclusions inside nano/microfibres with a polyethylene oxide matrix, prepared by the electrospinning technique. The structural, microstructural and spectroscopic analysis shows uniformly dispersed CrI3 nanosized inclusions inside the fibres, presenting a C2/m monoclinic structure at room temperature, where their c-axis is perpendicular to the fibre mat plane and the ab layers are in-plane. Analysis of the magnetic properties show that the samples have a ferromagnetic-paramagnetic phase transition at ∼55-56 K, lower than that of bulk CrI3. Noticeably, a field-driven metamagnetic transition is observed below ∼45 K, from M versus H curves, when the applied magnetic field is perpendicular to the fibre mat plane, while it is strongly reduced when the field is in-plane. This anisotropic behaviour is attributed to the field-induced changes from antiferromagnetic to ferromagnetic interlayer magnetic moment alignment along the CrI3 c-axis stacked layers. These CrI3 electrospun fibres then show an efficient cost-effective route to synthesize magnetic composite fibres with highly oriented van der Walls inclusions, for spintronic applications, taking advantage of their anisotropic 2D layered materials properties.

2.
ACS Appl Mater Interfaces ; 16(7): 8655-8667, 2024 Feb 21.
Artigo em Inglês | MEDLINE | ID: mdl-38301168

RESUMO

Currently, magnetocaloric refrigeration technologies are emerging as ecofriendly and more energy-efficient alternatives to conventional expansion-compression systems. However, major challenges remain. A particular concern is the mechanical properties of magnetocaloric materials, namely, their fatigue under cycling and difficulty in processing and shaping. Nevertheless, in the past few years, using multistimuli thermodynamic cycles with multicaloric refrigerants has led to higher heat-pumping efficiencies. To address simultaneously the challenges and develop a multicaloric material, in this work, we have prepared magnetocaloric-based flexible composite mats composed of micrometric electroactive (EA) polyvinylidene fluoride (PVDF) fibers with embedded magnetocaloric/strictive La(Fe,Si)13 particles by the simple and cost-effective electrospinning technique. The composite's structural characterization, using X-ray diffraction (XRD) analysis, Fourier transform infrared (FTIR) spectroscopy, and measurements of the local-scale piezoresponse, revealed a cubic NaZn13-type structure of the La(Fe,Si)13 phase and the formation of the dominant polar ß-phase of the PVDF polymer. The PVDF-La(Fe,Si)13 composite showed an enhancement of the longitudinal piezoelectric coefficient (effective d33) (-11.01 pm/V) compared with the single PVDF fiber matrix (-9.36 pm/V). The main magnetic properties of La(Fe,Si)13 powder were retained in the PVDF-La(Fe,Si)13 composite, including its giant magnetocaloric effect. By retaining the unique magnetic properties of La(Fe,Si)13 embedded in the electroactive piezoelectric polymer fiber mats, we have designed a flexible, easily shapeable, and multifunctional composite enabling its potential application in multicaloric heat-pumping devices and other sensing and actuating devices.

3.
Materials (Basel) ; 15(24)2022 Dec 12.
Artigo em Inglês | MEDLINE | ID: mdl-36556665

RESUMO

Prussian Blue (PB) thin films were prepared by DC chronoamperometry (CHA), symmetric pulse, and non-symmetric pulse electrodeposition techniques. The formation of PB was confirmed by infrared spectroscopy (FTIR), energy-dispersive X-ray spectroscopy (EDX) and UV-Vis transmission measurements. X-ray diffraction (XRD) shows the stabilization of the insoluble form of PB. From scanning electron microscopy (SEM) studies, an increase in porosity is obtained for the shorter pulse widths, which tends to improve the total charge exchange and electrochemical stability of the films. While the film prepared by CHA suffered a degradation of 82% after 260 cycles, the degradation reduced to 24% and 34% for the samples prepared by the symmetric and non-symmetric pulse methods, respectively. Additionally, in the non-symmetric pulse film, the improvement in the charge exchange reached ~522% after 260 cycles. According to this study, the deposition time distribution affects the physical/chemical properties of PB films. These results then render pulse electrodeposition methods especially suitable to produce high-quality thin films for electrochemical devices, based on PB.