Surfactant-Assisted Regulation of WS2/Tourmaline Microstructures for Excellent Photocatalytic Performance.

The controllable electrical and optical properties of two-dimensional tungsten disulfide (WS2) attracted much attention in photocatalysis, but commercial development has been severely restricted by their restacking properties. Surfactant-assisted synthesis techniques can be considered as an effective option to break this bottleneck. In this work, the effect of surfactants including sodium dodecylbenzene sulfonate (SDBS), hexadecyltrimethylammonium bromide (CTAB), and polyvinylpyrrolidone (PVP) on the microstructure of WS2/tourmaline composites prepared by coupled hydrothermal and calcination methods was explored. The WS2 nanosheets were uniformly deposited on the tourmaline surface with the assistance of 1.0 mmol/L SDBS. Meanwhile, WS2/Tour-SDBS exhibited the highest rhodamine B (RhB) degradation activity, which was 1.8 and 2.3 times higher than that of photocatalysts prepared with CTAB and PVP under the same conditions, respectively. This study provides a new tactic for the fabrication of high-performance WS2-based composites.

A novel highly dispersed calcium silicate hydrate nanosheets for efficient high-concentration Cu2+ adsorption.

Currently, the low cost and effective purification toward heavy metal ions in wastewater has garnered global attention. Herein, we used hydrothermal method to prepare highly dispersed calcium silicate hydrate in fluorite tailings. And the stacking thickness of calcium silicate hydrate layered morphology was less than 5 nm. For high concentration Cu2+ purification investigation in wastewater, we found that the equilibrium adsorption capacity reached 797.92 mg/g via the CSH with 3:2 Ca/Si molar ratio, be 1.43-21.8 times than that of reported data. Therein, the metal-metal exchange and deposition are the primary pathways for Cu2+ adsorption, and electrostatic attraction is the secondary pathway. And the relative ∼100 % removal rate of high-concentration Ni2+ and Cr3+ ions were confirmed via CSH prepared from different tailings. This method offers a cost-effective way to utilize tailings for preparing highly efficient adsorbents toward HMIs removal in wastewater.

Cost-Effective Fabrication of Modified Palygorskite-Reinforced Rigid Polyurethane Foam Nanocomposites.

Integration of nanoclay minerals into rigid polyurethane foams (RPUFs) is a cost-effective solution to enhance foam's performance via environmental protection technology. In this work, palygorskite/RPUFs nanocomposites (Pal/RPUFNs) with excellent mechanical properties and thermal stability were prepared via a one-step method, using 4,4'-diphenylmethane diisocyanate and polyether polyol as the starting materials, coupled with Pal modified by silane coupling agent KH570. The effects of the modified Pal on the mechanics, morphology, and thermal properties of the nanocomposites were studied systematically. When the content of the modified Pal was 8 wt% of polyether polyol, the elastic modulus and compressive strength of the Pal/RPUFNs were increased by ca. 131% and 97%, respectively. The scanning electron microscopy images indicated that the addition of the modified Pal significantly decreased the cell diameter of the Pal/RPUFNs. The results of thermogravimetric and derivative thermogravimetry analyses revealed that the addition of the modified Pal increased the thermal weight loss central temperature of the Pal/RPUFNs, showing better thermal stability in comparison with the pure RPUFs. A self-made evaluation device was used to estimate the thermal insulation ability of the Pal/RPUFNs. It was found that the small cell size and uniform cellular structure were keys to improving the thermal insulation performance of the RPUFs. The prepared Pal/RPUFNs are expected to have great potential in the field of building insulation.