Novel hydroxyl-terminated hyperbranched polymer as a synergistic modifier with tannin for preparation of casein-based films with superior performance.

A hyperbranched poly (titanium oxide) (HBPTi) with hydroxyl terminal groups was synthesized via polycondensation reaction as a synergistic modifier with tannin to promote performance of casein-based composite film. The synergistic effects of HBPTis, acquiring different hyperbranched structures, with tannin on the microstructure, mechanical characteristics, barrier against water vapor, and thermal stability of casein-based film were investigated in this work. The tensile strength of the composite films increased from 7.6 MPa to 22.1 MPa, which accounts for 190.79 % increase after the addition of HBPTi compared to casein-tannin films modified with glycerol. The casein-tannin films with the help of HBPTi presented excellent water vapor permeation, thermal stability, and showed nearly 100 % UV absorption in the range 200-400 nm. Additionally, the microstructure of HBPTi modified casein-tannin films tend to be more compact due to the promoted interaction of casein-tannin composite aided by covalent bonding and/or other types of bonding between casein, tannin and HBPTi. Therefore, associative modification using such hyperbranched polymers and tannins provides extendable application value for casein-based films especially as food packaging materials and for other fields as well.

Investigation of Potential Use of Soybean Protein Isolate-Chinese Bayberry Tannin Extract Cross-Linked Films in Packaging Applications.

The possibility of using commercial bayberry tannin (BT) from a Chinese source as a cross-linker and functional additive to develop soybean protein isolate (SPI)-based films was explored in this study by using the solvent casting method. In particular, the impacts of BT loading on the tensile strength, microstructure, thermal stability, water resistance and antioxidant capacity were fully investigated. The results reveal that SPI incorporated with BT yielded a phenolic-protein hybrid whose relevant films exhibited an improvement in tensile strength of around two times greater compared with native SPI as a result of the formed interactions and covalent cross-links, which could be proven using FTIR spectroscopy. The introduction of BT also led to the compact microstructure of SPI-BT films and enhanced the thermal stability, while the water vapor permeability was reduced compared with the control SPI film, especially at high loading content of tannin. Additionally, the use of BT significantly promoted the antioxidant capacity of the SPI-based films according to DPPH radical scavenging assay results. On this basis, Chinese bayberry tannin is considered a promising natural cross-linker and multifunctional additive that can be dedicated to developing protein-derived films with antioxidant activity for food packaging applications.