The exploitation of shape-stabilized phase change materials with high thermal conductivity and energy storage capacity is an effective strategy for improving energy efficiency. In this work, sunflower stem carbon/polyethylene glycol (SS-PEG) and sunflower receptacle carbon/polyethylene glycol (SR-PEG) shape-stabilized phase change materials, utilizing sunflower stem and receptacle biomass carbon with high specific surface area and pore volume obtained by carbonization as frameworks and polyethylene glycol as an energy storage material, were prepared by the vacuum impregnation method. The ability to load polyethylene glycol into the pore structure of carbon materials in different sunflower parts was mainly investigated, and the micro-morphology, compositional structure and thermal properties were characterized and analyzed using SEM, IR spectroscopy, XRD, DSC and TG techniques. The results showed that the carbonized sunflower stems maintained the sieve pore structure, and the carbonized sunflower receptacle was a macroporous structure containing a large number of three-dimensional interconnections. At the same time, the interaction between polyethylene glycol and each carbon material occurred through physisorption. The melting enthalpies of SS-PEG and SR-PEG shape-stabilized phase change materials were 153.4 J g-1 and 171.5 J g-1, respectively, and the loading rates reached 81.9% and 91.5%, with initial thermal decomposition temperatures (T 5%) of 344 °C and 368 °C.
RESUMO
To alleviate the increasing energy crisis and achieve energy saving and consumption reduction in building materials, preparing shape-stabilized phase-change materials using bio-porous carbon materials from renewable organic waste to building envelope materials is an effective strategy. In this work, pine cone porous biomass carbon (PCC) was prepared via a chemical activation method using renewable biomaterial pine cone as a precursor and potassium hydroxide (KOH) as an activator. Polyethylene glycol (PEG) and octadecane (OD) were loaded into PCC using the vacuum impregnation method to prepare polyethylene glycol/pine cone porous biomass carbon (PEG/PCC) and octadecane/pine cone porous biomass carbon (OD/PCC) shape-stabilized phase-change materials. PCCs with a high specific surface area and pore volume were obtained by adjusting the calcination temperature and amount of KOH, which was shown as a caterpillar-like and block morphology. The shape-stabilized PEG/PCC and OD/PCC composites showed high phase-change enthalpies of 144.3 J/g and 162.3 J/g, and the solar-thermal energy conversion efficiencies of the PEG/PCC and OD/PCC reached 79.9% and 84.8%, respectively. The effects of the contents of PEG/PCC and OD/PCC on the temperature-controlling capability of rigid polyurethane foam composites were further investigated. The results showed that the temperature-regulating and temperature-controlling capabilities of the energy-storing rigid polyurethane foam composites were gradually enhanced with an increase in the phase-change material content, and there was a significant thermostatic plateau in energy absorption at 25 °C and energy release at 10 °C, which decreased the energy consumption.