High-Performance Porous Organic Polymers for Environmental Remediation of Toxic Gases.

Sulfur dioxide (SO2) is a harmful acidic gas generated from power plants and fossil fuel combustion and represents a significant health risk and threat to the environment. Benzimidazole-linked polymers (BILPs) have emerged as a promising class of porous solid adsorbents for toxic gases because of their chemical and thermal stability as well as the chemical nature of the imidazole moiety. The performance of BILPs in SO2 capture was examined by synergistic experimental and theoretical studies. BILPs exhibit a significantly high SO2 uptake of up to 8.5 mmol g-1 at 298 K and 1.0 bar. The density functional theory (DFT) calculations predict that this high SO2 uptake is due to the dipole-dipole interactions between SO2 and the functionalized polymer frames through O2S(δ+)···N(δ-)-imine and O═S═O(δ-)···H(δ+)-aryl and intermolecular attraction between SO2 molecules (O═S═O(δ-)···S(δ+)O2). Moderate isosteric heats of adsorption (Qst ≈ 38 kJ mol-1) obtained from experimental SO2 uptake studies are well supported by the DFT calculations (≈40 kJ mol-1), which suggests physisorption processes enabling rapid adsorbent regeneration for reuse. Repeated adsorption experiments with almost identical SO2 uptake confirm the easy regeneration and robustness of BILPs. Moreover, BILPs possess very high SO2 adsorption selectivity at low concentration over carbon dioxide (CO2), methane (CH4), and nitrogen (N2): SO2/CO2, 19-24; SO2/CH4, 118-113; SO2/N2, 600-674. This study highlights the potential of BILPs in the desulfurization of flue gas or other gas mixtures through capturing trace levels of SO2.

Templated Synthesis of 2D Polyimide Covalent Organic Framework for Rechargeable Sodium-Ion Batteries.

Covalent organic frameworks (COFs) hold great promise for electrochemical energy storage because of their high surface area, readily accessible redox-active sites, and environment-friendly chemical composition. In this study, the synthesis of a redox-active pyrene-containing polyimide COF (PICOF-1) by linker exchange using an imine-linked COF as a template is reported and its performance in sodium-ion batteries (SIBs) is demonstrated. The reported synthetic route based on linker exchange mitigates the challenges typically encountered with crystallizing chemically stable polyimide COFs from typical condensation reactions; thus, facilitating their rapid synthesis and purification. Using this approach, PICOF-1 exhibits high crystallinity with very low refinement parameters RP and RWP of 0.415% and 0.326%, respectively. PICOF-1 has a high Brunauer-Emmette-Teller (BET) surface area of 924 m2  g-1 and well-defined one-dimentional (1D) channels of 2.46 × 1.90 nm, which enable fast ion transport and charge transfer, reaching a capacity at 0.1 C of almost nearly as its theoretical capacity and maintaining 99% Coulombic efficiency over 175 cycles at 0.3 C. The study demonstrates that imine-linked COFs are effective templates for integrating carbonyl-rich polyimide moieties into high-surface COFs to advance electrochemical energy storage applications.

Multifunctional Electrocatalytic Cathodes Derived from Metal-Organic Frameworks for Advanced Lithium-Sulfur Batteries.

The rechargeable lithium-sulfur (Li-S) battery is a promising candidate for the next generation of energy storage technology, owing to the high theoretical capacity, high specific energy density, and low cost of electrode materials. The main drawbacks in the development of long-life Li-S batteries are capacity fading and the sluggish kinetics at the cathode caused by the polysulfides shuttle. These limitations are addressed through the design of novel nanocages containing cobalt phosphide (CoP) nanoparticles embedded in highly porous nitrogen-doped carbon (CoP-N-GC) by thermal annealing of ZIF-67 in a reductive atmosphere followed by a phosphidation step using sodium hypophosphite. The CoP nanoparticles, with large surface area and uniform homogeneous distribution within the N-doped nanocage graphitic carbon, act as electrocatalysts to suppress the shuttle of soluble polysulfides through strong chemical interactions and catalyze the sulfur redox. As a result, the S@CoP-N-GC electrode delivers an extremely high specific capacity of 1410 mA h g-1 at 0.1 C (1 C=1675 mA g-1 ) with an excellent coulombic efficiency of 99.7 %. Moreover, capacity retention from 864 to 678 mA h g-1 is obtained after 460 cycles with a very low decay rate of 0.046 % per cycle at 0.5 C. Therefore, the combination of the CoP catalyst and polar conductive porous carbon effectively stabilizes the sulfur cathode, enhancing the electrochemical performance and stability of the battery.

Effect of acid-catalyzed formation rates of benzimidazole-linked polymers on porosity and selective CO2 capture from gas mixtures.

Benzimidazole-linked polymers (BILPs) are emerging candidates for gas storage and separation applications; however, their current synthetic methods offer limited control over textural properties which are vital for their multifaceted use. In this study, we investigate the impact of acid-catalyzed formation rates of the imidazole units on the porosity levels of BILPs and subsequent effects on CO2 and CH4 binding affinities and selective uptake of CO2 over CH4 and N2. Treatment of 3,3'-Diaminobenzidine tetrahydrochloride hydrate with 1,2,4,5-tetrakis(4-formylphenyl)benzene and 1,3,5-(4-formylphenyl)-benzene in anhydrous DMF afforded porous BILP-15 (448 m(2) g(-1)) and BILP-16 (435 m(2) g(-1)), respectively. Alternatively, the same polymers were prepared from the neutral 3,3'-Diaminobenzidine and catalytic amounts of aqueous HCl. The resulting polymers denoted BILP-15(AC) and BILP-16(AC) exhibited optimal surface areas; 862 m(2) g(-1) and 643 m(2) g(-1), respectively, only when 2 equiv of HCl (0.22 M) was used. In contrast, the CO2 binding affinity (Qst) dropped from 33.0 to 28.9 kJ mol(-1) for BILP-15 and from 32.0 to 31.6 kJ mol(-1) for BILP-16. According to initial slope calculations at 273 K/298 K, a notable change in CO2/N2 selectivity was observed for BILP-15(AC) (61/50) compared to BILP-15 (83/63). Similarly, ideal adsorbed solution theory (IAST) calculations also show the higher specific surface area of BILP-15(AC) and BILP-16(AC) compromises their CO2/N2 selectivity.

High Sodium Ion Storage by Multifunctional Covalent Organic Frameworks for Sustainable Sodium Batteries.

Rechargeable sodium batteries hold great promise for circumventing the increasing demand for lithium-ion batteries (LIBs) and the limited supply of lithium. However, efficient sodium ion storage remains a great impediment in this field. In this study, we report the designed synthesis of a multifunctional two-dimensional covalent organic framework featuring hexaazatrinaphthalene cores linked by imidazole moieties and demonstrate its effective performance in sodium ion storage. Benzimidazole-linked covalent organic framework (BCOF-1) was synthesized by a condensation reaction between hexaazatrinaphthalenehexamine (HATNHA) and terephthalaldehyde (TA) and exhibited a high theoretical specific capacity of 392 mA h g-1. BCOF-1 crystallizes, forming eclipsed AA stacking and mesoporous hexagonal one-dimensional channels with high surface area (840 m2 g-1), facilitating fast ionic mobility and charge transfer and enabling high-rate capability at high current rates. BCOF-1 exhibits pseudocapacitive-like behavior with a high specific capacity of 387 mA h g-1, an energy density of 302 W h kg-1 at 0.1 C, and a power density of 682 W kg-1 at 5 C. Our results demonstrate that redox-active COFs have the desired structural and electronic merits to advance the use of organic electrodes in sodium-ion storage toward sustainable and efficient batteries.

Selective Reduction of Multivariate Metal-Organic Frameworks for Advanced Electrocatalytic Cathodes in High Areal Capacity and Long-Life Lithium-Sulfur Batteries.

Lithium-sulfur batteries hold great promise as next-generation high-energy-density batteries. However, their performance has been limited by the low cycling stability and sulfur utilization. Herein, we demonstrate that a selective reduction of the multivariate metal-organic framework, MTV-MOF-74 (Co, Ni, Fe), transforms the framework into a porous carbon decorated with bimetallic CoNi alloy and Fe3O4 nanoparticles capable of entrapping soluble lithium polysulfides while synergistically facilitating their rapid conversion into Li2S. Electrochemical studies on coin cells containing 89 wt % sulfur loading revealed a reversible capacity of 1439.8 mA h g-1 at 0.05 C and prolonged cycling stability for 1000 cycles at 1 C/1060.2 mA h g-1 with a decay rate of 0.018% per cycle. At a high areal sulfur loading of 6.9 mg cm-2 and lean electrolyte/sulfur ratio (4.5 µL:1.0 mg), the battery based on the 89S@CoNiFe3O4/PC cathode provides a high areal capacity of 6.7 mA h cm-2. The battery exhibits an outstanding power density of 849 W kg-1 at 5 C and delivers a specific energy of 216 W h kg-1 at 2 C, corresponding to a specific power of 433 W kg-1. Density functional theory shows that the observed results are due to the strong interaction between the CoNi alloy and Fe3O4, facilitated by charge transfer between the polysulfides and the substrate.

A 2D mesoporous imine-linked covalent organic framework for high pressure gas storage applications.

Hole-some mixture: A 2D mesoporous covalent organic framework (see figure) featuring expanded pyrene cores and linked by imine linkages has a high surface area (SA(BET) = 2723 m(2) g(-1)) and exhibits significant gas storage capacities under high pressure, which make this class of material very promising for gas storage applications.

Postsynthetic Modification of Core-Shell Magnetic Covalent Organic Frameworks for the Selective Removal of Mercury.

Core-shell magnetic covalent organic framework (COF) materials were prepared, followed by shell material functionalization with different organic ligands, including thiosemicarbazide, through a postsynthetic modification approach. The structures of the prepared samples were characterized with various techniques, including powder X-ray diffraction (PXRD), Brunauer-Emmett-Teller (BET) method, thermogravimetric analysis (TGA), photoinduced force microscopy (PiFM), transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), and solid 13C NMR. PXRD and BET studies revealed that the crystalline and porous nature of the functionalized COFs was well maintained after three steps of postsynthetic modification. On the other hand, solid 13C NMR, TGA, and PiFM analyses confirmed the successful functionalization of COF materials with good covalent linkage connectivity. The use of the resulting functionalized magnetic COF for selective and ultrafast adsorption of Hg(II) has been investigated. The observations displayed rapid kinetics with adsorption dynamics conforming to the quasi-second-order kinetic model and the Langmuir adsorption model. Furthermore, this prepared crystalline magnetic material demonstrated a high Langmuir Hg(II) uptake capacity, reaching equilibrium in only 5 min. Thermodynamic calculations proved that the adsorption process is endothermic and spontaneous.

Synthesis, Characterization, and Environmental Applications of Novel Per-Fluorinated Organic Polymers with Azo- and Azomethine-Based Linkers via Nucleophilic Aromatic Substitution.

This study reports on the synthesis and characterization of novel perfluorinated organic polymers with azo- and azomethine-based linkers using nucleophilic aromatic substitution. The polymers were synthesized via the incorporation of decafluorobiphenyl and hexafluorobenzene linkers with diphenols in the basic medium. The variation in the linkers allowed the synthesis of polymers with different fluorine and nitrogen contents. The rich fluorine polymers were slightly soluble in THF and have shown molecular weights ranging from 4886 to 11,948 g/mol. All polymers exhibit thermal stability in the range of 350-500 °C, which can be attributed to their structural geometry, elemental contents, branching, and cross-linking. For instance, the cross-linked polymers with high nitrogen content, DAB-Z-1h and DAB-Z-1O, are more stable than azomethine-based polymers. The cross-linking was characterized by porosity measurements. The azo-based polymer exhibited the highest surface area of 770 m2/g with a pore volume of 0.35 cm3/g, while the open-chain azomethine-based polymer revealed the lowest surface area of 285 m2/g with a pore volume of 0.0872 cm3/g. Porous structures with varied hydrophobicities were investigated as adsorbents for separating water-benzene and water-phenol mixtures and selectively binding methane/carbon dioxide gases from the air. The most hydrophobic polymers containing the decafluorbiphenyl linker were suitable for benzene separation, while the best methane uptake values were 6.14 and 3.46 mg/g for DAB-Z-1O and DAB-A-1O, respectively. On the other hand, DAB-Z-1h, with the highest surface area and being rich in nitrogen sites, has recorded the highest CO2 uptake at 298 K (17.25 mg/g).

Heteroatom-Doped Porous Carbons as Effective Adsorbers for Toxic Industrial Gasses.

Ammonia (NH3), often stored in large quantities before being used in the production of fertilizer, and sulfur dioxide (SO2), a byproduct of fossil fuel consumption, particularly the burning of coal, are highly toxic and corrosive gases that pose a significant danger to humans if accidentally released. Therefore, developing advanced materials to enable their effective capture and safe storage is highly desired. Herein, advanced benzimidazole-derived carbons (BIDCs) with an exceptional capacity for NH3 and SO2 have been designed and tested. These heteroatom-doped porous carbon adsorbents were synthesized by thermolysis of imidazolate-potassium salts affording high surface area and controlled heteroatom content to optimize for rapid NH3 and SO2 gas uptake and release under practical conditions. According to gas uptake measurements, these nitrogen-doped carbons exhibit exceptional gas adsorption capacity, with BIDC-3-800 adsorbing 21.42 mmol/g SO2 at 298 K and 1 bar, exceeding most reported porous materials and BIDC-2-700 adsorbing 14.26 mmol/g NH3 under the same conditions. The NH3 uptake of BIDC-2-700 surpassed reported activated carbons and is among the best adsorbents including metal organic frameworks (MOFs). Our synthetic method allows for control over both textural and chemical properties of the carbon and enables heteroatom functionality to be incorporated directly into the carbon framework without the need for postsynthetic modification. These materials were also tested for recyclability; all adsorbents showed almost complete retention of their initial gas uptake capacity during recyclability studies and maintained their structural integrity and their previous adsorption capacity of both NH3 and SO2, highlighting their potential for practical application.

Exceptional Sodium-Ion Storage by an Aza-Covalent Organic Framework for High Energy and Power Density Sodium-Ion Batteries.

Redox-active covalent organic frameworks (COFs) are a new class of material with the potential to transform electrochemical energy storage due to the well-defined porosity and readily accessible redox-active sites of COFs. However, combining both high specific capacity and energy density in COF-based batteries remains a considerable challenge. Herein, we demonstrate the exceptional performance of Aza-COF in rechargeable sodium-ion batteries (SIBs). Aza-COF is a microporous 2D COF synthesized from hexaketocyclohexane and 1,2,4,5-benzenetetramine by a condensation reaction, which affords phenazine-decorated channels and a theoretical specific capacity of 603 mA h g-1. The Aza-COF-based electrode exhibits an exceptional average specific capacity (550 mA h g-1), energy density (492 W h kg-1) at 0.1 C, and power density (1182 W kg-1) at 40 C. The high capacity and energy density are attributed to swift surface-controlled redox processes and rapid sodium-ion diffusion inside the porous electrode. Rate capability studies showed that the battery also performs well at high current rates: 1 C (363 mA h g-1), 5 C (232 mA h g-1), 10 C (161 mA h g-1), and 20 C (103 mA h g-1). In addition, the long-term cycling stability test revealed very good capacity retention (87% at 5 C) and Coulombic efficiencies near unity over 500 cycles.

Heterogeneous catalysis by ultra-small bimetallic nanoparticles surpassing homogeneous catalysis for carbon-carbon bond forming reactions.

Palladium catalyzed cross-coupling reactions represent a significant advancement in contemporary organic synthesis as these reactions are of strategic importance in the area of pharmaceutical drug discovery and development. Supported palladium-based catalysts are highly sought-after in carbon-carbon bond forming catalytic processes to ensure catalyst recovery and reuse while preventing product contamination. This paper reports the development of heterogeneous Pd-based bimetallic catalysts supported on fumed silica that have high activity and selectivity matching those of homogeneous catalysts, eliminating the catalyst's leaching and sintering and allowing efficient recycling of the catalysts. Palladium and base metal (Cu, Ni or Co) contents of less than 1.0 wt% loading are deposited on a mesoporous fumed silica support (surface area SABET = 350 m2 g-1) using strong electrostatic adsorption (SEA) yielding homogeneously alloyed nanoparticles with an average size of 1.3 nm. All bimetallic catalysts were found to be highly active toward Suzuki cross-coupling (SCC) reactions with superior activity and stability for the CuPd/SiO2 catalyst. A low CuPd/SiO2 loading (Pd: 0.3 mol%) completes the conversion of bromobenzene and phenylboronic acid to biphenyl in 30 minutes under ambient conditions in water/ethanol solvent. In contrast, monometallic Pd/SiO2 (Pd: 0.3 mol%) completes the same reaction in three hours under the same conditions. The combination of Pd with the base metals helps in retaining the Pd0 status by charge donation from the base metals to Pd, thus lowering the activation energy of the aryl halide oxidative addition step. Along with its exceptional activity, CuPd/SiO2 exhibits excellent recycling performance with a turnover frequency (TOF) of 280 000 h-1 under microwave reaction conditions at 60 °C. Our study demonstrates that SEA is an excellent synthetic strategy for depositing ultra-small Pd-based bimetallic nanoparticles on porous silica for SCC. This avenue not only provides highly active and sintering-resistant catalysts but also significantly lowers Pd contents in the catalysts without compromising catalytic activity, making the catalysts very practical for large-scale applications.

Redox-Active Porous Organic Polymers as Novel Electrode Materials for Green Rechargeable Sodium-Ion Batteries.

The use of redox-active organic materials in rechargeable batteries has the potential to transform the field by enabling lightweight, flexible, green batteries while replacing lithium with sodium would mitigate the limited supplies and high cost of lithium. Herein, we report the first use of highly porous azo-linked polymers (ALPs) as a new redox-active electrode material for rechargeable sodium-ion batteries. ALPs are highly cross-linked polymers and therefore eliminate the solubility issue of organic electrodes in common electrolytes, which is prominent in small organic molecules and leads to fast capacity fading. Moreover, the high surface area coupled with the π-conjugated microporous nature of ALPs facilitates electrolyte adsorption in the pores and assists in fast ionic transport and charge transfer rates. An average specific capacity of 170 mA h g-1 at 0.3 C rate was attained while maintaining 96% Coulombic efficiency over 150 charge/discharge cycles.

Rapid transformation of heterocyclic building blocks into nanoporous carbons for high-performance supercapacitors.

The ever-increasing global energy consumption necessitates the development of efficient energy conversion and storage devices. Nitrogen-doped porous carbons as electrode materials for supercapacitors feature superior electrochemical performances compared to pristine activated carbons. Herein, a facile synthetic strategy including solid-state mixing of benzimidazole as an inexpensive single-source precursor of nitrogen and carbon and zinc chloride as a high temperature solvent/activator followed by pyrolysis of the mixture (T = 700-1000 °C under Ar) is introduced. The addition of ZnCl2 prevents early sublimation of benzimidazole and promotes carbonization and pore generation. The sample obtained under the optimal carbonization temperature of 900 °C and ZnCl2/benzimidazole weight ratio of 2/1 (ZBIDC-2-900) features a moderate specific surface area of 855 m2 g-1, high N-doping level (10 wt%), and a wide micropore size distribution (∼1 nm). ZBIDC-2-900 as a supercapacitor electrode exhibits a large gravimetric capacitance of 332 F g-1 (at 1 A g-1 in 1 M H2SO4) thanks to the cooperative advantages of the electrochemical activity of the nitrogen functional groups and the accessible porosity. The excellent capacitance performance coupled with robust cyclic stability, high yield and straightforward synthesis of the proposed carbons holds great potential for large-scale energy storage applications.

Nitrogen-Rich Porous Polymers for Carbon Dioxide and Iodine Sequestration for Environmental Remediation.

The use of fossil fuels for energy production is accompanied by carbon dioxide release into the environment causing catastrophic climate changes. Meanwhile, replacing fossil fuels with carbon-free nuclear energy has the potential to release radioactive iodine during nuclear waste processing and in case of a nuclear accident. Therefore, developing efficient adsorbents for carbon dioxide and iodine capture is of great importance. Two nitrogen-rich porous polymers (NRPPs) derived from 4-bis-(2,4-diamino-1,3,5-triazine)-benzene building block were prepared and tested for use in CO2 and I2 capture. Copolymerization of 1,4-bis-(2,4-diamino-1,3,5-triazine)-benzene with terephthalaldehyde and 1,3,5-tris(4-formylphenyl)benzene in dimethyl sulfoxide at 180 °C afforded highly porous NRPP-1 (SABET = 1579 m2 g-1) and NRPP-2 (SABET = 1028 m2 g-1), respectively. The combination of high nitrogen content, π-electron conjugated structure, and microporosity makes NRPPs very effective in CO2 uptake and I2 capture. NRPPs exhibit high CO2 uptakes (NRPP-1, 6.1 mmol g-1 and NRPP-2, 7.06 mmol g-1) at 273 K and 1.0 bar. The 7.06 mmol g-1 CO2 uptake by NRPP-2 is the second highest value reported to date for porous organic polymers. According to vapor iodine uptake studies, the polymers display high capacity and rapid reversible uptake release for I2 (NRPP-1, 192 wt % and NRPP-2, 222 wt %). Our studies show that the green nature (metal-free) of NRPPs and their effective capture of CO2 and I2 make this class of porous materials promising for environmental remediation.

Pyrene Bearing Azo-Functionalized Porous Nanofibers for CO2 Separation and Toxic Metal Cation Sensing.

A novel luminescent azo-linked polymer (ALP) has been constructed from 1,3,6,8-tetra(4-aminophenyl)pyrene using a copper(I)-catalyzed oxidative homocoupling reaction. The polymer displays high porosity with a Brunauer-Emmett-Teller surface area of 1259 m2 g-1 and narrow pore size distribution (1.06 nm) and is able to take up a significant amount of CO2 (2.89 mmol g-1) at 298 K and 1.00 bar with a high isosteric heat of adsorption of 27.5 kJ mol-1. Selectivity studies applying the ideal adsorbed solution theory revealed that the novel polymer has moderately good selectivities for CO2/N2 (55.1) and CO2/CH4 (10.9). Furthermore, the ALP shows fluorescence quenching in the presence of Hg2+, Pb2+, Tl+, and Al3+ ions. Compared with these ions, the ALP showed no sensitivity to light metal ions such as Na+, K+, and Ca2+ in ethanol-water solution, clearly indicating the high selectivity of the ALP toward heavy metal ions. The exceptional physiochemical stability, high porosity, and strong luminescence make this polymer an excellent candidate as a fluorescent chemical sensor for the detection of heavy metal ions.

Rapid Formation of Metal-Organic Frameworks (MOFs) Based Nanocomposites in Microdroplets and Their Applications for CO2 Photoreduction.

A copper-based metal-organic framework (MOF), [Cu3(TMA)2(H2O)3]n (also known as HKUST-1, where TMA stands for trimesic acid), and its TiO2 nanocomposites were directly synthesized in micrometer-sized droplets via a rapid aerosol route for the first time. The effects of synthesis temperature and precursor component ratio on the physicochemical properties of the materials were systematically investigated. Theoretical calculations on the mass and heat transfer within the microdroplets revealed that the fast solvent evaporation and high heat transfer rates are the major driving forces. The fast droplet shrinkage because of evaporation induces the drastic increase in the supersaturation ratio of the precursor, and subsequently promotes the rapid nucleation and crystal growth of the materials. The HKUST-1-based nanomaterials synthesized via the aerosol route demonstrated good crystallinity, large surface area, and great photostability, comparable with those fabricated by wet-chemistry methods. With TiO2 embedded in the HKUST-1 matrix, the surface area of the composite is largely maintained, which enables significant improvement in the CO2 photoreduction efficiency, as compared with pristine TiO2. In situ diffuse reflectance infrared Fourier transform spectroscopy analysis suggests that the performance enhancement was due to the stable and high-capacity reactant adsorption by HKUST-1. The current work shows great promise in the aerosol route's capability to address the mass and heat transfer issues of MOFs formation at the microscale level, and ability to synthesize a series of MOFs-based nanomaterials in a rapid and scalable manner for energy and environmental applications.

Palladium Nanoparticles Supported on Ce-Metal-Organic Framework for Efficient CO Oxidation and Low-Temperature CO2 Capture.

In this article, we report the lowest-temperature CO oxidation catalyst supported on metal-organic frameworks (MOFs). We have developed a facile, general, and effective approach based on microwave irradiation for the incorporation of Pd nanoparticle catalyst within Ce-MOF. The resulting Pd/Ce-MOF material is a unique catalyst that is capable of CO oxidation at modest temperatures and also of efficient uptake of the product CO2 gas at low temperatures. The observed catalytic activity of this material toward CO oxidation is significantly higher than those of other reported metal nanoparticles supported on MOFs. The high activity of the Pd/Ce-MOF catalyst is due to the presence of Ce(III) and Ce(IV) ions within the metal-organic framework support. The Pd nanoparticles supported on the Ce-MOF store oxygen in the form of a thin palladium oxide layer at the particle-support interface, in addition to the oxygen stored on the Ce(III)/Ce(IV) centers. Oxygen from these reservoirs can be released during CO oxidation at 373 K. At lower temperatures (273 K), the Pd/Ce-MOF has a significant CO2 uptake of 3.5 mmol/g.

Effective Approach for Increasing the Heteroatom Doping Levels of Porous Carbons for Superior CO2 Capture and Separation Performance.

Development of efficient sorbents for carbon dioxide (CO2) capture from flue gas or its removal from natural gas and landfill gas is very important for environmental protection. A new series of heteroatom-doped porous carbon was synthesized directly from pyrazole/KOH by thermolysis. The resulting pyrazole-derived carbons (PYDCs) are highly doped with nitrogen (14.9-15.5 wt %) as a result of the high nitrogen-to-carbon ratio in pyrazole (43 wt %) and also have a high oxygen content (16.4-18.4 wt %). PYDCs have a high surface area (SABET = 1266-2013 m2 g-1), high CO2 Qst (33.2-37.1 kJ mol-1), and a combination of mesoporous and microporous pores. PYDCs exhibit significantly high CO2 uptakes that reach 2.15 and 6.06 mmol g-1 at 0.15 and 1 bar, respectively, at 298 K. At 273 K, the CO2 uptake improves to 3.7 and 8.59 mmol g-1 at 0.15 and 1 bar, respectively. The reported porous carbons also show significantly high adsorption selectivity for CO2/N2 (128) and CO2/CH4 (13.4) according to ideal adsorbed solution theory calculations at 298 K. Gas breakthrough studies of CO2/N2 (10:90) at 298 K showed that PYDCs display excellent separation properties. The ability to tailor the physical properties of PYDCs as well as their chemical composition provides an effective strategy for designing efficient CO2 sorbents.

From Azo-Linked Polymers to Microporous Heteroatom-Doped Carbons: Tailored Chemical and Textural Properties for Gas Separation.

Heteroatom-doped porous carbons with ultrahigh microporosity were prepared from a nitrogen-rich azo-linked polymer (ALP-6) as a precursor for gas separation applications. Direct carbonization and chemical activation of ALP-6 with ZnCl2 and KOH were successfully applied to obtain three different classes of porous carbons (ALPDCs). Synthetic processes were conducted at relatively mild temperatures (500-800 °C),which resulted in retention of appreciable levels of nitrogen content (4.7-14.3 wt %). Additionally, oxygen functionalities were found to be present in chemically activated samples. The resultant porous carbons feature a diverse range of textural properties with a predominant microporous nature in common. The highest CO2 uptake value of 5.2 mmol g(-1) at 1 bar and 298 K in ALPDCK600 was originated from well-developed porosity and basic heteroatoms (N and O) on the pore walls. The highest heteroatom doping level (12 wt % nitrogen and 20 wt % oxygen) coupled with the high level of microporosity (84%) for ALPDCK500 led to notable CO2/N2 (62) and CO2/CH4 (11) selectivity values and a high CO2 uptake capacity (1.5 mmol g(-1), at 0.15 bar) at 298 K. This study illustrates the effective use of a single-source precursor with robust nitrogen bonds in combination with diverse carbonization methods to tailor the chemical and textural properties of heteroatom-doped porous carbons for CO2 capture and separation applications.