Three-dimensional (3D) organic-inorganic lead halide perovskites have emerged in the past few years as a promising material for low-cost, high-efficiency optoelectronic devices. Spurred by this recent interest, several subclasses of halide perovskites such as two-dimensional (2D) halide perovskites have begun to play a significant role in advancing the fundamental understanding of the structural, chemical, and physical properties of halide perovskites, which are technologically relevant. While the chemistry of these 2D materials is similar to that of the 3D halide perovskites, their layered structure with a hybrid organic-inorganic interface induces new emergent properties that can significantly or sometimes subtly be important. Synergistic properties can be realized in systems that combine different materials exhibiting different dimensionalities by exploiting their intrinsic compatibility. In many cases, the weaknesses of each material can be alleviated in heteroarchitectures. For example, 3D-2D halide perovskites can demonstrate novel behavior that neither material would be capable of separately. This review describes how the structural differences between 3D halide perovskites and 2D halide perovskites give rise to their disparate materials properties, discusses strategies for realizing mixed-dimensional systems of various architectures through solution-processing techniques, and presents a comprehensive outlook for the use of 3D-2D systems in solar cells. Finally, we investigate applications of 3D-2D systems beyond photovoltaics and offer our perspective on mixed-dimensional perovskite systems as semiconductor materials with unrivaled tunability, efficiency, and technologically relevant durability.
RESUMO
One of the primary methods for band gap tuning in metal halide perovskites has been halide (I/Br) mixing. Despite widespread usage of this type of chemical substitution in perovskite photovoltaics, there is still little understanding of the structural impacts of halide alloying, with the assumption being the formation of ideal solid solutions. The FASnI3-xBrx (x = 0-3) family of compounds provides the first example where the assumption breaks down, as the composition space is broken into two unique regimes (x = 0-2.9; x = 2.9-3) based on their average structure with the former having a 3D and the latter having an extended 3D (pseudo 0D) structure. Pair distribution function (PDF) analyses further suggest a dynamic 5s2 lone pair expression resulting in increasing levels of off-centering of the central Sn as the Br concentration is increased. These antiferroelectric distortions indicate that even the x = 0-2.9 phase space behaves as a nonideal solid-solution on a more local scale. Solid-state NMR confirms the difference in local structure yielding greater insight into the chemical nature and local distributions of the FA+ cation. In contrast to the FAPbI3-xBrx series, a drastic photoluminescence (PL) quenching is observed with x ≥ 1.9 compounds having no observable PL. Our detailed studies attribute this quenching to structural transitions induced by the distortions of the [SnBr6] octahedra in response to stereochemically expressed lone pairs of electrons. This is confirmed through density functional theory, having a direct impact on the electronic structure.
RESUMO
The long search for nontoxic alternatives to lead halide perovskites (LHPs) has shown that some compelling properties of LHPs, such as low effective masses of carriers, can only be attained in their closest Sn(II) and Ge(II) analogues, despite their tendency toward oxidation. Judicious choice of chemistry allowed formamidinium tin iodide (FASnI3) to reach a power conversion efficiency of 14.81% in photovoltaic devices. This progress motivated us to develop a synthesis of colloidal FASnI3 NCs with a concentration of Sn(IV) reduced to an insignificant level and to probe their intrinsic structural and optical properties. Intrinsic FASnI3 NCs exhibit unusually low absorption coefficients of 4 × 103 cm-1 at the first excitonic transition, a 190 meV increase of the band gap as compared to the bulk material, and a lack of excitonic resonances. These features are attributed to a highly disordered lattice, distinct from the bulk FASnI3 as supported by structural characterizations and first-principles calculations.
RESUMO
Ternary cuprous (Cu+)-based metal halides, represented by cesium copper iodide (e.g., CsCu2I3 and Cs3Cu2I5), are garnering increasing interest for light-emitting applications owing to their intrinsically high photoluminescence quantum yield and direct bandgap. Toward electrically driven light-emitting diodes (LEDs), it is highly desirable for the light emitters to have a high structural dimensionality as it may favor efficient electrical injection. However, unlike lead-based halide perovskites whose light-emitting units can be facilely arranged in three-dimensional (3D) ways, to date, nearly all ternary Cu+-based metal halides crystallize into 0D or 1D networks of Cu-X (X = Cl, Br, I) polyhedra, whereas 3D and even 2D structures remain mostly uncharted. Here, by employing a fluorinated organic cation, we report a new kind of ternary Cu+-based metal halides, (DFPD)CuX2 (DFPD+ = 4,4-difluoropiperidinium), which exhibits unique 2D layered crystal structure. Theoretical calculations reveal a highly dispersive conduction band of (DFPD)CuBr2, which is beneficial for charge carrier injection. It is also of particular significance to find that the 2D (DFPD)CuBr2 crystals show appealing properties, including improved ambient stability and an efficient warm white-light emission, making it a promising candidate for single-component lighting and display applications.
RESUMO
The alloyed lead/tin (Pb/Sn) halide perovskites have gained significant attention in the development of tandem solar cells and other optoelectronic devices due to their widely tunable absorption edge. To gain a better understanding of the intriguing properties of Pb/Sn perovskites, such as their anomalous bandgap's dependence on stoichiometry, it is important to deepen the understanding of their chemical behavior and local structure. Herein, we investigate a series of two-dimensional Ruddlesden-Popper (RP) and Dion-Jacobson (DJ) phase alloyed Pb/Sn bromide perovskites using butylammonium (BA) and 3-(aminomethyl)pyridinium (3AMPY) as the spacer cations: (BA)2(MA)n-1PbxSnn-xBr3n+1 (n = 1-3) and (3AMPY)(MA)n-1PbxSnn-xBr3n+1 (n = 1-3) through a solution-based approach. Our results show that the ratio and site preference of Pb/Sn atoms are influenced by the layer thickness (n) and spacer cations (A'), as determined by single-crystal X-ray diffraction. Solid-state 1H, 119Sn, and 207Pb NMR spectroscopy analysis shows that the Pb atoms prefer the outer layers in n = 3 members: (BA)2(MA)PbxSnn-xBr10 and (3AMPY)(MA)PbxSnn-xBr10. Layered 2D DJ alloyed Pb/Sn bromide perovskites (3AMPY)(MA)n-1PbxSnn-xBr3n+1 (n = 1-3) demonstrate much narrower optical band gaps, lower energy PL emission peaks, and longer carrier lifetimes compared to those of RP analogs. Density functional theory calculations suggest that Pb-rich alloys (Pb:Sn â¼4:1) for n = 1 compounds are thermodynamically favored over 50:50 (Pb:Sn â¼1:1) compositions. From grazing-incidence wide-angle X-ray scattering (GIWAXS), we see that films in the RP phase orient parallel to the substrate, whereas for DJ cases, random orientations are observed relative to the substrate.
RESUMO
Three-dimensional (3D) halide perovskites have attracted enormous research interest, but the choice of the A-site cations is limited by the Goldschmidt tolerance factor. In order to accommodate cations that lie outside the acceptable range of the tolerance factor, low-dimensional structures usually form. To maintain the favorable 3D connection, the links among the metal-halide octahedra need to be rearranged to fit the large cations. This can result in a departure from the proper corner-sharing perovskite architectures and lead to distinctly different perovskitoid motifs with edge- and face-sharing. In this work, we report four new 3D bromide perovskitoids incorporating linear organic diammonium cations, A'Pb2Br6 (A' is a +2 cation). We propose a rule that can guide the further expansion of this class of compounds, analogous to the notion of Goldschmidt tolerance factor widely adopted for 3D AMX3 perovskites. The fundamental building blocks in A'Pb2Br6 consist of two edge-shared octahedra, which are then connected by corner-sharing to form a 3D network. Different compounds adopt different structural motifs, which can be transformed from one to another by symmetry operations. Electronic structure calculations suggest that they are direct bandgap semiconductors, with relatively large band dispersions created by octahedra connected by corner-sharing. They exhibit similar electronic band structures and dynamic lattice characteristics to the regular 3D AMX3 perovskites. Structures with smaller Pb-Br-Pb angles and larger octahedra distortion exhibit broad photoluminescence at room temperature. The emerging structure-property relationships in these 3D perovskitoids set the foundation for designing and investigating these compounds for a variety of optoelectronic applications.
RESUMO
The nature of the organic cation in two-dimensional (2D) hybrid lead iodide perovskites tailors the structural and technological features of the resultant material. Herein, we present three new homologous series of (100) lead iodide perovskites with the organic cations allylammonium (AA) containing an unsaturated CâC group and iodopropylammonium (IdPA) containing iodine on the organic chain: (AA)2MAn-1PbnI3n+1 (n = 3-4), [(AA)x(IdPA)1-x]2MAn-1PbnI3n+1 (n = 1-4), and (IdPA)2MAn-1PbnI3n+1 (n = 1-4), as well as their perovskite-related substructures. We report the in situ transformation of AA organic layers into IdPA and the incorporation of these cations simultaneously into the 2D perovskite structure. Single-crystal X-ray diffraction shows that (AA)2MA2Pb3I10 crystallizes in the space group P21/c with a unique inorganic layer offset (0, <1/2), comprising the first example of n = 3 halide perovskite with a monoammonium cation that deviates from the Ruddlesden-Popper (RP) halide structure type. (IdPA)2MA2Pb3I10 and the alloyed [(AA)x(IdPA)1-x]2MA2Pb3I10 crystallize in the RP structure, both in space group P21/c. The adjacent I···I interlayer distance in (AA)2MA2Pb3I10 is â¼5.6 Å, drawing the [Pb3I10]4- layers closer together among all reported n = 3 RP lead iodides. (AA)2MA2Pb3I10 presents band-edge absorption and photoluminescence (PL) emission at around 2.0 eV that is slightly red-shifted in comparison to (IdPA)2MA2Pb3I10. The band structure calculations suggest that both (AA)2MA2Pb3I10 and (IdPA)2MA2Pb3I10 have in-plane effective masses around 0.04m0 and 0.08m0, respectively. IdPA cations have a greater dielectric contribution than AA. The excited-state dynamics investigated by transient absorption (TA) spectroscopy reveal a long-lived (â¼100 ps) trap state ensemble with broad-band emission; our evidence suggests that these states appear due to lattice distortions induced by the incorporation of IdPA cations.
RESUMO
Three-dimensional organic-inorganic perovskites have emerged as one of the most promising thin-film solar cell materials owing to their remarkable photophysical properties, which have led to power conversion efficiencies exceeding 20 per cent, with the prospect of further improvements towards the Shockley-Queisser limit for a singlejunction solar cell (33.5 per cent). Besides efficiency, another critical factor for photovoltaics and other optoelectronic applications is environmental stability and photostability under operating conditions. In contrast to their three-dimensional counterparts, Ruddlesden-Popper phases--layered two-dimensional perovskite films--have shown promising stability, but poor efficiency at only 4.73 per cent. This relatively poor efficiency is attributed to the inhibition of out-of-plane charge transport by the organic cations, which act like insulating spacing layers between the conducting inorganic slabs. Here we overcome this issue in layered perovskites by producing thin films of near-single-crystalline quality, in which the crystallographic planes of the inorganic perovskite component have a strongly preferential out-of-plane alignment with respect to the contacts in planar solar cells to facilitate efficient charge transport. We report a photovoltaic efficiency of 12.52 per cent with no hysteresis, and the devices exhibit greatly improved stability in comparison to their three-dimensional counterparts when subjected to light, humidity and heat stress tests. Unencapsulated two-dimensional perovskite devices retain over 60 per cent of their efficiency for over 2,250 hours under constant, standard (AM1.5G) illumination, and exhibit greater tolerance to 65 per cent relative humidity than do three-dimensional equivalents. When the devices are encapsulated, the layered devices do not show any degradation under constant AM1.5G illumination or humidity. We anticipate that these results will lead to the growth of single-crystalline, solution-processed, layered, hybrid, perovskite thin films, which are essential for high-performance opto-electronic devices with technologically relevant long-term stability.
RESUMO
In the fast-evolving field of halide perovskite semiconductors, the 2D perovskites (A')2(A) n-1M n X3n+1 [where A = Cs+, CH3NH3+, HC(NH2)2+; A' = ammonium cation acting as spacer; M = Ge2+, Sn2+, Pb2+; and X = Cl-, Br-, I-] have recently made a critical entry. The n value defines the thickness of the 2D layers, which controls the optical and electronic properties. The 2D perovskites have demonstrated preliminary optoelectronic device lifetime superior to their 3D counterparts. They have also attracted fundamental interest as solution-processed quantum wells with structural and physical properties tunable via chemical composition, notably by the n value defining the perovskite layer thickness. The higher members (n > 5) have not been documented, and there are important scientific questions underlying fundamental limits for n To develop and utilize these materials in technology, it is imperative to understand their thermodynamic stability, fundamental synthetic limitations, and the derived structure-function relationships. We report the effective synthesis of the highest iodide n-members yet, namely (CH3(CH2)2NH3)2(CH3NH3)5Pb6I19 (n = 6) and (CH3(CH2)2NH3)2(CH3NH3)6Pb7I22 (n = 7), and confirm the crystal structure with single-crystal X-ray diffraction, and provide indirect evidence for "(CH3(CH2)2NH3)2(CH3NH3)8Pb9I28" ("n = 9"). Direct HCl solution calorimetric measurements show the compounds with n > 7 have unfavorable enthalpies of formation (ΔHf), suggesting the formation of higher homologs to be challenging. Finally, we report preliminary n-dependent solar cell efficiency in the range of 9-12.6% in these higher n-members, highlighting the strong promise of these materials for high-performance devices.
RESUMO
Two-dimensional (2D) halide perovskites have several distinct structural classes and exhibit great tunability, stability, and high potential for photovoltaic applications. Here, we report a new series of hybrid 2D perovskites in the Dion-Jacobson (DJ) class based on aromatic m-phenylenediammonium (mPDA) dications. The crystal structures of the DJ perovskite materials (mPDA)MAn-1PbnI3n+1 (n = 1-3) were solved and refined using single-crystal X-ray crystallography. The results indicate a short I···I interlayer distance of 4.00-4.04 Å for the (mPDA)MAn-1PbnI3n+1 (n = 2 and 3) structures, which is the shortest among DJ perovskites. However, Pb-I-Pb angles are as small as 158-160°, reflecting the large distortion of the inorganic framework, which results in larger band gaps for these materials than those in other DJ analogues. Density functional theory calculations suggest appreciable dispersion in the stacking direction, unlike the band structures of the Ruddlesden-Popper phases, which exhibit flat bands along the stacking direction. This is a consequence of the short interlayer I···I distances that can lead to interlayer electronic coupling across the layers. The solution-deposited films (nominal (mPDA)MAn-1PbnI3n+1 compositions of n = 1-6) reveal improved surface coverage with increasing nominal n value with the higher n films being composed of a mixture of n = 1 and bulk three-dimensional MAPbI3 perovskites. The films made from solutions of these materials behave differently from those of other 2D iodide perovskites, and their solar cells have a mixture of n = 1 DJ and MAPbI3 as light-absorbing semiconductors.
RESUMO
Hybrid halide perovskites are now superstar materials leading the field of low-cost thin film photovoltaics technologies. Following the surge for more efficient and stable 3D bulk alloys, multilayered halide perovskites and colloidal perovskite nanostructures appeared in 2016 as viable alternative solutions to this challenge, largely exceeding the original proof of concept made in 2009 and 2014, respectively. This triggered renewed interest in lower-dimensional hybrid halide perovskites and at the same time increasingly more numerous and differentiated applications. The present paper is a review of the past and present literature on both colloidal nanostructures and multilayered compounds, emphasizing that availability of accurate structural information is of dramatic importance to reach a fair understanding of quantum and dielectric confinement effects. Layered halide perovskites occupy a special place in the history of halide perovskites, with a large number of seminal papers in the 1980s and 1990s. In recent years, the rationalization of structure-properties relationship has greatly benefited from new theoretical approaches dedicated to their electronic structures and optoelectronic properties, as well as a growing number of contributions based on modern experimental techniques. This is a necessary step to provide in-depth tools to decipher their extensive chemical engineering possibilities which surpass the ones of their 3D bulk counterparts. Comparisons to classical semiconductor nanostructures and 2D van der Waals heterostructures are also stressed. Since 2015, colloidal nanostructures have undergone a quick development for applications based on light emission. Although intensively studied in the last two years by various spectroscopy techniques, the description of quantum and dielectric confinement effects on their optoelectronic properties is still in its infancy.
RESUMO
The Goldschmidt tolerance factor in halide perovskites limits the number of cations that can enter their cages without destabilizing their overall structure. Here, we have explored the limits of this geometric factor and found that the ethylammonium (EA) cations which lie outside the tolerance factor range can still enter the cages of the 2D halide perovskites by stretching them. The new perovskites allow us to study how these large cations occupying the perovskite cages affect the structural, optical, and electronic properties. We report a series of cation engineered 2D Ruddlesden-Popper lead iodide perovskites (BA)2(EAxMA1-x)2Pb3I10 (x = 0-1, BA is n-butylammonium, MA is methylammonium) by the incorporation of a large EA cation in the cage. An analysis of the single-crystal structures reveals that the incorporation of EA in the cage significantly stretches Pb-I bonds, expands the cage, and induces a larger octahedral distortion in the inorganic framework. Spectroscopic and theoretical studies show that such structural deformation leads to a blue-shifted bandgap, sub-bandgap trap states with wider energetic distribution, and stronger photoluminescence quenching. These results enrich the family of 2D perovskites and provide new insights for understanding the structure-property relationship in perovskite materials.
RESUMO
Large organic A cations cannot stabilize the 3D perovskite AMX3 structure because they cannot be accommodated in the cubo-octhedral cage (do not follow the Goldschmidt tolerance factor rule), and they generally template low-dimensional structures. Here we report that the large dication aminomethylpyridinium (AMPY) can template novel 3D structures which resemble conventional perovskites. They have the formula (xAMPY)M2I6 (x = 3 or 4, M = Sn2+ or Pb2+) which is double of the AMX3 formula. However, because of the steric requirement of the Goldschmidt tolerance factor rule, it is impossible for (xAMPY)M2I6 to form proper perovskite structures. Instead, a combination of corner-sharing and edge-sharing connectivity is adopted in these compounds leading to the new 3D structures. DFT calculations reveal that the compounds are indirect band gap semiconductors with direct band gaps presenting at slightly higher energies and dispersive electronic bands. The indirect band gaps of the Sn and Pb compounds are â¼1.7 and 2.0 eV, respectively, which is slightly higher than the corresponding AMI3 3D perovskites. The Raman spectra for the compounds are diffuse, with a broad rising central peak at very low frequencies around 0 cm-1, a feature that is characteristic of dynamical lattices, high anharmonicity, and dissipative vibrations very similar to the 3D AMX3 perovskites. Devices of (3AMPY)Pb2I6 crystals exhibit clear photoresponse under ambient light without applied bias, reflecting a high carrier mobility (µ) and long carrier lifetime (τ). The devices also exhibit sizable X-ray generated photocurrent with a high µτ product of â¼1.2 × 10-4 cm2 /V and an X-ray sensitivity of 207 µC·Gy-1·cm-2.
RESUMO
Organic-inorganic hybrid halide perovskites are promising semiconductors with tailorable optical and electronic properties. The choice of A-site cation to support a three-dimensional (3D) perovskite structure AMX3 (where M is a metal and X is a halide) is limited by the geometric Goldschmidt tolerance factor. However, this geometric constraint can be relaxed in two-dimensional (2D) perovskites, providing us an opportunity to understand how various A-site cations modulate the structural properties and thereby the optoelectronic properties. Here, we report the synthesis and structures of single-crystal (BA)2(A)Pb2I7 where BA = butylammonium and A = methylammonium (MA), formamidinium (FA), dimethylammonium (DMA), or guanidinium (GA), with a series of A-site cations varying in size. Single-crystal X-ray diffraction reveals that the MA, FA, and GA structures crystallize in the same Cmcm space group, while the DMA imposes the Ccmb space group. We observe that as the A-site cation becomes larger, the Pb-I bond continuously elongates, expanding the volume of the perovskite cage, equivalent to exerting "negative pressure" on the perovskite structures. Optical studies and DFT calculations show that the Pb-I bond length elongation reduces the overlap of the Pb s- and I p-orbitals and increases the optical bandgap, while Pb-I-Pb tilting angles play a secondary role. Raman spectra show lattice softening with increasing size of the A-site cation. These structural changes with enlarged A cations result in significant decreases in photoluminescence intensity and lifetime, consistent with a more pronounced nonradiative decay. Transient absorption microscopy results suggest that the PL drop may derive from a higher concentration of traps or phonon-assisted nonradiative recombination. The results highlight that extending the range of Goldschmidt tolerance factors for 2D perovskites is achievable, enabling further tuning of the structure-property relationships in 2D perovskites.
RESUMO
Layered hybrid metal-halide perovskites with non-centrosymmetric crystal structure are predicted to show spin-selective band splitting from Rashba effects. Thus, fabrication of metal-halide perovskites with defined crystal symmetry is desired to control the spin-splitting in their electronic states. Here, we report the influence of halogen para-substituents on the crystal structure of benzylammonium lead iodide perovskites (4-XC6H4CH2NH3)2PbI4 (X = H, F, Cl, Br). Using X-ray diffraction and second-harmonic generation, we study structure and symmetry of single-crystal and thin-film samples. We report that introduction of a halogen atom lowers the crystal symmetry such that the chlorine- and bromine-substituted structures are non-centrosymmetric. The differences can be attributed to the nature of the intermolecular interactions between the organic molecules. We calculate electronic band structures and find good control of Rashba splittings. Our results present a facile approach to tailor hybrid layered metal halide perovskites with potential for spintronic and nonlinear optical applications.
RESUMO
Hybrid layered halide perovskites have achieved impressive performance in optoelectronics. New structural types in the two-dimensional (2D) halide system such as the Dion-Jacobson phases have attracted wide research attention due to the short interlayer distance and unique layer orientation that facilitate better charge-transport and higher stability in optoelectronic devices. Here, we report the first solid solution series incorporating both A and A' cations in the 2D Dion-Jacobson family, with the general formula (A')(A)Pb2Br7 ((A' = 3-(aminomethyl)piperidinium (3AMP) and 4-(aminomethyl)piperidinium) (4AMP); A = methylammonium (MA) and formamidinium (FA)). Mixing the spacing A' cations and perovskitizer A cations generates the new (3AMP)a(4AMP)1-a(FA)b(MA)1-bPb2Br7 perovskites. The crystallographically refined crystal structures using single-crystal X-ray diffraction data reveal that the distortion of the inorganic framework is heavily influenced by the degree of A' and A alloying. A rising fraction of 4AMP in the structure, decreases the Pb-Br-Pb angles, making the framework more distorted. On the contrary, higher FA fractions increase the Pb-Br-Pb angles. This structural evolution fine-tunes the optical properties where the larger the Pb-Br-Pb angle, the narrower the band gap. The photoluminescence emission energy mirrors this trend. Raman spectroscopy reveals a highly dynamical lattice similar to MAPbBr3 and consistent with the local distortion environment of the [Pb2Br7] framework. Density functional theory (DFT) calculations of the electronic structures reveal the same trend as the experimental results where (3AMP)(FA)Pb2Br7 has the smallest band gap while (4AMP)(MA)Pb2Br7 has the largest band gap. The structural effects from solely the organic cations in the 2D system highlight the importance of understanding the high sensitivity of the optoelectronic properties on the structural tuning in this broad class of materials.
RESUMO
The optical and light emission properties of tin and lead halide perovskites are remarkable because of the robust room-temperature (RT) performance, broad wavelength tunability, high efficiency, and good quenching resistance to defects. These highly desirable attributes promise to transform current light-emitting devices, phosphors, and lasers. One disadvantage in most of these materials is the sensitivity to moisture. Here, we report a new air-stable one-dimensional (1D) hybrid lead-free halide material (DAO)Sn2I6 (DAO, 1,8-octyldiammonium) that is resistant to water for more than 15 h. The material exhibits a sharp optical absorption edge at 2.70 eV and a strong broad orange light emission centered at 634 nm, with a full width at half-maximum (fwhm) of 142 nm (0.44 eV). The emission has a long photoluminescence (PL) lifetime of 582 ns, while the intensity is constant over a very broad temperature range (145-415 K) with a photoluminescence quantum yield (PLQY) of at least 20.3% at RT. Above 415 K the material undergoes a structural phase transition from monoclinic (C2/c) to orthorhombic (Ibam) accompanied by a red shift in the band gap and a quench in the photoluminescence emission. Density functional theory calculations support the trend in the optical properties and the 1D electronic nature of the structure, where the calculated carrier effective masses along the inorganic chain are significantly lower than those perpendicular to the chain. Thin films of the compound readily fabricated from solutions exhibit the same optical properties, but with improved PLQY of 36%, for a 60 nm thick film, among the highest reported for lead-free low-dimensional 2D and 1D perovskites and metal halides.
RESUMO
Lead halide perovskites have emerged as promising new semiconductor materials for high-efficiency photovoltaics, light-emitting applications and quantum optical technologies. Their luminescence properties are governed by the formation and radiative recombination of bound electron-hole pairs known as excitons, whose bright or dark character of the ground state remains unknown and debated. While symmetry analysis predicts a singlet non-emissive ground exciton topped with a bright exciton triplet, it has been predicted that the Rashba effect may reverse the bright and dark level ordering. Here, we provide the direct spectroscopic signature of the dark exciton emission in the low-temperature photoluminescence of single formamidinium lead bromide perovskite nanocrystals under magnetic fields. The dark singlet is located several millielectronvolts below the bright triplet, in fair agreement with an estimation of the long-range electron-hole exchange interaction. Nevertheless, these perovskites display an intense luminescence because of an extremely reduced bright-to-dark phonon-assisted relaxation.
RESUMO
Two-dimensional layered halide organic perovskites (LHOPs) are promising candidates for many optoelectronic applications due to their interesting tunable properties. They provide a unique opportunity to control energy and charge dynamics via the independent tunability of the energy levels within the perovskite and the organic spacer for various optoelectronic applications. In the perovskite layer alone, one can replace the Pb (Sn), the halide (X = I, Br, Cl), the organic component, and the number of layers between the organic spacer layers. In addition, there are many possibilities for organic spacer layers between the perovskite layers, making it difficult for experimental methods to comprehensively explore such an extensive combinatorial space. Of particular technological interest is alignment of electronic levels between the perovskite layer and the organic spacer layer, leading to desired transfer of energy or charge carriers between perovskite and organic components. For example, as band edge absorption is almost entirely attributed to the perovskite layer, one way to demonstrate energy transfer is to observe triplet emission from organic spacers. State-of-the-art computational chemistry tools can be used to predict the properties of many stoichiometries in search for LHOPs that have the most promising electronic-structure features. In this first-principles study, we survey a group of π-conjugated organic spacer candidates for use in triplet light-emitting LHOPs. Utilizing density functional theory (DFT) and time-dependent DFT, we calculate the first singlet (S1) and triplet (T1) excitation energy in the ground-state geometry and the first triplet excitation energy in the excited-triplet-state relaxed geometry (T1*). By comparing these energies to the known lowest exciton energy level of PbnX3n+1 perovskite layers (X = I, Br, Cl), we can identify organic spacer and perovskite layer pairings for possible transfer of Wannier excitons from the inorganic perovskite lattice to spin-triplet Frenkel excitons located on the organic cation. We successfully identify ten organic spacer candidates for possible pairing with perovskite layers of specific halide composition to achieve triplet light emission across the visible energy range. Molecular dynamics simulations predict that finite temperatures and perovskite environment have little influence on the average excitation energies of the two common organic spacers naphthylethylammonium (NEA) and phenelethylammonium (PEA). We find significant thermal broadening up to 0.5 eV of the optical excitation energies appearing due to finite temperature effects. The findings herein provide insights into alignment of electronic levels of the conjugated organic spacer with the layer.
RESUMO
Two-dimensional (2D) halide perovskites have extraordinary optoelectronic properties and structural tunability. Among them, the Dion-Jacobson phases with the inorganic layers stacking exactly on top of each other are less explored. Herein, we present the new series of 2D Dion-Jacobson halide perovskites, which adopt the general formula of A'An-1PbnI3n+1 (A' = 4-(aminomethyl)pyridinium (4AMPY), A = methylammonium (MA), n = 1-4). By modifying the position of the CH2NH3+ group from 4AMPY to 3AMPY (3AMPY = 3-(aminomethyl)pyridinium), the stacking of the inorganic layers changes from exactly eclipsed to slightly offset. The perovskite octahedra tilts are also different between the two series, with the 3AMPY series exhibiting smaller bandgaps than the 4AMPY series. Compared to the aliphatic cation of the same size (AMP = (aminomethyl)piperidinium), the aromatic spacers increase the rigidity of the cation, reduce the interlayer spacing, and decrease the dielectric mismatch between inorganic layer and the organic spacer, showing the indirect but powerful influence of the organic cations on the structure and consequently on the optical properties of the perovskite materials. All A'An-1PbnI3n+1 compounds exhibit strong photoluminescence (PL) at room temperature. Preliminary solar cell devices based on the n = 4 perovskites as absorbers of both series exhibit promising performances, with a champion power conversion efficiency (PCE) of 9.20% for (3AMPY)(MA)3Pb4I13-based devices, which is higher than the (4AMPY)(MA)3Pb4I13 and the corresponding aliphatic analogue (3AMP)(MA)3Pb4I13-based ones.