RESUMO
We show, in this paper that multivalent ferrocyanide anions can penetrate into exponentially growing (PGA/PAH)n multilayer films whatever the nature of the last deposited layer. These ions are not able to diffuse out of the film when it is brought in contact with a pure buffer solution. However, the contact of this film with a poly(allylamine) (PAH) or a poly(L-glutamic acid) (PGA) solution leads to the release of ferrocyanide ions from the multilayer. It is shown that the release of ferrocyanide anions, when the film is in contact with a PGA solution, is due to the diffusion of the PGA chains into the film so that an exchange between ferrocyanide ions and PGA chains takes place inside the film. On the other hand, PAH chains do not diffuse into PGA/PAH multilayers. When the film is then brought in contact with a PAH solution, the PAH chains from the solution are expected to strongly interact with the ferrocyanide ions and thus induce a diffusion mechanism of the multivalent anions out of the film, the film/solution interface playing the role of a sink for these ions. This work thus shows that interactions between multivalent ions and exponentially growing films are much more complex than expected at first sight and that polyelectrolyte multilayers must be seen as dynamic entities in which diffusion and exchange processes can take place.
Assuntos
Materiais Biocompatíveis/química , Eletrólitos/química , Ferrocianetos/química , Poliaminas/química , Ácido Poliglutâmico/química , Adsorção , Difusão , Íons , Soluções/química , Espectroscopia de Infravermelho com Transformada de Fourier , Fatores de TempoRESUMO
Mechanically responsive surfaces that allow to switch reversibly from a hydrophobic to a hydrophilic substrate are reported. The surfaces are constituted of polyelectrolyte multilayers deposited on modified charged silicone sheets. n bilayers of poly(allylamine)-Nafion (PAH-Naf) and m bilayers of poly(allylamine)-poly(acrylic acid) (PAH-PAA) composed the multilayers. A (PAH-Naf)(n) film possesses a water contact angle of around 105 degrees, whereas the contact angle of a (PAH-Naf)(4)-(PAH-PAA)(m) multilayer is around 50 degrees. When such a film with m < 5 and terminated by PAA is stretched out, its water contact angle increases up to around 100 degrees. Successive elongation/retraction cycles allow the water contact angle to alternate reversibly between 100 and 57 degrees indicating the reversible mechanical responsive nature of the film.