Monolayer of silica nanospheres assembled onto ITO-coated glass substrates by spin-coating.

In this work, we synthesized colloidal silica nanospheres with an average size of 400 nm through the modified Stöber method and successfully fabricated an ordered close-packed silica nanosphere monolayer onto ITO-coated glass substrates using a three-step spin-coating method. ITO films showed resistivity comparable to that of commercial ITO and the silica nanosphere monolayer-coated ITO/glass substrate exhibited good optical transmittance in the visible (550 nm) and near-infrared (900 nm) regions of 62% and 82%, respectively. The results suggest that this monolayer can be used in optoelectronic devices to enhance efficiency in photovoltaic cells.

The use of a Ga+ focused ion beam to modify graphene for device applications.

In this work, we clarify the features of the lateral damage of line defects in single layer graphene. The line defects were produced through well-controlled etching of graphene using a Ga(+) focused ion beam. The lateral damage length was obtained from both the integrated intensity of the disorder induced Raman D band and the minimum ion fluence. Also, the line defects were characterized by polarized Raman spectroscopy. It was found that graphene is resilient under the etching conditions since the intensity of the defect induced Raman D peak exhibits a dependence on the direction of the lines relative to the crystalline lattice and also on the direction of the laser polarization relative to the lines. In addition, electrical measurements of the modified graphene were performed. Different ion fluences were used in order to obtain a completely insulating defect line in graphene, which was determined experimentally by means of charge injection and electric force microscopy measurements. These studies demonstrate that a Ga+ ion column combined with Raman spectroscopy is a powerful technique to produce and understand well-defined periodic arrays of defects in graphene, opening possibilities for better control of nanocarbon devices.

Micro-arc oxidation as a tool to develop multifunctional calcium-rich surfaces for dental implant applications.

Titanium (Ti) is commonly used in dental implant applications. Surface modification strategies are being followed in last years in order to build Ti oxide-based surfaces that can fulfill, simultaneously, the following requirements: induced cell attachment and adhesion, while providing a superior corrosion and tribocorrosion performance. In this work micro-arc oxidation (MAO) was used as a tool for the growth of a nanostructured bioactive titanium oxide layer aimed to enhance cell attachment and adhesion for dental implant applications. Characterization of the surfaces was performed, in terms of morphology, topography, chemical composition and crystalline structure. Primary human osteoblast adhesion on the developed surfaces was investigated in detail by electronic and atomic force microscopy as well as immunocytochemistry. Also an investigation on the early cytokine production was performed. Results show that a relatively thick hybrid and graded oxide layer was produced on the Ti surface, being constituted by a mixture of anatase, rutile and amorphous phases where calcium (Ca) and phosphorous (P) were incorporated. An outermost nanometric-thick amorphous oxide layer rich in Ca was present in the film. This amorphous layer, rich in Ca, improved fibroblast viability and metabolic activity as well as osteoblast adhesion. High-resolution techniques allowed to understand that osteoblasts adhered less in the crystalline-rich regions while they preferentially adhere and spread over in the Ca-rich amorphous oxide layer. Also, these surfaces induce higher amounts of IFN-γ cytokine secretion, which is known to regulate inflammatory responses, bone microarchitecture as well as cytoskeleton reorganization and cellular spreading. These surfaces are promising in the context of dental implants, since they might lead to faster osseointegration.