Superior Large-Signal Piezoelectric Coefficient in Textured NBT-Based Piezoceramics by Template-Induced Structure and Composition Modulation.

The field-induced-phase transition in (Na1/2Bi1/2)TiO3-based lead-free piezoceramics can be facilitated in the ⟨001⟩-crystallographic orientation, and the templated grain growth is an effective method to align polycrystalline ceramics along with specific directions. However, due to the low texturing degree and undesirable composite effect of the added templates, the textured ceramics using the templated grain growth (TGG) method usually require a higher driving field to trigger the phase transition instead. Here, ⟨001⟩-textured (Na0.5Bi0.5)0.935Ba0.065Ti0.978(Fe0.5Nb0.5)0.022O3 ceramics are prepared through a liquid-phase-assisted TGG process at a low sintering temperature (1000 °C), in which the NaNbO3 (NN) templates induce a strong crystallographic anisotropic structure (a high Lotgering factor of 95%) while dissolving into oriented grains. The dissolution of templates acts as a composition doping and contributes to reducing the driving electric field as proven by the phase-field simulation analysis. Furthermore, electrical and structural characterizations reveal that an increased ionic disorder occurs in the textured ceramic, causing highly dynamic polar nanoregions and a larger reversible phase transition. Thanks to the appropriate structure/composition control, the textured ceramic achieves a large d33* value of 907 pm/V at 40 kV/cm. The high-performance lead-free ceramic under low driving electric field benefits the development of multilayer piezoelectric actuators.

Lead-Free BF-BT Ceramics With Ultrahigh Curie Temperature for Piezoelectric Accelerometer.

Piezoelectric ceramics have been widely used in high precision sensors such as vibration detection, but piezoelectric accelerometers in high-temperature applications are very rare. We prepared ( 1- x ) BiFeO3- x BaTiO3-0.0035MnO2-0.001Li2CO3(BF- x BT) ceramics by a solid state approach, and investigated the effect of BT content( x ) on the phase structure, microstructure, dielectric properties, ferroelectric properties, piezoelectric properties, temperature stability, and especially the sensitivity of the piezoelectric accelerometer. The crystal structure of the sample is pure perovskite structure with the MPB (R and P phases) locating in a composition range of 0.28 ≤ x ≤ 0.32 for BF-xBT ceramics, and the single R phase exist at . When x = 0.30, the ceramic presents both high Curie temperature and d33 . Notably, the sensitivity of BF-0.30BT piezoelectric accelerometer reaches the highest value of about 40 pC/g and shows an excellent stability until 400 °C, indicating that this material is a promising candidate for high-temperature piezoelectric accelerometer applications.

Enhanced Dielectric Energy Storage Performance of 0.45Na0.5Bi0.5TiO3-0.55Sr0.7Bi0.2TiO3/AlN 0-3 Type Lead-Free Composite Ceramics.

Na0.5Bi0.5TiO3 (NBT) ceramic is the promising dielectric material for energy storage devices due to its high maximum polarizability and temperature stability. However, its low breakdown strength limits its application. Here, we prepared 0-3 type composite 0.45Na0.5Bi0.5TiO3-0.55Sr0.7Bi0.2TiO3/x wt % AlN (NBT-SBT/xAlN) to increase the breakdown strength. The effects of the various AlN contents on the phase composition, microstructures, dielectric, and energy storage properties of NBT-SBT were systematically discussed. The result showed that the enhanced energy storage properties were obtained by introducing AlN particles. The NBT-SBT/6AlN composite ceramics showed a high breakdown strength of 360 kV/cm, large energy density of 5.53 J/cm3, and energy efficiency of 90%. Meanwhile, the excellent frequency (10-500 Hz) and temperature stability (25-125 °C) were exhibited with the fluctuation of energy storage within 9% and energy efficiency more than 87%, suggesting that the 0-3 composite NBT-SBT/xAlN is a candidate dielectric material for the dielectric energy storage.