Intratubular penetration in post cementing: A comparative study between a total etching system and a self-etching cement.

PURPOSE: To analyze the penetration depth and percentage perimeter with penetration of two fiber post cementing systems using confocal laser scanning microscopy (CLSM). METHODS: 20 maxillary incisors were shaped with the Mtwo system and filled using lateral condensation and TopSeal mixed with fluorescein. Fiber posts were cemented. The samples were divided into two groups of 10 teeth each, according to the post cementing technique used: Prime&Bond NT combined with Rebilda DC using a total dentin etching technique (Group 1); or BisCem a self-adhesive cement (Group 2). Rhodamine B was incorporated in the adhesive systems. Cross-sections were prepared, with the selection of three sections (coronal, middle and apical thirds). CLSM was used to measure the percentage perimeter of the root canal showing penetration of the endodontic cement and of the adhesive system in the dentin tubules, together with the maximum penetration depth. The nonparametric Mann-Whitney U-test was used to compare the data referred to each of the three tooth sections between the two study groups. The Friedman test was used to compare the variables by coronal, middle and apical thirds within each group. RESULTS: Greater penetration was recorded with the BisCem system in all thirds, with statistically significant differences in the case of the middle and apical thirds (P = 0.001). The percentage perimeter with penetration was also greater in all thirds with the BisCem system, though without significant differences between the two groups. Penetration depth and percentage were found to decrease in the coronal to apical direction in both groups.

Root canal adaptation and intra-tubular penetration of three fiber-post cementation systems.

BACKGROUND: To measure the penetration of three bonding systems for the luting of fiber glass posts in endodontically treated teeth, using confocal laser scanning microscopy (CLSM). MATERIAL AND METHODS: A total of 30 maxillary incisors were shaped with the Mtwo system and filled with gutta-percha and Top Seal cement. The sample was divided into three groups (ni=10) according to the bonding system used to cement the posts: Group 1 (Prime&Bond NT and Rebilda DC with a total-etch technique); Group 2 (Futurabond DC and Rebilda DC with a dentin self-etch technique); and Group 3 (BisCem self-adhesive cement). Rhodamine B was added to the bonding systems to allow visualization by CLSM. Three 1-mm thick cross-sections were obtained of each root at a distance of 2, 5 and 8 mm from the coronal limit of the root. The specific software of the CLSM system was used to measure the percentage of the root canal perimeter showing penetration of the bonding system in the dentinal tubules, together with the maximum depth of penetration. Comparison between groups were made by Kruskal Wallis test, and comparison two by two groups with Mann-Whitney U-test. RESULTS: Depth of penetration of the resin tags, were distributed from greater to lesser depth as follows: BisCem > Prime&Bond NT > Futurabond DC. BisCem showed significantly greater penetration in the middle and apical thirds than the rest of the systems (906.14±67.42 and 699.27±76.26 µm, respectively). The percentage perimeter exhibiting penetration in the coronal third was significantly greater with BisCem versus Futurabond DC (56.08±7.24 and 44.38±5.23%, respectively). No significant differences were recorded in the middle and apical thirds among the three systems. CONCLUSIONS: BisCem resulted in greater depth of intratubular penetration at all studied levels. The percentage perimeter of the canal showing penetration was similar for all the bonding systems. Key words:Fiber post luting, sealer adaptation, confocal laser scanning microscope.