RESUMO
Interface modulation of nickel phosphide (Ni2 P) to produce an optimal catalytic activation barrier has been considered a promising approach to enhance the hydrogen production activity via water splitting. Herein, heteronuclei-mediated in situ growth of hollow Ni2 P nanospheres on a surface defect-engineered titanium carbide (Ti3 C2 Tx ) MXene showing high electrochemical activity for the hydrogen evolution reaction (HER) is demonstrated. The heteronucleation drives intrinsic strain in hexagonal Ni2 P with an observable distortion at the Ni2 P@Ti3 C2 Tx MXene heterointerface, which leads to charge redistribution and improved charge transfer at the interface between the two components. The strain at the Ni2 P@Ti3 C2 Tx MXene heterointerface significantly boosts the electrochemical catalytic activities and stability toward HER in an acidic medium via a combination between experimental results and theoretical calculations. In a 0.5 m H2 SO4 electrolyte, the Ni2 P@Ti3 C2 Tx MXene hybrid shows excellent HER catalytic performance, requiring an overpotential of 123.6 mV to achieve 10 mA cm-2 with a Tafel slope of 39 mV dec-1 and impressive durability over 24 h operation. This approach presents a significant potential to rationally design advanced catalysts coupled with 2D materials and transition metal-based compounds for state-of-the-art high efficiency energy conversions.
RESUMO
In this study, a solution-processable compact vanadium oxide (V2O5) film with a globular nanoparticulate structure is introduced to the hole transport layer (HTL) of polymer bulk-heterojunction based solar cells comprised of PTB7:PC70BM by using a facile metal-organic decomposition method to replace the conventionally utilized poly(3,4-ethylenedioxythiophene): poly(styrenesulfonate) (PEDOT:PSS). For this, a biocompatible structure-determining agent, polyethylene glycol (PEG, Mn 300), is used as an additive in the precursor to form the nanoparticulate compact V2O5 (hereafter referred to as NP-V2O5) film, which possesses an outstandingly smooth surface morphology. The introduction of NP-V2O5 HTL via the solution process with a neutral pH condition successfully improved the stability by preventing the decomposition of indium tin oxide (ITO) glass and the penetration of heavy-metal components and moisture, which are considered as the crucial drawbacks of using PEDOT:PSS. Over 1440 h (60 days) of the stability test, an organic solar cell (OSC) with NP-V2O5 showed a significant durability, maintaining 82% of its initial power conversion efficiency (PCE), whereas an OSC with PEDOT:PSS maintained 51% of its initial PCE. Furthermore, due to the positive effects of the modified surface properties of NP-V2O5, the PCE was slightly enhanced from 7.47% to 7.89% with a significant improvement in the short-circuit current density and fill factor.