RESUMO
Articular cartilage is a highly organized tissue that has a limited ability to heal. Tissue engineering is actively exploited for joint tissue reconstruction in numerous cases of articular cartilage degeneration associated with trauma, arthrosis, rheumatoid arthritis, and osteoarthritis. However, the optimal scaffolds for cartilage repair are not yet identified. Here we have directly compared five various scaffolds, namely collagen-I membrane, collagen-II membrane, decellularized cartilage, a cellulose-based implant, and commercially available Chondro-Gide® (Geistlich Pharma AG, Wolhusen, Switzerland) collagen membrane. The scaffolds were implanted in osteochondral full-thickness defects, formed on adult Wistar rats using a hand-held cutter with a diameter of 2.0 mm and a depth of up to the subchondral bone. The congruence of the articular surface was almost fully restored by decellularized cartilage and collagen type II-based scaffold. The most vivid restoration was observed 4 months after the implantation. The formation of hyaline cartilage was not detected in any of the groups. Despite cellular infiltration into scaffolds being observed in each group except cellulose, neither chondrocytes nor chondro-progenitors were detected. We concluded that for restoration of hyaline cartilage, scaffolds have to be combined either with cellular therapy or morphogens promoting chondrogenic differentiation.
Assuntos
Cartilagem Hialina/patologia , Implantação de Prótese , Alicerces Teciduais/química , Animais , Colágenos Fibrilares/metabolismo , Articulação do Joelho/patologia , Masculino , Osteogênese , Ratos Wistar , Fatores de Transcrição SOX9/metabolismoRESUMO
Decellularized bovine pericardium (DBP)-based biomeshes are the gold standard in reconstructive surgery. In order to prolong their stability after the transplantation, various chemical cross-linking strategies are employed. However, structural and functional properties of the biomeshes differ in dependence on the cross-linker used. Here, we performed a bottom-up study of structural and functional alterations of DBP-based biomeshes following cross-linking with hexamethylene diisocyanate (HMDC), ethylene glycol diglycidyl ether (EGDE), 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide (EDC) and genipin. The in vitro cytotoxicity tests supported their clinical applicability. Their structural differences (eg roughness, fibre thickness, pore morphology) were evaluated using the two-photon confocal laser scanning, atomic force, scanning electron and polarized light microscopies. HMDC and EDC samples appeared to be the roughest. Complex mechanical trials indicated the tendency to reduced Young's Modulus and mechanical anisotropy values of DBP upon cross-linking. The lowest mechanical anisotropy was found in EDC and genipin sample groups. In vitro collagenase susceptibility was the highest for EDC samples and the lowest for EGDE samples. The comparative analysis of the results allowed us to recognize the strengths and weaknesses of each cross-linker in relation to a particular clinical application.
Assuntos
Teste de Materiais , Pericárdio/cirurgia , Engenharia Tecidual , Transplante Heterólogo , Animais , Bovinos , Reagentes de Ligações Cruzadas , Iridoides/farmacologia , Teste de Materiais/métodos , Engenharia Tecidual/métodosRESUMO
Further progress in regenerative medicine and bioengineering highly depends on the development of 3D polymeric scaffolds with active biological properties. The most attention is paid to natural extracellular matrix components, primarily collagen. Herein, nonwoven nanofiber materials with various degrees of collagen denaturation and fiber diameters 250-500 nm were produced by electrospinning, stabilized by genipin, and characterized in detail. Collagen denaturation has been confirmed using DSC and FTIR analysis. The comparative study of collagen and gelatin nonwoven materials (NWM) revealed only minor differences in their biocompatibility with skin fibroblasts and keratinocytes in vitro. In long-term subcutaneous implantation study, the inflammation was less evident on collagen than on gelatin NWM. Remarkably, the pronounced calcification was revealed in the collagen NWM only. The results obtained can be useful in terms of improving the electrospinning technology of collagen from aqueous solutions, as well as emphasize the importance of long-term study to ensure proper implementation of the material, taking into account the ability of collagen to provoke calcification.
Assuntos
Nanofibras , Alicerces Teciduais , Gelatina/farmacologia , Engenharia Tecidual/métodos , Colágeno/farmacologiaRESUMO
Enhancement of cell adhesion and growth on surface of the biodegradable materials is one of the important tasks in development of materials for regenerative medicine. This work focuses on comparison of various methods of collagen coating deposition onto polylactide films, aiming to increase their biocompatibility with human mesenchymal stromal cells. The collagen deposition was realized using either preliminary plasma treatment of the polylactide films or pre-swelling in solvent mixture. These techniques were compared in terms of the effect on the surface's chemical structure, morphology, hydrophilicity and ability to support adhesion and growth of human mesenchymal stromal cells.
RESUMO
Bioprosthetic materials based on mammalian pericardium tissue are the gold standard in reconstructive surgery. Their application range covers repair of rectovaginal septum defects, abdominoplastics, urethroplasty, duraplastics, maxillofacial, ophthalmic, thoracic and cardiovascular reconstruction, etc. However, a number of factors contribute to the success of their integration into the host tissue including structural organization, mechanical strength, biocompatibility, immunogenicity, surface chemistry, and biodegradability. In order to improve the material's properties, various strategies are developed, such as decellularization, crosslinking, and detoxification. In this review, the existing issues and long-term achievements in the development of bioprosthetic materials based on the mammalian pericardium tissue, aimed at a wide-spectrum application in reconstructive surgery are analyzed. The basic technical approaches to preparation of biocompatible forms providing continuous functioning, optimization of biomechanical and functional properties, and clinical applicability are described.
Assuntos
Materiais Biocompatíveis , Pericárdio , Engenharia Tecidual , Animais , Humanos , Mamíferos , Próteses e Implantes/normas , Transplante HeterólogoRESUMO
For efficient manufacturing of fibrous collagen-based materials by electrospinning, the search on optimal rheological parameters is of the great importance. Rheological characteristics and denaturation of collagen in aqueous dispersions were studied as a function of shear rate and acetic acid concentration in the range of 3-9% w/w at temperature from 20 to 40°C. It was shown that an increase in temperature, acetic acid concentration of the collagen dispersion leads to a significant decrease in its viscosity. It was found that helical conformation of the collagen macromolecules is preserved up to 31°C. An increase in acetic acid concentration leads to a reduction of denaturation temperature. The complex viscosity of collagen dispersions exhibits a sharp drop, followed by a rapid growth of damping factor in the temperature range from 22 to 35°C. Both storage (G') and loss (Gâ³) moduli increase with frequency and collagen concentration. It was revealed that optimal parameters for electrospinning of highly concentrated collagen dispersions can be achieved by adjusting of the concentration of acetic acid, temperature, and stirring speed. As a result, collagen nonwoven materials with diameter from 100 to 700 nm were obtained. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 107A: 312-318, 2019.
Assuntos
Colágeno Tipo I/química , Nanofibras/química , Animais , Bovinos , Colágeno Tipo I/ultraestrutura , Nanofibras/ultraestrutura , Conformação Proteica em alfa-Hélice , Desnaturação Proteica , Reologia , Temperatura , ViscosidadeRESUMO
Graft-copolymers based on bioresorbable synthetic (oligo-/polylactide) and natural (chitosan and collagen/gelatin) components were synthesized through solid-state reactive co-extrusion and used for fabrication of fibrous non-woven mats via the electrospinning technique. The effect of the macromolecular features of the initial components on the copolymer characteristics was evaluated using FTIR-spectroscopy, differential scanning calorimetry and elemental analysis. Dynamic light scattering analysis showed that the copolymers have a tendency to form stable ultra-fine dispersions with a mean size of macromolecular aggregates of 150 nm within chlorinated solvents. The copolymer-containing non-woven fibrous mats were fabricated via an electrospinning procedure using chloroform as a solvent. An effect of the copolymer composition on the casting solution's viscosity, conductivity and surface tension was evaluated. Scanning electron microscopy showed that the obtained mats consist of randomly distributed fibers with a mean size of â¼5 µm and a more complex morphology than mats fabricated from neat polylactide. The proposed mechanochemical approach to obtain hybrid copolymeric compositions differs from typical liquid-phase methods in terms of high efficiency, simplicity and cleanness.