Immediate bond performance of resin composite luting systems to saliva-contaminated enamel and dentin in different curing modes.

The purpose of this study was to evaluate the immediate shear bond strength of resin composite luting systems to tooth with or without saliva contamination in different curing modes. The Knoop hardness number of the resin composite luting agents was measured. Four combinations of resin composite luting systems were used. The shear bond strength to bovine teeth was measured with and without saliva contamination in different curing modes at different storage periods. The Knoop hardness number of the resin composite luting agents was also evaluated. Significantly lower enamel and dentin shear bond strengths and Knoop hardness number values were observed in all resin composite luting systems at 5 min versus 24 h, regardless of the curing mode or saliva contamination. The influence of the curing mode of the resin composite luting systems on shear bond strengths and Knoop hardness number was dependent on material. For the saliva contamination conditions, only G-CEM ONE EM did not show any significant difference in shear bond strength among the groups with and without saliva contamination, regardless of curing mode, storage period, or tooth substrate. All the resin composite luting systems showed lower shear bond strengths and Knoop hardness number values immediately after setting.

Evaluation of the effect of a glass ionomer cement containing fluoro-zinc-silicate glass on dentin remineralization using the ultrasonic pulse-echo method.

The purpose of this study was to investigate the protective effect of a glass ionomer cement (GIC) consisting of fluoro-zinc-silicate glass on the demineralization of bovine dentin using the ultrasonic pulse-echo method. The findings were compared with those obtained using a conventional GIC. Slabs of dentin from bovine teeth were sliced, shaped into a rectangular form, and immersed in 0.5 M ethylenediaminetetraacetic acid solution at 25ºC for 6 days, followed by storage in distilled water for 3 days. After demineralization, they were immersed in artificial saliva with and without the GIC specimens. The propagation times of the longitudinal ultrasonic waves in the samples were measured. The ultrasonic velocities of the fluoro-zinc-silicate glass-containing GICs were significantly increased 2-3 days after the start of the experiment and showed an upward trend thereafter. These findings indicate that the GICs containing fluoro-zinc-silicate glass might exhibit the potential to promote remineralization in the dentin.

Early Phase Enamel Bond Performance of a Two-step Adhesive Containing a Primer Derived from a Universal Adhesive.

PURPOSE: To investigate the changes in the enamel bond performance of a two-step adhesive containing a primer derived from a universal adhesive in the early phase before 24 h and compare them to those of other adhesives. The Knoop hardness number (KHN) of the cured adhesive layers and resin composite was measured. MATERIALS AND METHODS: A new two-step adhesive using universal adhesive technology, G2-Bond Universal, was tested. Two conventional two-step adhesives, Clearfil SE Bond 2 and OptiBond eXTRa, and an established universal adhesive, Scotchbond Universal Plus Adhesive, were used as comparison materials. Twelve specimens per group were used to measure the shear bond strength (SBS) to bovine enamel in different etching modes. The bonded specimens were stored in distilled water at 37°C for 5 min or 1, 6, 12, or 24 h before SBS testing. The KHN of the adhesive layer and resin composite was determined after the same storage periods as for SBS testing. RESULTS: All adhesives exhibited increased SBS with prolonged storage periods, irrespective of the etching mode. The KHN of the adhesive layer and resin composite increased over time. CONCLUSIONS: There were strong positive correlations between the SBS and KHN of the adhesive layer and resin composite. Phosphoric acid pre-etching of enamel effectively increases enamel bond performance. The two-step adhesive G2-Bond Universal demonstrated significantly higher bond strength in the early phase than the other adhesives in self-etch mode.