RESUMO
We report the synthesis, fabrication and extensive characterization of a visible-blind photodetector based on p-i-n junction GaN nanowire ensembles. The nanowires were grown by plasma-assisted molecular beam epitaxy on an n-doped Si(111) substrate, encapsulated into a spin-on-glass and processed using dry etching and metallization techniques. The detector presents a high peak responsivity of 0.47 A W(-1) at - 1 V. The spectral response of the detector is restricted to the UV range with a UV-to-visible rejection ratio of 2 x 10(2). The dependence on the incident power and the operation speed of the photodetector are discussed.
RESUMO
We analyze the thermal behavior of a flexible nanowire (NW) light-emitting diode (LED) operated under different injection conditions. The LED is based on metal-organic vapor-phase deposition (MOCVD)-grown self-assembled InGaN/GaN NWs in a polydimethylsiloxane (PDMS) matrix. Despite the poor thermal conductivity of the polymer, active nitride NWs effectively dissipate heat to the substrate. Therefore, the flexible LED mounted on a copper heat sink can operate under high injection without significant overheating, while the device mounted on a plastic holder showed a 25% higher temperature for the same injected current. The efficiency of the heat dissipation by nitride NWs was further confirmed with finite-element modeling of the temperature distribution in a NW/polymer composite membrane.
RESUMO
Gallium nitride [GaN] nanorods grown on a Si(111) substrate at 720°C via plasma-assisted molecular beam epitaxy were studied by field-emission electron microscopy and cathodoluminescence [CL]. The surface topography and optical properties of the GaN nanorod cluster and single GaN nanorod were measured and discussed. The defect-related CL spectra of GaN nanorods and their dependence on temperature were investigated. The CL spectra along the length of the individual GaN nanorod were also studied. The results reveal that the 3.2-eV peak comes from the structural defect at the interface between the GaN nanorod and Si substrate. The surface state emission of the single GaN nanorod is stronger as the diameter of the GaN nanorod becomes smaller due to an increased surface-to-volume ratio.