RESUMO
We report on the static and dynamic magnetic properties of W/CoFeB/Ta/CoFeB/MgO stacks, where the CoFeB layer is split in two by a 0.3 nm-thick Ta "dusting" layer. A total CoFeB thickness between 1.2 and 2.4 nm is studied. Perpendicular magnetic anisotropy is obtained for thickness below 1.8 nm even at the as-deposited stacks, and it is enhanced after annealing. Saturation magnetization is 1520 (1440) kA/m before (after) annealing, increased compared to non-split CoFeB layers. Ferromagnetic resonance measurements show that high magnetic anisotropy energy may be achieved (effective anisotropy field 0.571 ± 0.003 T), combined to a moderate Gilbert damping (0.030 ± 0.001). We argue that the above characteristics make the split-CoFeB system advantageous for spintronics applications.
RESUMO
We present experimental work that reveals the benefits of performing magnetic force microscopy measurements employing the torsional resonance mode of cantilever oscillation. This approach provides two clear advantages: the ability of performing magnetic imaging without topography-related interference and the significant lateral resolution improvement (approximately 15%). We believe that this work demonstrates a significant improvement to a versatile magnetic imaging technique widely used in academia and in industry.
Assuntos
Magnetismo/instrumentação , Microscopia de Força Atômica/instrumentação , Desenho de Equipamento , Propriedades de Superfície , Torção MecânicaRESUMO
The fct L10-FeNi alloy is a promising candidate for the development of high performance critical-elements-free magnetic materials. Among the different materials, the Au-Cu-Ni alloy has resulted very promising; however, a detailed investigation of the effect of the buffer-layer composition on the formation of the hard FeNi phase is still missing. To accelerate the search of the best Au-Cu-Ni composition, a combinatorial approach based on High-Throughput (HT) experimental methods has been exploited in this paper. HT magnetic characterization methods revealed the presence of a hard magnetic phase with an out-of-plane easy-axis, whose coercivity increases from 0.49 kOe up to 1.30 kOe as the Au content of the Cu-Au-Ni buffer-layer decreases. Similarly, the out-of-plane magneto-crystalline anisotropy energy density increases from 0.12 to 0.35 MJ/m3. This anisotropy is attributed to the partial formation of the L10 FeNi phase induced by the buffer-layer. In the range of compositions we investigated, the buffer-layer structure does not change significantly and the modulation of the magnetic properties with the Au content in the combinatorial layer is mainly related to the different nature and extent of interlayer diffusion processes, which have a great impact on the formation and order degree of the L10 FeNi phase.