Lubrication Properties of Ammonium-Based Ionic Liquids Confined between Silica Surfaces Using Resonance Shear Measurements.

To evaluate the friction properties of new lubrication systems, two types of ammonium-based ionic liquids (ILs), N,N-diethyl-N-methyl-N-(2-methoxyethyl) ammonium tetrafluoroborate ([DEME][BF4]) and N,N-diethyl-N-methyl-N-(2-methoxyethyl) ammonium bis(trifluoromethanesulfonyl) imide ([DEME][TFSI]), were investigated by resonance shear measurements (RSM) and reciprocating type tribotests between silica (glass) surfaces. RSM revealed that an IL layer of ca. 2 nm in thickness was maintained between the silica surfaces under an applied load of 0.40 mN ∼ 1.2 mN. The relative intensity of the RMS signal indicated that the friction of the system was lower for [DEME][BF4], 0.12, than that of [DEME][TFSI], 0.18. On the other hand, the friction coefficients µk obtained from the tribotests of [DEME][BF4] were lower than that of [DEME][TFSI] for sliding velocities in the range of 5.0 × 10(-4) m s(-1) to 3.0 × 10(-2) m s(-1) under applied loads of 196-980 mN. The friction coefficients obtained by the tribotest are discussed with reference to the RSM results.

Albumin Hydrogel-Coated Mesoporous Silica Nanoparticle as a Carrier of Cationic Porphyrin and Ratiometric Fluorescence pH Sensor.

Here, we report that a mesoporous silica nanoparticle (MSN) coated with a fluoresceine-labeled bovine serum albumin (F-BSA) hydrogel layer works as a temperature-responsive nanocarrier for tetrakis-N-methylpyridyl porphyrin (TMPyP) and as a fluorescence ratiometric pH probe. F-BSA hydrogel-coated MSN containing TMPyP (F-BSA/MSN/TMPyP) was synthesized by thermal gelation of denatured F-BSA on the external surface of MSN. The F-BSA hydrogel layer was composed of an inner hard corona layer and an outer soft layer and was stable under physiological conditions. F-BSA/MSN/TMPyP exhibited temperature-dependent exponential release of TMPyP. In this release profile, the MSN was found to be a suitable host for stable encapsulation of tetracationic TMPyP by electrostatic interactions, and the F-BSA hydrogel layer mediated the diffusion of TMPyP from the MSN pore interior into the solution phase. Increasing temperature promoted partitioning of TMPyP from the pore interior to the F-BSA hydrogel layer, from where it was spontaneously released into the bulk solution phase by cation exchange. F-BSA/MSN/TMPyP also gave a linear ratiometric fluorescence response (1.3 per pH unit) in the pH range from 6.1 to 8.9.

Protein Condensation at Nanopore Entrances as Studied by Differential Scanning Calorimetry and Small-Angle Neutron Scattering.

The condensation of globular myoglobin (Mb) at the pore entrances of mesoporous silica (MPS) with a series of pore diameters (4.2, 6.4, 7.7, and 9.0 nm) was examined by differential scanning calorimetry (DSC) and contrast-matching small-angle neutron scattering (CM-SANS) experiments. The DSC measurements were performed to estimate the amount of Mb adsorbed at two different adsorption sites, namely, the pore interior and the pore entrance regions. The CM-SANS measurements were conducted to observe condensation of Mb molecules at the pore entrance regions. Notably, the nanopore entrance with a diameter close to twice that of the Mb diameter was found to be the specific cavity to facilitate the condensation of globular Mb. The Mb condensation occurred at the entrances of the 6.4 nm pore during the adsorption uptake from concentrated Mb solutions, whereas the adsorption uptake from diluted Mb solutions induced the condensation of Mb at the entrances of the 7.7 nm pore.

Mechanical and Lubrication Properties of Double Network Ion Gels Obtained by a One-Step Process.

Human joints support us to reduce the impact on our body and move them smoothly. As they are composed of gel-like structures, gel materials with soft and resilient properties are expected, as lubricants, to provide high efficiency and a long lifetime for mechanical parts. While double network gels including ionic liquids as swelling agents possess high mechanical strength and stable low friction under high temperature or vacuum, their fabrication process is complex and time-consuming. In this study, we applied one-pot synthesis to a double network ion gel (DNIG) to obtain a thin gel film by a simple coating method and examined its thermal, mechanical and tribological properties. The DNIG was obtained by one-pot synthesis (DNIG-1) combining polycondensation of tetraethoxysilane and radical polymerization of methyl methacrylate to form silica and poly(methyl methacrylate) as a 1st and 2nd network, respectively. Such obtained DNIG-1 was characterized and compared with DNIG obtained by a conventional two-step process (DNIG-2). Thermogravimetric analysis and the compressive stress-strain test showed high thermal stability and mechanical strength of DNIG-1. As friction at the glass/DNIG-1 interface showed high friction compared with that at glass/DNIG-2, various counterface materials were applied to examine their effect on the friction of DNIG-1. As SUS304/DNIG-1 showed much lower friction compared with glass/DNIG-1, the difference in the friction was presumably due to the different adsorption forces and compatibility between the materials.

Electrical Stimuli-Responsive Decomposition of Layer-by-Layer Films Composed of Polycations and TEMPO-Modified Poly(acrylic acid).

We previously reported that layer-by-layer (LbL) film prepared by a combination of 2,2,6,6-tetramethylpiperidinyl N-oxyl (TEMPO)-modified polyacrylic acid (PAA) and polyethyleneimine (PEI) were decomposed by application of an electric potential. However, there have been no reports yet for other polycationic species. In this study, LbL films were prepared by combining various polycationics (PEI, poly(allylamine hydrochloride) (PAH), poly(diallydimethylammonium chloride) (PDDA), and polyamidoamine (PAMAM) dendrimer) and TEMPO-PAA, and the decomposition of the thin films was evaluated using cyclic voltammetry (CV) and constant potential using an electrochemical quartz crystal microbalance (eQCM). When a potential was applied to an electrode coated on an LbL thin film of polycations and TEMPO-PAA, an oxidation potential peak (Epa) was obtained around +0.6 V vs. Ag/AgCl in CV measurements. EQCM measurements showed the decomposition of the LbL films at voltages near the Epa of the TEMPO residues. Decomposition rate was 82% for the (PEI/TEMPO-PAA)5 film, 52% for the (PAH/TEMPO-PAA)5 film, and 49% for the (PDDA/TEMPO-PAA)5 film. It is considered that the oxoammonium ion has a positive charge, and the LbL films were decomposed due to electrostatic repulsion with the polycations (PEI, PAH, and PDDA). These LbL films may lead to applications in drug release by electrical stimulation. On the other hand, the CV of the (PAMAM/TEMPO-PAA)5 film did not decompose. It is possible that the decomposition of the thin film is not promoted, probably because the amount of TEMPO-PAA absorbed is small.

Acid-base equilibria inside amine-functionalized mesoporous silica.

Acid-base equilibria and effective proton concentration inside a silica mesopore modified with a trimethyl ammonium (TMAP) layer were studied by steady-state fluorescence experiments. The mesoporous silica with a dense TMAP layer (1.4 molecules/nm(2)) was prepared by a post grafting of N-trimethoxysilylpropyl-N,N,N-trimethylammonium at surfactant-templated mesoporous silica (diameter of silica framework =3.1 nm). The resulting TMAP-modified mesoporous silica strongly adsorbed of anionic fluorescence indicator dyes (8-hydroxypyrene-1,3,6-trisulfonate (pyranine), 8-aminopyrene-1,3,6-trisulfonate (APTS), 5,10,15,20-tetraphenyl-21H,23H-porphinetetrasulfonic acid disulfuric acid (TPPS), 2-naphthol-3,6-disulfonate (2NT)) and fluorescence excitation spectra of these dyes within TMAP-modified mesoporous silica were measured by varying the solution pH. The fluorescence experiments revealed that the acid-base equilibrium reactions of all pH indicator dyes within the TMAP-modified silica mesopore were quite different from those in bulk water. From the analysis of the acid-base equilibrium of pyranine, the following relationships between solution pH (pH(bulk)) and the effective proton concentration inside the pore (pH(pore)) were obtained: (1) shift of pH(pore) was 1.8 (ΔpH(pore)=1.8) for the pH(bulk) change from 2.1 to 9.1 (ΔpH(bulk)=7.0); (2) pH(pore) was not simply proportional to pH(bulk); (3) the inside of the TMAP-modified silica mesopore was suggested to be in a weak acidic or neutral condition when pH(bulk) was changed from 2.0 to 9.1. Since these relationships between pH(bulk) and pH(pore) could explain the acid-base equilibria of other pH indicator dyes (APTS, TPPS, 2NT), these relationships were inferred to describe the effective proton concentration inside the TMAP-modified silica mesopore.

In Situ Surface-Initiated Atom-Transfer Radical Polymerization Utilizing the Nonvolatile Nature of Ionic Liquids: A First Attempt.

In this paper, in situ surface-initiated atom-transfer radical polymerization (SI-ATRP) based on both an open and a coated system, without using volatile reagents, was developed to overcome the limited usage of ATRP due to the necessity of sealing. Nonvolatile ionic liquid (IL)-type components were used, specifically N,N-diethyl-N-(2-methacryloylethyl)-N-methylammonium bis(trifluoromethylsulfonyl)imide as the polymerizable monomer and N,N-diethylmethyl(2-methoxyethyl)ammonium bis(trifluoromethylsulfonyl)imide as the polymerization solvent. In the experiment, the reversible-deactivation radical polymerization characteristics are properly ensured in nonvolatile ATRP solution coated on silicon wafer as thin liquid film, to form concentrated polymer brushes (CPBs). The average molecular weight and molecular-weight distribution of the polymer produced in the liquid film and formed on silicon wafer were measured by gel permeation chromatography, which confirms that the polymerization reaction occurred as designed. Furthermore, it is clarified that the surface of the polymer brush synthesized in situ swollen by IL also exhibited low friction characteristics, comparable to that synthesized in a typical immersion process. This paper is the first to establish the effectiveness of in situ preparation for CPBs by using the coating technique.

Adsorption and Release of Rose Bengal on Layer-by-Layer Films of Poly(Vinyl Alcohol) and Poly(Amidoamine) Dendrimers Bearing 4-Carboxyphenylboronic Acid.

Phenylboronic acid-bearing polyamidoamine dendrimer (PBA-PAMAM)/poly(vinyl alcohol) (PVA) multilayer films were prepared through the layer-by-layer (LbL) deposition of PBA-PAMAM solution and PVA solution. PBA-PAMAM/PVA films were constructed successfully through the formation of boronate ester bonds between the boronic acid moiety in PBA and 1,3-diol units in PVA. When the (PBA-PAMAM/PVA)5 films were immersed in rose bengal (RB) solution, RB was adsorbed onto the LbL films. The amount of RB adsorbed was higher in the LbL films immersed in acidic solution than in basic solution. The release of RB from the LbL films was also promoted in the basic solution, while it was suppressed in the acidic solution. The boronic acid ester is oxidized to phenol by hydrogen peroxide (H2O2) and the carbon-boron bond is cleaved, so that the (PBA-PAMAM/PVA)5 films can be decomposed by immersion in H2O2 solution. Therefore, when RB-adsorbed (PBA-PAMAM/PVA)5 films were immersed in H2O2 solution, the release of RB was moderately promoted when the solution was weakly acidic.

Decomposition of Glucose-Sensitive Layer-by-Layer Films Using Hemin, DNA, and Glucose Oxidase.

Glucose-sensitive films were prepared through the layer-by-layer (LbL) deposition of hemin-modified poly(ethyleneimine) (H-PEI) solution and DNA solution (containing glucose oxidase (GOx)). H-PEI/DNA + GOx multilayer films were constructed using electrostatic interactions. The (H-PEI/DNA + GOx)5 film was then partially decomposed by hydrogen peroxide (H2O2). The mechanism for the decomposition of the LbL film was considered to involve more reactive oxygen species (ROS) that were formed by the reaction of hemin and H2O2, which then caused nonspecific DNA cleavage. In addition, GOx present in the LbL films reacts with glucose to generate hydrogen peroxide. Therefore, decomposition of the (H-PEI/DNA + GOx)5 film was observed when the thin film was immersed in a glucose solution. (H-PEI/DNA + GOx)5 films exposed to a glucose solution for periods of 24, 48 72, and 96 h indicated that the decomposition of the film increased with the time to 9.97%, 16.3%, 23.1%, and 30.5%, respectively. The rate of LbL film decomposition increased with the glucose concentration. At pH and ionic strengths close to physiological conditions, it was possible to slowly decompose the LbL film at low glucose concentrations of 1-10 mM.

Solvation dynamics of coumarin 153 in alcohols confined in silica nanochannels.

Solvation dynamics in alcohols confined in silica nanochannels was examined by time-resolved fluorescence spectroscopy using coumarin 153 (C153) as a fluorescent probe. Surfactant-templated mesoporous silica was fabricated inside the pores of an anodic alumina membrane. The surfactant was removed by calcination to give mesoporous silica (Cal-NAM) containing one-dimensional (1D) silica nanochannels (diameter, 3.1 nm) whose inner surface was covered with silanol groups. By treating Cal-NAM with trimethylchlorosilane, trimethylsilyl (TMS) groups were formed on the inner surface of the silica nanochannels (TMS-NAM). Fluorescence dynamic Stokes shifts of C153 were measured in alcohols (ethanol, butanol, hexanol, and decanol) confined in the silica nanochannels of Cal- and TMS-NAMs, and the time-dependent fluorescence decay profiles could be best fitted by a biexponential function. The estimated solvent relaxation times were much larger than those observed in bulk alcohols for both Cal- and TMS-NAMs when ethanol or butanol was used as a solvent, indicating that the mobility of these alcohol molecules was restricted within the silica nanochannels. However, hexanol or decanol in Cal- and TMS-NAMs did not cause a remarkable increase in the solvent relaxation time in contrast to ethanol or butanol. Therefore, it was concluded that a relatively rigid assembly of alcohols (an alcohol chain) was formed within the silica nanochannels by hydrogen bonding interaction and van der Waals force between the surface functional groups of the silica nanochannels and alcohol molecules and by the successive interaction between alcohol molecules when alcohol with a short alkyl chain (ethanol or butanol) was used as a solvent.

Synthesis of Monodisperse Silica Particles Grafted with Concentrated Ionic Liquid-Type Polymer Brushes by Surface-Initiated Atom Transfer Radical Polymerization for Use as a Solid State Polymer Electrolyte.

A polymerizable ionic liquid, N,N-diethyl-N-(2-methacryloylethyl)-N-methylammonium bis(trifluoromethylsulfonyl)imide (DEMM-TFSI), was polymerized via copper-mediated atom transfer radical polymerization (ATRP). The polymerization proceeded in a living manner producing well-defined poly(DEMM-TFSI) of target molecular weight up to about 400 K (including a polycation and an counter anion). The accurate molecular weight as determined by a GPC analysis combined with a light scattering measurement, and the molecular weight values obtained exhibited good agreement with the theoretical values calculated from the initial molar ratio of DEMM-TFSI and the monomer conversion. Surface-initiated ATRP on the surface of monodisperse silica particles (SiPs) with various diameters was successfully performed, producing SiPs grafted with well-defined poly(DEMM-TFSI) with a graft density as high as 0.15 chains/nm². Since the composite film made from the silica-particle-decorated polymer brush and ionic liquid shows a relatively high ionic conductivity, we have evaluated the relationship between the grafted brush chain length and the ionic conductivity.

Functionalization of mesoporous silica membrane with a Schiff base fluorophore for Cu(II) ion sensing.

A Schiff base (SB) immobilized hybrid mesoporous silica membrane (SB-HMM) was prepared by immobilizing a Schiff base onto the pore surface of mesoporous silica (pore size=3.1 nm) embedded in the pores of a porous anodic alumina membrane. In contrast to the non-fluorescent analogous SB molecule in homogeneous solutions, SB-HMM exhibited intense fluorescence due to emission enhancement caused by aggregation of SB groups on the pore surface. The high quantum efficiency of the surface SB groups allows SB-HMM to function as a fluorescent sensor for Cu(II) ions in an aqueous solution with good sensitivity, selectivity and reproducibility. Under the optimal conditions described, the linear ranges of fluorescence intensity for Cu(II) are 1.2-13.8(M (R(2)=0.993) and 19.4-60 (R(2)=0.992) (M. The limit of detection for Cu(II) is 0.8 µM on basis of the definition by IUPAC (C(LOD)=3.3S(b)/m).