The Effect of the Modification of Carbon Spheres with ZnCl2 on the Adsorption Properties towards CO2.

Zinc chloride and potassium oxalate are often applied as activating agents for carbon materials. In this work, we present the preparation of ZnO/carbon spheres composites using resorcinol-formaldehyde resin as a carbon source in a solvothermal reactor heated with microwaves. Zinc chloride as a zinc oxide source and potassium oxalate as an activating agent were applied. The effect of their addition and preparation conditions on the adsorption properties towards carbon dioxide at 0 °C and 25 °C were investigated. Additionally, for all tested sorbents, the CO2 sorption tests at 40 °C, carried out utilizing a thermobalance, confirmed the trend of sorption capacity measured at 0 and 25 °C. Furthermore, the sample activated using potassium oxalate and modified using zinc chloride (a carbon-to-zinc ratio equal to 10:1) displayed not only a high CO2 adsorption capacity (2.69 mmol CO2/g at 40 °C) but also exhibited a stable performance during the consecutive multicycle adsorption-desorption process.

CO2 Sorbents Based on Spherical Carbon and Photoactive Metal Oxides: Insight into Adsorption Capacity, Selectivity and Regenerability.

This work aimed to obtain hybrid composites based on photoactive metal oxide and carbon having adsorption properties. The materials, composed of titanium dioxide or zinc oxide and spherical carbon, were obtained from resorcinol-formaldehyde resin, treated in a solvothermal reactor heated with microwaves and then subjected to carbonization, were received. The functional groups of pure carbon spheres (unsaturated stretching C=C, stretching C-OH and C-H bending vibrations), CS/ZnO and CS/TiO2 samples were determined by FT-IR analysis. The characteristic bands for ZnO and TiO2 were observed below 1000 cm-1. The thermal oxidative properties are similar for TiO2- and ZnO-modified carbon spheres. We have observed that the increased carbon sphere content in nanocomposites results in starting the decomposition process at a lower temperature, therefore, nanocomposites have a broader combustion temperature range. The effect of the oxides' addition to carbon spheres on their adsorption properties was evaluated in detail by examining CO2 adsorption from the gas phase. The selectivity of CO2 over N2 at a temperature of 25 °C and pressure of 1 bar (a novelty in testing CS-based sorbents) calculated for 3.00 CS/TiO2 and 4.00 CS/ZnO was 15.09 and 16.95, respectively. These nanocomposites exhibit excellent cyclic stability checked over 10 consecutive adsorption-desorption cycles.

Antibacterial properties of TiO2 modified with reduced graphene oxide.

In this paper, the antibacterial activity of titanium dioxide modified with reduced graphene oxide (rGO) was presented. TiO2/rGO photocatalysts were prepared by the hydrothermal method under elevated pressure at 180°C and heated at 100°C in Ar flow. The obtained photocatalysts were characterized by means of XRD, FTIR/DRS, UV-vis/DR, Raman spectroscopy and scanning electron microscopy (SEM). The carbon content was also examined. FTIR/DRS and Raman analysis confirmed the presence of rGO in the TiO2 structure, suggesting a successful modification. The antimicrobial photoactivity of photocatalysts was conducted against E. coli under an artificial solar light. The results show that all TiO2/rGO photocatalysts exhibited an antibacterial activity higher than unmodified TiO2. The best result was found for sample with 1.5wt% additive of reduced graphene oxide. In this case, total inactivation of E. coli was noticed after 75min of irradiation. It was found that the presence of rGO in sample improves the antimicrobial activity.

On the Selectivity of Simultaneous CO2 and N2 Reduction Using TiO2/Carbon Sphere Photocatalysts Prepared by Microwave Treatment and Mounted on Silica Cloth.

This paper presents new photocatalysts obtained by treating carbon spheres (CS) and TiO2 in a microwave reactor at a pressure of 20 atm and a temperature of up to 300 °C for 15 min and then depositing TiO2/CS composites on glass fibre cloths. Such highly CO2-adsorbing photocatalysts showed photoactivity in the simultaneous water-splitting process, generating H2, reducing CO2 to CO and CH4, and reducing N2 to NH3. In addition, calculations of the hydrogen balance involved in all reactions were performed. Adding 1 g of carbon spheres per 1 g of TiO2 maintained the high selectivity of nitrogen fixation at 95.87-99.5%, which was continuously removed from the gas phase into the water as NH4+ ions.

New Insight on Carbon Dioxide-Mediated Hydrogen Production.

A new approach to hydrogen production from water is described. This simple method is based on carbon dioxide-mediated water decomposition under UV radiation. The water contained dissolved sodium hydroxide, and the solution was saturated with gaseous carbon dioxide. During saturation, the pH decreased from about 11.5 to 7-8. The formed bicarbonate and carbonate ions acted as scavengers for hydroxyl radicals, preventing the recombination of hydroxyl and hydrogen radicals and prioritizing hydrogen gas formation. In the presented method, not yet reported in the literature, hydrogen production is combined with carbon dioxide. For the best system with alkaline water (0.2 m NaOH) saturated with CO2 under UV-C, the hydrogen production amounted to 0.6 µmol h-1 during 24 h of radiation.

ZnO/Carbon Spheres with Excellent Regenerability for Post-Combustion CO2 Capture.

This paper examines the synthesis of the ZnO/carbon spheres composites using resorcinol-formaldehyde resin as a carbon source and zinc nitrate as a zinc oxide source in a solvothermal reactor heated with microwaves. The influence of activation with potassium oxalate and modification with zinc nitrate on the physicochemical properties of the obtained materials and CO2 adsorption capacity was investigated. It was found that in the case of nonactivated material as well as activated materials, the presence of zinc oxide in the carbon matrix had no effect or slightly increased the values of CO2 adsorption capacity. Only for the material where the weight ratio of carbon:zinc was 2:1, the decrease of CO2 adsorption capacity was reported. Additionally, CO2 adsorption experiments on nonactivated carbon spheres and those activated with potassium oxalate with different amounts of zinc nitrate were carried out at 40 °C using thermobalance. The highest CO2 adsorption capacity at temperature 40 °C (2.08 mmol/g adsorbent) was achieved for the material after activation with potassium oxalate with the highest zinc nitrate content as ZnO precursor. Moreover, repeated adsorption/desorption cycle experiments revealed that the as-prepared carbon spheres were very good CO2 adsorbents, exhibiting excellent cyclic stability with a performance decay of less than 10% over up to 25 adsorption-desorption cycles.

Assessment of the Suitability of the One-Step Hydrothermal Method for Preparation of Non-Covalently/Covalently-Bonded TiO2/Graphene-Based Hybrids.

A hybrid nanocomposites containing nanocrystalline TiO2 and graphene-related materials (graphene oxide or reduced graphene oxide) were successfully prepared by mechanical mixing and the hydrothermal method in the high-pressure atmosphere. The presented X-ray photoelectron spectroscopy (XPS) study and quantitative elemental analysis confirm similar content of carbon in graphene oxide GO (52 wt% and 46 wt%, respectively) and reduced graphene oxide rGO (92 wt% and 98 wt%, respectively). No chemical interactions between TiO2 and GO/rGO was found. TiO2 nanoparticles were loaded on GO or rGO flakes. However, Fourier transform infrared-diffuse reflection spectroscopy (FTIR/DRS) allowed finding peaks characteristic of GO and rGO. XPS study shows that since the concentration of TiO2 in the samples was no less than 95 wt%, it was assumed that the interactions between TiO2 and graphene should not influence the lower layers of titanium atoms in the TiO2 and they occurred as Ti4+ ions. Hydrothermal treatment at 200 °C did not cause the reduction of GO to rGO in TiO2-GO nanocomposites. In general, the one-step hydrothermal method must be considered to be inefficient for preparation of chemically-bonded composites synthesized from commercially available TiO2 and unfunctionalized graphene sheets obtained from graphite powder.