RESUMO
OBJECTIVES: Our primary aim was to describe migration of the Exeter stem with a 32 mm head on highly crosslinked polyethylene and whether this is influenced by age. Our secondary aims were to assess functional outcome, satisfaction, activity, and bone mineral density (BMD) according to age. PATIENTS AND METHODS: A prospective cohort study was conducted. Patients were recruited into three age groups: less than 65 years (n = 65), 65 to 74 years (n = 68), and 75 years and older (n = 67). There were 200 patients enrolled in the study, of whom 115 were female and 85 were male, with a mean age of 69.9 years (sd 9.5, 42 to 92). They were assessed preoperatively, and at three, 12 and, 24 months postoperatively. Stem migration was assessed using Einzel-Bild-Röntgen-Analyse (EBRA). Western Ontario and McMaster Universities Osteoarthritis Index (WOMAC), Harris Hip Score (HHS), Hip Disability and Osteoarthritis Outcome Score (HOOS), EuroQol-5 domains questionnaire (EQ-5D), short form-36 questionnaire (SF-36,) and patient satisfaction were used to assess outcome. The Lower Extremity Activity Scale (LEAS), Timed Up and Go (TUG) test, and activPAL monitor (energy expelled, time lying/standing/walking and step count) were used to assess activity. The BMD was assessed in Gruen and Charnley zones. RESULTS: Mean varus/valgus tilt was -0.77° and axial subsidence was -1.20 mm. No significant difference was observed between age groups (p ⩾ 0.07). There was no difference according to age group for postoperative WOMAC (p ⩾ 0.11), HHS (p ⩾ 0.06), HOOS (p ⩾ 0.46), EQ-5D (p ⩾ 0.38), patient satisfaction (p ⩾ 0.05), or activPAL (p ⩾ 0.06). Patients 75 years and older had a worse SF-36 physical function (p = 0.01) and physical role (p = 0.03), LEAS score (p < 0.001), a shorter TUG (p = 0.01), and a lower BMD in Charnley zone 1 (p = 0.02). CONCLUSION: Exeter stem migration is within normal limits and is not influenced by age group. Functional outcome, patient satisfaction, activity level, and periprosthetic BMD are similar across all age groups.Cite this article: N. D. Clement, M. Bardgett, K. Merrie, S. Furtado, R. Bowman, D. J. Langton, D. J. Deehan, J. Holland. Cemented Exeter total hip arthroplasty with a 32 mm head on highly crosslinked polyethylene: Does age influence functional outcome, satisfaction, activity, stem migration, and periprosthetic bone mineral density? Bone Joint Res 2019;8:275-287. DOI: 10.1302/2046-3758.86.BJR-2018-0300.R1.
RESUMO
OBJECTIVES: We investigated the reliability of the cobalt-chromium (CoCr) synovial joint fluid ratio (JFR) in identifying the presence of a severe aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL) response and/or suboptimal taper performance (SOTP) following metal-on-metal (MoM) hip arthroplasty. We then examined the possibility that the CoCr JFR may influence the serum partitioning of Co and Cr. METHODS: For part A, we included all revision surgeries carried out at our unit with the relevant data, including volumetric wear analysis, joint fluid (JF) Co and Cr concentrations, and ALVAL grade (n = 315). Receiver operating characteristic curves were constructed to assess the reliability of the CoCr JFR in identifying severe ALVAL and/or SOTP. For part B, we included only patients with unilateral prostheses who had given matched serum and whole blood samples for Co and Cr analysis (n = 155). Multiple regression was used to examine the influence of JF concentrations on the serum partitioning of Co and Cr in the blood. RESULTS: A CoCr JFR > 1 showed a specificity of 83% (77% to 88%) and sensitivity of 63% (55% to 70%) for the detection of severe ALVAL and/or SOTP. In patients with CoCr JFRs > 1, the median blood Cr to serum Cr ratio was 0.99, compared with 0.71 in patients with CoCr JFRs < 1 (p < 0.001). Regression analysis demonstrated that the blood Cr to serum Cr value was positively associated with the JF Co concentration (p = 0.011) and inversely related to the JF Cr concentration (p < 0.001). CONCLUSION: Elevations in CoCr JFRs are associated with adverse biological (severe ALVAL) or tribocorrosive processes (SOTP). Comparison of serum Cr with blood Cr concentrations may be a useful additional clinical tool to help to identify these conditions.Cite this article: D. J. Langton, S. Natu, C. F. Harrington, J. G. Bowsher, A. V. F. Nargol. Is the synovial fluid cobalt-to-chromium ratio related to the serum partitioning of metal debris following metal-on-metal hip arthroplasty? Bone Joint Res 2019;8:146-155. DOI: 10.1302/2046-3758.83.BJR-2018-0049.R1.
RESUMO
OBJECTIVES: We have encountered patients who developed large joint fluid collections with massive elevations in chromium (Cr) and cobalt (Co) concentrations following metal-on-metal (MoM) hip arthroplasties. In some cases, retrieval analysis determined that these ion concentrations could not be explained simply by the wear rates of the components. We hypothesized that these effects may be associated with aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL). PATIENTS AND METHODS: We examined the influence of the ALVAL grade on synovial fluid Co and Cr concentrations following adjustment for patient and device variables, including volumetric wear rates. Initially restricting the analysis to include only patients with one MoM hip resurfacing device, we performed multiple regression analyses of prospectively collected data. We then repeated the same statistical approach using results from a larger cohort with different MoM designs, including total hip arthroplasties. RESULTS: In the resurfacing cohort (n = 76), the statistical modelling indicated that the presence of severe ALVAL and a large fluid collection were associated with greater joint fluid Co concentrations after adjustment for volumetric wear rates (p = 0.005). These findings were replicated in the mixed implant group (n = 178), where the presence of severe ALVAL and a large fluid collection were significantly associated with greater fluid Co concentrations (p < 0.001). CONCLUSION: The development of severe ALVAL is associated with elevations in metal ion concentrations far beyond those expected from the volumetric loss from the prosthetic surfaces. This finding may aid the understanding of the sequence of events leading to soft-tissue reactions following MoM hip arthroplasties.Cite this article: D. J. Langton, R. P. Sidaginamale, T. J. Joyce, J. G. Bowsher, J. P. Holland, D. Deehan, A. V. F. Nargol, S. Natu. Aseptic lymphocyte-dominated vasculitis-associated lesions are related to changes in metal ion handling in the joint capsules of metal-on-metal hip arthroplasties. Bone Joint Res 2018;7:388-396. DOI: 10.1302/2046-3758.76.BJR-2018-0037.
RESUMO
AIMS: There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs. PATIENTS AND METHODS: We examined an existing retrieval database to identify all Exeter V40 and Universal MoP THAs. Volumetric wear analysis of the taper surfaces was conducted using previously validated methodology. These values were compared with those obtained from a series of MoM THAs using non-parametric statistical methodology. A number of patient and device variables were accounted for using multiple regression modelling. RESULTS: A total of 95 Exeter MoP and 249 MoM THAs were examined. The median volumetric loss from the MoM cohort was over four times larger than that from the MoP cohort (1.01 mm3 vs 0.23 mm3, p < 0.001), despite a significantly shorter median period in vivo for the MoM group (48 months vs 90 months, p < 0.001). Multiple regression modelling indicated that the dominant variables leading to greater female taper material loss were bearing diameter (p < 0.001), larger female taper angles (p < 0.001), and male titanium stem tapers (p < 0.001). CONCLUSION: Consistent with the long-term clinical success of the device, the volumetric material loss from Exeter femoral head tapers was, in general, small compared with that from larger-diameter MoM head tapers. Cite this article: Bone Joint J 2018;100-B:1310-9.
Assuntos
Artroplastia de Quadril/instrumentação , Prótese de Quadril , Próteses Articulares Metal-Metal , Polietileno , Falha de Prótese , Adulto , Idoso , Idoso de 80 Anos ou mais , Feminino , Cabeça do Fêmur , Seguimentos , Humanos , Masculino , Pessoa de Meia-Idade , Desenho de Prótese , Análise de RegressãoRESUMO
OBJECTIVES: The high revision rates of the DePuy Articular Surface Replacement (ASR) and the DePuy ASR XL (the total hip arthroplasty (THA) version) have led to questions over the viability of metal-on-metal (MoM) hip joints. Some designs of MoM hip joint do, however, have reasonable mid-term performance when implanted in appropriate patients. Investigations into the reasons for implant failure are important to offer help with the choice of implants and direction for future implant designs. One way to assess the performance of explanted hip prostheses is to measure the wear (in terms of material loss) on the joint surfaces. METHODS: In this study, a coordinate measuring machine (CMM) was used to measure the wear on five failed cementless Biomet Magnum/ReCap/ Taperloc large head MoM THAs, along with one Biomet ReCap resurfacing joint. Surface roughness measurements were also taken. The reason for revision of these implants was pain and/or adverse reaction to metal debris (ARMD) and/or elevated blood metal ion levels. RESULTS: The mean wear rate of the articulating surfaces of the heads and acetabular components of all six joints tested was found to be 6.1 mm3/year (4.1 to 7.6). The mean wear rate of the femoral head tapers of the five THAs was 0.054 mm3/year (0.021 to 0.128) with a mean maximum wear depth of 5.7 µm (4.3 to 8.5). CONCLUSION: Although the taper wear was relatively low, the wear from the articulating surfaces was sufficient to provide concern and was potentially large enough to have been the cause of failure of these joints. The authors believe that patients implanted with the ReCap system, whether the resurfacing prosthesis or the THA, should be closely monitored.Cite this article: S. C. Scholes, B. J. Hunt, V. M. Richardson, D. J. Langton, E. Smith, T. J. Joyce. Explant analysis of the Biomet Magnum/ReCap metal-on-metal hip joint. Bone Joint Res 2017;6:113-122. DOI: 10.1302/2046-3758.62.BJR-2016-0130.R2.
RESUMO
AIMS: We sought to determine whether cobalt-chromium alloy (CoCr) femoral stem tapers (trunnions) wear more than titanium (Ti) alloy stem tapers (trunnions) when used in a large diameter (LD) metal-on-metal (MoM) hip arthroplasty system. PATIENTS AND METHODS: We performed explant analysis using validated methodology to determine the volumetric material loss at the taper surfaces of explanted LD CoCr MoM hip arthroplasties used with either a Ti alloy (n = 28) or CoCr femoral stem (n = 21). Only 12/14 taper constructs with a rough male taper surface and a nominal included angle close to 5.666° were included. Multiple regression modelling was undertaken using taper angle, taper roughness, bearing diameter (horizontal lever arm) as independent variables. Material loss was mapped using a coordinate measuring machine, profilometry and scanning electron microscopy. RESULTS: After adjustment for other factors, CoCr stem tapers were found to have significantly greater volumetric material loss than the equivalent Ti stem tapers. CONCLUSION: When taper junction damage is identified during revision of a LD MoM hip, it should be suspected that a male taper composed of a standard CoCr alloy has sustained significant changes to the taper cone geometry which are likely to be more extensive than those affecting a Ti alloy stem. Cite this article: Bone Joint J 2017;99-B:1304-12.
Assuntos
Artroplastia de Quadril/métodos , Ligas de Cromo , Prótese de Quadril , Próteses Articulares Metal-Metal , Adulto , Idoso , Idoso de 80 Anos ou mais , Corrosão , Análise de Falha de Equipamento , Feminino , Humanos , Masculino , Microscopia Eletrônica de Varredura , Pessoa de Meia-Idade , Desenho de Prótese , Falha de Prótese , Estresse Mecânico , Propriedades de SuperfícieRESUMO
AIMS: We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces. PATIENTS AND METHODS: We investigated the influence of the source and volume of metal debris on chromium (Cr) and cobalt (Co) concentrations in corresponding blood and hip synovial fluid samples and the observed agglomerated particle sizes in excised tissues using multiple regression analysis of prospectively collected data. A total of 199 explanted MoM hips (177 patients; 132 hips female) were analysed to determine rates of volumetric wear at the bearing surfaces and taper junctions. RESULTS: The statistical modelling suggested that a greater source contribution of metal debris from the taper junction was associated with smaller aggregated particle sizes in the local tissues and a relative reduction of Cr ion concentrations in the corresponding synovial fluid and blood samples. Metal debris generated from taper junctions appears to be of a different morphology, composition and therefore, potentially, immunogenicity to that generated from bearing surfaces. CONCLUSION: The differences in debris arising from the taper and the articulating surfaces may provide some understanding of the increased incidence of soft-tissue reactions reported in patients implanted with MoM total hip arthroplasties compared with patients with hip resurfacings. Cite this article: Bone Joint J 2016;98-B:925-33.
Assuntos
Artroplastia de Quadril , Cromo/análise , Cobalto/análise , Prótese de Quadril , Próteses Articulares Metal-Metal , Líquido Sinovial/química , Adulto , Idoso , Idoso de 80 Anos ou mais , Feminino , Humanos , Masculino , Pessoa de Meia-Idade , Tamanho da Partícula , Estudos Prospectivos , Desenho de Prótese , Adulto JovemRESUMO
OBJECTIVES: Wear debris released from bearing surfaces has been shown to provoke negative immune responses in the recipient. Excessive wear has been linked to early failure of prostheses. Analysis using coordinate measuring machines (CMMs) can provide estimates of total volumetric material loss of explanted prostheses and can help to understand device failure. The accuracy of volumetric testing has been debated, with some investigators stating that only protocols involving hundreds of thousands of measurement points are sufficient. We looked to examine this assumption and to apply the findings to the clinical arena. METHODS: We examined the effects on the calculated material loss from a ceramic femoral head when different CMM scanning parameters were used. Calculated wear volumes were compared with gold standard gravimetric tests in a blinded study. RESULTS: Various scanning parameters including point pitch, maximum point to point distance, the number of scanning contours or the total number of points had no clinically relevant effect on volumetric wear calculations. Gravimetric testing showed that material loss can be calculated to provide clinically relevant degrees of accuracy. CONCLUSIONS: Prosthetic surfaces can be analysed accurately and rapidly with currently available technologies. Given these results, we believe that routine analysis of explanted hip components would be a feasible and logical extension to National Joint Registries. Cite this article: Bone Joint Res 2014;3:60-8.
RESUMO
OBJECTIVES: The aims of this piece of work were to: 1) record the background concentrations of blood chromium (Cr) and cobalt (Co) concentrations in a large group of subjects; 2) to compare blood/serum Cr and Co concentrations with retrieved metal-on-metal (MoM) hip resurfacings; 3) to examine the distribution of Co and Cr in the serum and whole blood of patients with MoM hip arthroplasties; and 4) to further understand the partitioning of metal ions between the serum and whole blood fractions. METHODS: A total of 3042 blood samples donated to the local transfusion centre were analysed to record Co and Cr concentrations. Also, 91 hip resurfacing devices from patients who had given pre-revision blood/serum samples for metal ion analysis underwent volumetric wear assessment using a coordinate measuring machine. Linear regression analysis was carried out and receiver operating characteristic curves were constructed to assess the reliability of metal ions to identify abnormally wearing implants. The relationship between serum and whole blood concentrations of Cr and Co in 1048 patients was analysed using Bland-Altman charts. This relationship was further investigated in an in vitro study during which human blood was spiked with trivalent and hexavalent Cr, the serum then separated and the fractions analysed. RESULTS: Only one patient in the transfusion group was found to have a blood Co > 2 µg/l. Blood/Serum Cr and Co concentrations were reliable indicators of abnormal wear. Blood Co appeared to be the most useful clinical test, with a concentration of 4.5 µg/l showing sensitivity and specificity for the detection of abnormal wear of 94% and 95%, respectively. Generated metal ions tended to fill the serum compartment preferentially in vivo and this was replicated in the in vitro study when blood was spiked with trivalent Cr and bivalent Co. CONCLUSIONS: Blood/serum metal ion concentrations are reliable indicators of abnormal wear processes. Important differences exist however between elements and the blood fraction under study. Future guidelines must take these differences into account.
RESUMO
INTRODUCTION: There is an ongoing debate about the optimal use of metal-on-metal (MoM) bearings in total hip replacement, since there are uncertainties about local and systemic adverse effects due to wear and corrosion of these bearings. Despite various national recommendations, efforts to achieve international harmonization of specific evidence-based recommendations for best practice are still lacking. HYPOTHESIS: An international consensus study group should be able to develop recommendations on the use and monitoring of MoM bearings, preferably at the European level, through a multidisciplinary approach, by integrating the perspectives of various stakeholders. MATERIALS AND METHODS: Twenty-one experts representing three stakeholder groups and eight countries participated in this European consensus study, which consisted of a consensus meeting, subsequent structured discussion, and consensus voting. RESULTS: The current statement defines first of all benefits, local and systemic risks, as well as uncertain issues related to MoM bearings. Safety assessment after implantation of MoM comprises all patients. A closer follow-up is recommended for large head MoM (≥36mm) and resurfacing. In these implants basic follow-up should consist of x-rays and metal ion measurement of cobalt in whole blood, performed with GF-AAS or ICP-MS. Clinical and/or radiographic abnormality as well as elevated ion levels needs additional imaging (ultrasound, CT-scan and/or MARS-MRI). Cobalt values less than 2 µg/L are probably devoid of clinical concern, the threshold value for clinical concern is expected to be within the range of 2-7 µg/L. DISCUSSION: This is the first multinational, interdisciplinary, and multiprofessional approach for developing a recommendation for the use and monitoring of MoM bearings in total hip replacement. The current recommendations are in partial agreement with previous statements regarding the extent of follow-up and imaging techniques. They however differ from previous communications regarding measurement of metal ions and especially the investigated medium, technique, and eventual threshold levels. LEVEL OF EVIDENCE: Level V, expert opinion/agreement conference.
Assuntos
Prótese de Quadril , Próteses Articulares Metal-Metal , Artroplastia de Quadril , Cobalto , Europa (Continente) , Humanos , Osteoartrite do Quadril/cirurgia , Tamanho da PartículaRESUMO
We present the clinical results and survivorship of consecutive 100 Birmingham Hip Resurfacings in 90 patients at a minimum follow-up of ten years. All procedures were carried out by an independent surgeon who commenced a prospective study in 1998. Patients were assessed clinically using the Western Ontario and McMaster Universities osteoarthritis index, Short-Form 36, Harris hip score and University of California, Los Angeles activity score. Radiological analysis was performed by an independent observer and blood metal ion levels concentrations were measured at ten years post-operatively in 62 patients. The median acetabular component inclination was 46.2° (34° to 59°) and anteversion 11.0° (0° to 30°). The median chromium concentration in the unilateral group was 1.74 (0.41 to 15.23) and for the bilateral group was 2.98 (1.57 to 18.01). The equivalent values for cobalt were 1.67 (0.54 to 20.4) and 1.88 (1.38 to 19.32). In total there were eight failures giving an overall survival at ten years of 92% (95% confidence interval (CI) 86.7 to 97.3). BHR in male patients had an improved survivorship of 94.6% (95% CI 89.4 to 100) compared with females at 84.6% (95% CI 70.7 to 98.5), but this did not reach statistical significance (p = 0.119). Four of the nine BHRs with a bearing diameter of 42 mm failed. The overall results were consistent with data produced from other centres in that the clinical outcome of large male patients was extremely encouraging, whereas the survival of the smaller joints was less satisfactory.
Assuntos
Artroplastia de Quadril/métodos , Metais/sangue , Osteoartrite do Quadril/cirurgia , Adulto , Idoso , Cromo/sangue , Cobalto/sangue , Feminino , Seguimentos , Articulação do Quadril/diagnóstico por imagem , Articulação do Quadril/fisiopatologia , Prótese de Quadril , Humanos , Masculino , Pessoa de Meia-Idade , Osteoartrite do Quadril/diagnóstico por imagem , Satisfação do Paciente , Falha de Prótese , Radiografia , Índice de Gravidade de Doença , Fatores Sexuais , Resultado do Tratamento , Adulto JovemRESUMO
OBJECTIVES: An ongoing prospective study to investigate failing metal-on-metal hip prostheses was commenced at our centre in 2008. We report on the results of the analysis of the first consecutive 126 failed mated total hip prostheses from a single manufacturer. METHODS: Analysis was carried out using highly accurate coordinate measuring to calculate volumetric and linear rates of the articular bearing surfaces and also the surfaces of the taper junctions. The relationship between taper wear rates and a number of variables, including bearing diameter and orientation of the acetabular component, was investigated. RESULTS: The measured rates of wear and distribution of material loss from the taper surfaces appeared to show that the primary factor leading to taper failure is the increased lever arm acting on this junction in contemporary large-diameter metal-on-metal hip replacements. CONCLUSIONS: Our analysis suggests that varus stems, laterally engaging taper systems and larger head diameters all contribute to taper failure.
RESUMO
This study reports the mid-term results of a large-bearing hybrid metal-on-metal total hip replacement in 199 hips (185 patients) with a mean follow-up of 62 months (32 to 83). Two patients died of unrelated causes and 13 were lost to follow-up. In all, 17 hips (8.5%) have undergone revision, and a further 14 are awaiting surgery. All revisions were symptomatic. Of the revision cases, 14 hips showed evidence of adverse reactions to metal debris. The patients revised or awaiting revision had significantly higher whole blood cobalt ion levels (p = 0.001), but no significant difference in acetabular component size or position compared with the unrevised patients. Wear analysis (n = 5) showed increased wear at the trunnion-head interface, normal levels of wear at the articulating surfaces and evidence of corrosion on the surface of the stem. The cumulative survival rate, with revision for any reason, was 92.4% (95% confidence interval 87.4 to 95.4) at five years. Including those awaiting surgery, the revision rate would be 15.1% with a cumulative survival at five years of 89.6% (95% confidence interval 83.9 to 93.4). This hybrid metal-on-metal total hip replacement series has shown an unacceptably high rate of failure, with evidence of high wear at the trunnion-head interface and passive corrosion of the stem surface. This raises concerns about the use of large heads on conventional 12/14 tapers.
Assuntos
Artroplastia de Quadril/instrumentação , Prótese de Quadril/efeitos adversos , Falha de Prótese , Idoso , Artroplastia de Quadril/efeitos adversos , Artroplastia de Quadril/métodos , Cobalto/sangue , Corrosão , Análise de Falha de Equipamento/métodos , Feminino , Seguimentos , Articulação do Quadril/diagnóstico por imagem , Humanos , Masculino , Metais/efeitos adversos , Pessoa de Meia-Idade , Desenho de Prótese , Radiografia , Reoperação , Análise de SobrevidaRESUMO
We sought to establish the incidence of joint failure secondary to adverse reaction to metal debris (ARMD) following metal-on-metal hip resurfacing in a large, three surgeon, multicentre study involving 4226 hips with a follow-up of 10 to 142 months. Three implants were studied: the Articular Surface Replacement; the Birmingham Hip Resurfacing; and the Conserve Plus. Retrieved implants underwent analysis using a co-ordinate measuring machine to determine volumetric wear. There were 58 failures associated with ARMD. The median chromium and cobalt concentrations in the failed group were significantly higher than in the control group (p < 0.001). Survival analysis showed a failure rate in the patients with Articular Surface Replacement of 12.8% [corrected] at five years, compared with < 1% at five years for the Conserve Plus and 1.5% at ten years for the Birmingham Hip Resurfacing. Two ARMD patients had relatively low wear of the retrieved components. Increased wear from the metal-on-metal bearing surface was associated with an increased rate of failure secondary to ARMD. However, the extent of tissue destruction at revision surgery did not appear to be dose-related to the volumetric wear.
Assuntos
Artroplastia de Quadril/efeitos adversos , Prótese de Quadril/efeitos adversos , Adulto , Idoso , Artroplastia de Quadril/métodos , Cromo/sangue , Cobalto/sangue , Análise de Falha de Equipamento/métodos , Feminino , Seguimentos , Humanos , Masculino , Pessoa de Meia-Idade , Desenho de Prótese , Falha de Prótese , Reoperação , Análise de SobrevidaRESUMO
There is widespread concern regarding the incidence of adverse soft-tissue reactions after metal-on-metal (MoM) hip replacement. Recent National Joint Registry data have shown clear differences in the rates of failure of different designs of hip resurfacing. Our aim was to update the failure rates related to metal debris for the Articular Surface Replacement (ASR). A total of 505 of these were implanted. Kaplan-Meier analysis showed a failure rate of 25% at six years for the ASR resurfacing and of 48.8% for the ASR total hip replacement (THR). Of 257 patients with a minimum follow-up of two years, 67 (26.1%) had a serum cobalt concentration which was greater than 7 µg/l. Co-ordinate measuring machine analysis of revised components showed that all patients suffering adverse tissue reactions in the resurfacing group had abnormal wear of the bearing surfaces. Six THR patients had relatively low rates of articular wear, but were found to have considerable damage at the trunion-taper interface. Our results suggest that wear at the modular junction is an important factor in the development of adverse tissue reactions after implantation of a large-diameter MoM THR.
Assuntos
Prótese de Quadril/efeitos adversos , Artroplastia de Quadril/efeitos adversos , Artroplastia de Quadril/métodos , Cromo/sangue , Cobalto/sangue , Métodos Epidemiológicos , Análise de Falha de Equipamento/métodos , Feminino , Humanos , Masculino , Desenho de Prótese , Falha de Prótese , ReoperaçãoRESUMO
We present the early clinical and radiological results of Articular Surface Replacement (ASR) resurfacings in 214 hips (192 patients) with a mean follow-up of 43 months (30 to 57). The mean age of the patients was 56 years (28 to 74) and 85 hips (40%) were in 78 women. The mean Harris hip score improved from 52 (11 to 81) to 95 (27 to 100) at two years and the mean University of California, Los Angeles activity score from 3.9 (1 to 10) to 7.4 (2 to 10) in the same period. Narrowing of the neck (to a maximum of 9%) was noted in 124 of 209 hips (60%). There were 12 revisions (5.6%) involving four (1.9%) early fractures of the femoral neck and two (0.9%) episodes of collapse of the femoral head secondary to avascular necrosis. Six patients (2.8%) had failure related to metal wear debris. The overall survival for our series was 93% (95% confidence interval 80 to 98) and 89% (95% confidence interval 82 to 96) for hips with acetabular components smaller than 56 mm in diameter. The ASR implant has a lower diametrical clearance and a subhemispherical acetabular component when compared with other more frequently implanted metal-on-metal hip resurfacings. These changes may contribute to the higher failure rate than in other series, compared with other designs. Given our poor results with the small components we are no longer implanting the smaller size.
Assuntos
Artroplastia de Quadril/métodos , Fraturas do Colo Femoral/cirurgia , Articulação do Quadril/diagnóstico por imagem , Osteoartrite do Quadril/cirurgia , Complicações Pós-Operatórias/diagnóstico por imagem , Adulto , Idoso , Feminino , Fraturas do Colo Femoral/complicações , Fraturas do Colo Femoral/diagnóstico por imagem , Articulação do Quadril/cirurgia , Humanos , Masculino , Metais/sangue , Pessoa de Meia-Idade , Osteoartrite do Quadril/diagnóstico por imagem , Avaliação de Resultados em Cuidados de Saúde , Complicações Pós-Operatórias/cirurgia , Estudos Prospectivos , Desenho de Prótese , Radiografia , Reoperação , Reino UnidoRESUMO
Early failure associated with adverse reactions to metal debris is an emerging problem after hip resurfacing but the exact mechanism is unclear. We analysed our entire series of 660 metal-on-metal resurfacings (Articular Surface Replacement (ASR) and Birmingham Hip Resurfacing (BHR)) and large-bearing ASR total hip replacements, to establish associations with metal debris-related failures. Clinical and radiological outcomes, metal ion levels, explant studies and lymphocyte transformation tests were performed. A total of 17 patients (3.4%) were identified (all ASR bearings) with adverse reactions to metal debris, for which revision was required. This group had significantly smaller components, significantly higher acetabular component anteversion, and significantly higher whole concentrations of blood and joint chromium and cobalt ions than asymptomatic patients did (all p < 0.001). Post-revision lymphocyte transformation tests on this group showed no reactivity to chromium or cobalt ions. Explants from these revisions had greater surface wear than retrievals for uncomplicated fractures. The absence of adverse reactions to metal debris in patients with well-positioned implants usually implies high component wear. Surgeons must consider implant design, expected component size and acetabular component positioning in order to reduce early failures when performing large-bearing metal-on-metal hip resurfacing and replacement.
Assuntos
Artroplastia de Quadril/efeitos adversos , Articulação do Quadril/patologia , Metais/sangue , Adulto , Idoso , Idoso de 80 Anos ou mais , Artroplastia de Quadril/métodos , Análise de Falha de Equipamento , Feminino , Articulação do Quadril/imunologia , Humanos , Estimativa de Kaplan-Meier , Masculino , Metais/imunologia , Pessoa de Meia-Idade , Dor Pós-Operatória/etiologia , Dor Pós-Operatória/imunologia , Dor Pós-Operatória/mortalidade , Desenho de Prótese/métodos , Falha de Prótese , Reoperação , Fatores de Tempo , Resultado do TratamentoRESUMO
There have been no large comparative studies of the blood levels of metal ions after implantation of commercially available hip resurfacing devices which have taken into account the effects of femoral size and inclination and anteversion of the acetabular component. We present the results in 90 patients with unilateral articular surface replacement (ASR) hip resurfacings (mean time to blood sampling 26 months) and 70 patients with unilateral Birmingham Hip Resurfacing (BHR) implants (mean time 47 months). The whole blood and serum chromium (Cr) and cobalt (Co) concentrations were inversely related to the size of the femoral component in both groups (p < 0.05). Cr and Co were more strongly influenced by the position of the acetabular component in the case of the ASR, with an increase in metal ions observed at inclinations > 45 degrees and anteversion angles of < 10 degrees and > 20 degrees. These levels were only increased in the BHR group when the acetabular component was implanted with an inclination > 55 degrees. A significant relationship was identified between the anteversion of the BHR acetabular component and the levels of Cr and Co (p < 0.05 for Co), with an increase observed at anteversion angles < 10 degrees and > 20 degrees. The median whole blood and serum Cr concentrations of the male ASR patients were significantly lower than those of the BHR men (p < 0.001). This indicates that reduced diametral clearance may equate to a reduction in metal ion concentrations in larger joints with satisfactory orientation of the acetabular component.
Assuntos
Artroplastia de Quadril/métodos , Cromo/sangue , Cobalto/sangue , Articulação do Quadril/cirurgia , Adulto , Idoso , Artroplastia de Quadril/instrumentação , Feminino , Humanos , Masculino , Pessoa de Meia-IdadeRESUMO
Increased concentrations of metal ions after metal-on-metal resurfacing arthroplasty of the hip remain a concern. Although there has been no proven link to long-term health problems or early prosthetic failure, variables associated with high metal ion concentrations should be identified and, if possible, corrected. Our study provides data on metal ion levels from a series of 76 consecutive patients (76 hips) after resurfacing arthroplasty with the Articular Surface Replacement. Chromium and cobalt ion concentrations in the whole blood of patients with smaller (