Breaking the Size Limitation of Directly-Synthesized PbS Quantum Dot Inks Toward Efficient Short-wavelength Infrared Optoelectronic Applications.

PbS quantum dots (QDs) are promising building blocks for solution-processed short-wavelength infrared (SWIR) devices. The recently developed direct synthesis of semi-conductive PbS QD inks has substantially simplified the preparation processing and reduced the material cost, while facing the challenge to synthesize large-size QDs with absorption covering the SWIR region. Herein, we for the first time realize a low-cost, scalable synthesis of SWIR PbS QD inks after an extensive investigation of the reaction kinetics. Finally, based on these PbS SWIR QD inks, the solar cell demonstrates a record-high power conversion efficiency (PCE) of 1.44 % through an 1100 nm cutoff silicon filter and the photodetector device shows a low dark current density of 2×10-6  A cm-2 at -0.8 V reverse bias with a high external quantum efficiency (EQE) of 70 % at ≈1300 nm. Our results realize the direct synthesis of low-cost and scalable SWIR QD inks and may accelerate the industrialization of consumer SWIR technologies.

Room-temperature direct synthesis of semi-conductive PbS nanocrystal inks for optoelectronic applications.

Lead sulphide (PbS) nanocrystals (NCs) are promising materials for low-cost, high-performance optoelectronic devices. So far, PbS NCs have to be first synthesized with long-alkyl chain organic surface ligands and then be ligand-exchanged with shorter ligands (two-steps) to enable charge transport. However, the initial synthesis of insulated PbS NCs show no necessity and the ligand-exchange process is tedious and extravagant. Herein, we have developed a direct one-step, scalable synthetic method for iodide capped PbS (PbS-I) NC inks. The estimated cost for PbS-I NC inks is decreased to less than 6 $·g-1, compared with 16 $·g-1 for conventional methods. Furthermore, based on these PbS-I NCs, photodetector devices show a high detectivity of 1.4 × 1011 Jones and solar cells show an air-stable power conversion efficiency (PCE) up to 10%. This scalable and low-cost direct preparation of high-quality PbS-I NC inks may pave a path for the future commercialization of NC based optoelectronics.

High-Efficiency PbS Quantum-Dot Solar Cells with Greatly Simplified Fabrication Processing via "Solvent-Curing".

PbS quantum-dot (QD) solar cells are promising candidates for low-cost solution-processed photovoltaics. However, the device fabrication usually requires ten more times film deposition and rinsing steps, which is not ideal for scalable manufacturing. Here, a greatly simplified deposition processing is demonstrated by replacing methanol with acetonitrile (ACN) as the rinsing solvent. It is discovered that ACN can effectively "cure" the film cracks generated from the volume loss during the solid-state ligand-exchange process, which enables the deposition of thick and dense films with much fewer deposition steps. Meanwhile, due to the aprotic nature of ACN, fewer trap states can be introduced during the rinsing process. As a result, with only three deposition steps for the active layer, a CPVT-certified 11.21% power conversion efficiency is obtained, which is the highest efficiency ever reported for PbS QD solar cells employing a solid-state ligand-exchange process. More importantly, the simple film-deposition processing provides an opportunity for the future application of QDs in low-cost printing of optoelectronic devices.

In Situ Passivation for Efficient PbS Quantum Dot Solar Cells by Precursor Engineering.

Current efforts on lead sulfide quantum dot (PbS QD) solar cells are mostly paid to the device architecture engineering and postsynthetic surface modification, while very rare work regarding the optimization of PbS synthesis is reported. Here, PbS QDs are successfully synthesized using PbO and PbAc2  ·â€†3H2 O as the lead sources. QD solar cells based on PbAc-PbS have demonstrated a high power conversion efficiency (PCE) of 10.82% (and independently certificated values of 10.62%), which is significantly higher than the PCE of 9.39% for PbO-PbS QD based ones. For the first time, systematic investigations are carried out on the effect of lead precursor engineering on the device performance. It is revealed that acetate can act as an efficient capping ligands together with oleic acid, providing better surface coverage and replace some of the harmful hydroxyl (OH) ligands during the synthesis. Then the acetate on the surface can be exchanged by iodide and lead to desired passivation. This work demonstrates that the precursor engineering has great potential in performance improvement. It is also pointed out that the initial synthesis is an often neglected but critical stage and has abundant room for optimization to further improve the quality of the resultant QDs, leading to breakthrough efficiency.

Pulsed Lasers Employing Solution-Processed Plasmonic Cu3- x P Colloidal Nanocrystals.

A new approach to synthesize self-doped colloidal Cu3-x P NCs with controlled size and localized surface plasmon resonance absorption is reported. These Cu3-x P NCs show ultrafast exciton dynamics and huge optical nonlinearities due to plasmonic resonances, which afford the first demonstration of plasmonic Cu3-x P NCs as simple, effective, and solution-processed nonlinear absorbers for high-energy Q-switched fiber laser.