Epoxy⁻PCM Composites with Nanocarbons or Multidimensional Boron Nitride as Heat Flow Enhancers.

The need for affordable systems that are capable of regulating the temperature of living or storage spaces has increased the interest in exploring phase change materials (PCMs) for latent heat thermal energy storage (LHTES). This study investigates n-nonadecane (C19H40) and n-eicosane (C20H42) as alkane hydrocarbons/paraffins for LHTES applications. An epoxy resin is used as the support matrix medium to mitigate paraffin leakage, and a thickening agent is utilized to suppress phase separation during the curing process. In order to enhance the thermal conductivity of the epoxy-paraffin composite, conductive agents including carbon nanofibers (CNFs), carbon nanotubes (CNTs), boron nitride (BN) microparticles, or boron nitride nanotubes (BNNTs) are incorporated in different gravimetric ratios. Enhancements in latent heat, thermal conductivity, and heat transfer are realized with the addition of the thermal fillers. The sample composition with 10 wt.% BN shows excellent reversibility upon extended heating-cooling cycles and adequate viscosity for template casting as well as direct three-dimensional (3D) printing on fabrics, demonstrating the feasibility for facile integration onto liners/containers for thermal regulation purposes.

Impact of Current and Temperature on Extremely Low Loading Epoxy-CNT Conductive Composites.

Carbon nanotube (CNT) conductive composites have attracted significant attention for their potential use in applications such as electrostatic dissipation and/or electromagnetic interference shielding. The focus of this work is to evaluate resistivity trends of extremely low loading (<0.1 wt%) epoxy-CNT composites that lack a connected CNT network, but still present electrical conductivity values appropriate for those uses. The impact of current, temperature, and cycle life on electrical properties are here identified and tied to possible performance limits. At extremely low loadings, the CNT content is not sufficient to form a completely interconnected grid, thus, electrons must travel through insulating media. While still in the semi-conductor range, resistivity values are observed to decrease with increasing direct current and demonstrate a non-ohmic behavior. CNT epoxy composites were subjected to elevated currents and/or temperatures over diverse periods of time to examine impacts on resistivity. Microstructural analyses of composite samples were conducted to observe signs of damage for specimens taken to extreme temperatures/currents. An understanding of the electrical conductivity characteristics of extremely low loading epoxy-CNT composites and their failure mechanisms will aid in understanding risks associated with their use in challenging environments that may include high temperatures, high currents, and/or high frequencies.

Modeling of Energy Demand and Savings Associated with the Use of Epoxy-Phase Change Material Formulations.

This manuscript integrates the experimental findings of recently developed epoxy-phase change material (PCM) formulations with modeling efforts aimed to determine the energy demands and savings derived from their use. The basic PCM system employed was composed of an epoxy resin, a thickening agent, and nonadecane, where the latter was the hydrocarbon undergoing the phase transformation. Carbon nanofibers (CNF) and boron nitride (BN) particulates were used as heat flow enhancers. The thermal conductivities, densities, and latent heat determined in laboratory settings were introduced in a model that calculated, using EnergyPlus software, the energy demands, savings and temperature profiles of the interior and the walls of a shelter for six different locations on Earth. A shipping container was utilized as exemplary dwelling. Results indicated that all the epoxy-PCM formulations had a positive impact on the total energy savings (between 16% and 23%) for the locations selected. The use of CNF and BN showed an increase in performance when compared with the formulation with no thermal filler additives. The formulations selected showed great potential to reduce the energy demands, increase savings, and result in more adequate temperatures for living and storage spaces applications.

Reduction Expansion Synthesis of Sintered Metal.

Described herein is a novel method, Reduction Expansion Synthesis-Sintered Metal (RES-SM), to create a sintered metal body of a designed shape at ambient pressure, hundreds of degrees below the metal melting temperature. The precursor to the metal part is a mixture of metal oxide particles and activated metal particles, and in this study specifically nickel oxide and activated nickel metal particles. It is postulated that the metal oxide component is reduced via exposure to chemical radical species produced via thermal decomposition of urea or other organic compounds. In the study performed, the highest temperature required was 950 °C, the longest duration of high temperature treatment was 1200 s, and in all cases, the atmosphere was inert gas at ambient pressure. As discovered using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and x-ray diffraction (XRD), the metal that forms via the RES process presents necks of completely reduced metal between existing metal particles. The 'as produced' parts are similar in properties to 'brown' metal parts created using more standard methods and require 'post processing' to full densify. Parts treated by hot isostatic pressing show fully self-supporting, robust structures, with hardness values like others reported in literature for traditional fabrication methods. This novel method uses affordable and environmentally friendly precursors to join metallic parts at moderate temperatures, produces fully reduced metals in a very short time and has potential to make many parts simultaneously in a standard laboratory furnace.

Electrically Conductive CNT Composites at Loadings below Theoretical Percolation Values.

It is well established that dramatic increases in conductivity occur upon the addition of conductive filler materials to highly resistive polymeric matrices in experimental settings. However, the mechanisms responsible for the observed behavior at low filler loadings, below theoretical percolation limits, of even high aspect ratio fillers such as carbon nanotubes (CNT) are not completely understood. In this study, conductive composites were fabricated using CNT bundles dispersed in epoxy resins at diverse loadings, using different dispersion and curing protocols. Based on electron microscopy observation of the CNTs strands distribution in the polymeric matrices and the corresponding electrical conductivities of those specimens, we concluded that no single electron transfer model can accurately explain the conductive behavior for all the loading values. We propose the existence of two different conductive mechanisms; one that exists close to the percolation limit, from 'low loadings' to higher CNT contents (CNT % wt > 0.1) and a second for 'extremely low loadings', near the percolation threshold (CNT % wt < 0.1). The high conductivity observed for composites at low CNT loading values can be explained by the existence of a percolative CNT network that coexists with micron size regions of non-conductive material. In contrast, samples with extremely low CNT loading values, which present no connectivity or close proximity between CNT bundles, show an electrical conductivity characterized by a current/voltage dependence. Data suggests that at these loadings, conduction may occur via a material breakdown mechanism, similar to dielectric breakdown in a capacitor. The lessons learned from the data gathered in here could guide future experimental research aimed to control the conductivity of CNT composites.

Novel Formulations of Phase Change Materials-Epoxy Composites for Thermal Energy Storage.

This research aimed to evaluate the thermal properties of new formulations of phase change materials (PCMs)-epoxy composites, containing a thickening agent and a thermally conductive phase. The composite specimens produced consisted of composites fabricated using (a) inorganic PCMs (hydrated salts), epoxy resins and aluminum particulates or (b) organic PCM (paraffin), epoxy resins, and copper particles. Differential Scanning Calorimetry (DSC) was used to analyze the thermal behavior of the samples, while hardness measurements were used to determine changes in mechanical properties at diverse PCM and conductive phase loading values. The results indicate that the epoxy matrix can act as a container for the PCM phase without hindering the heat-absorbing behavior of the PCMs employed. Organic PCMs presented reversible phase transformations over multiple cycles, an advantage that was lacking in their inorganic counterparts. The enthalpy of the organic PCM-epoxy specimens increased linearly with the PCM content in the matrix. The use of thickening agents prevented phase segregation issues and allowed the fabrication of specimens containing up to 40% PCM, a loading significantly higher than others reported. The conductive phase seemed to improve the heat transfer and the mechanical properties of the composites when present in low percentages (<10 wt %); however, given its mass, the enthalpy detected in the composites was reduced as their loading further increased. The conductive phase combination (PCM + epoxy resin + hardener + thickening agent) presents great potential as a heat-absorbing material at the temperatures employed.

Novel Chemical Process for Producing Chrome Coated Metal.

This work demonstrates that a version of the Reduction Expansion Synthesis (RES) process, Cr-RES, can create a micron scale Cr coating on an iron wire. The process involves three steps. I. A paste consisting of a physical mix of urea, chrome nitrate or chrome oxide, and water is prepared. II. An iron wire is coated by dipping. III. The coated, and dried, wire is heated to ~800 °C for 10 min in a tube furnace under a slow flow of nitrogen gas. The processed wires were then polished and characterized, primarily with scanning electron microscopy (SEM). SEM indicates the chrome layer is uneven, but only on the scale of a fraction of a micron. The evidence of porosity is ambiguous. Elemental mapping using SEM electron microprobe that confirmed the process led to the formation of a chrome metal layer, with no evidence of alloy formation. Additionally, it was found that thickness of the final Cr layer correlated with the thickness of the precursor layer that was applied prior to the heating step. Potentially, this technique could replace electrolytic processing, a process that generates carcinogenic hexavalent chrome, but further study and development is needed.

Reduction Expansion Synthesis as Strategy to Control Nitrogen Doping Level and Surface Area in Graphene.

Graphene sheets doped with nitrogen were produced by the reduction-expansion (RES) method utilizing graphite oxide (GO) and urea as precursor materials. The simultaneous graphene generation and nitrogen insertion reactions are based on the fact that urea decomposes upon heating to release reducing gases. The volatile byproducts perform two primary functions: (i) promoting the reduction of the GO and (ii) providing the nitrogen to be inserted in situ as the graphene structure is created. Samples with diverse urea/GO mass ratios were treated at 800 °C in inert atmosphere to generate graphene with diverse microstructural characteristics and levels of nitrogen doping. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to study the microstructural features of the products. The effects of doping on the samples structure and surface area were studied by X-ray diffraction (XRD), Raman Spectroscopy, and Brunauer Emmet Teller (BET). The GO and urea decomposition-reduction process as well as nitrogen-doped graphene stability were studied by thermogravimetric analysis (TGA) coupled with mass spectroscopy (MS) analysis of the evolved gases. Results show that the proposed method offers a high level of control over the amount of nitrogen inserted in the graphene and may be used alternatively to control its surface area. To demonstrate the practical relevance of these findings, as-produced samples were used as electrodes in supercapacitor and battery devices and compared with conventional, thermally exfoliated graphene.

Fabrication of a Low Density Carbon Fiber Foam and Its Characterization as a Strain Gauge.

Samples of carbon nano-fiber foam (CFF), essentially a 3D solid mat of intertwined nanofibers of pure carbon, were grown using the Constrained Formation of Fibrous Nanostructures (CoFFiN) process in a steel mold at 550 °C from a palladium particle catalysts exposed to fuel rich mixtures of ethylene and oxygen. The resulting material was studied using Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDX), Surface area analysis (BET), and Thermogravimetric Analysis (TGA). Transient and dynamic mechanical tests clearly demonstrated that the material is viscoelastic. Concomitant mechanical and electrical testing of samples revealed the material to have electrical properties appropriate for application as the sensing element of a strain gauge. The sample resistance versus strain values stabilize after a few compression cycles to show a perfectly linear relationship. Study of microstructure, mechanical and electrical properties of the low density samples confirm the uniqueness of the material: It is formed entirely of independent fibers of diverse diameters that interlock forming a tridimensional body that can be grown into different shapes and sizes at moderate temperatures. It regains its shape after loads are removed, is light weight, presents viscoelastic behavior, thermal stability up to 550 °C, hydrophobicity, and is electrically conductive.