Pressure-induced amorphization of YVO4:Eu³âº nanoboxes.

A structural transformation from the zircon-type structure to an amorphous phase has been found in YVO4:Eu(3+) nanoboxes at high pressures above 12.7 GPa by means of x-ray diffraction measurements. However, the pair distribution function of the high-pressure phase shows that the local structure of the amorphous phase is similar to the scheelite-type YVO4. These results are confirmed both by Raman spectroscopy and Eu(3+) photoluminescence which detect the phase transition to a scheelite-type structure at 10.1 and 9.1 GPa, respectively. The irreversibility of the phase transition is observed with the three techniques after a maximum pressure in the upstroke of around 20 GPa. The existence of two (5)D0-->(7)F0 photoluminescence peaks confirms the existence of two local environments for Eu(3+), at least for the low-pressure phase. One environment is the expected for substituting Y(3+) and the other is likely a disordered environment possibly found at the surface of the nanoboxes.

Optical pressure and temperature sensor based on the luminescence properties of Nd3+ ion in a gadolinium scandium gallium garnet crystal.

Hypersensitivity to pressure and temperature is observed in the near-infrared emission lines of the Nd(3+) ion in a Cr(3+),Nd(3+):Gd(3)Sc(2)Ga(3)O(12) crystal, associated to the R(1,2)((4)F(3/2))→Z(5)((4)I(9/2)) and R(1,2)((4)F(3/2))→Z(1)((4)I(9/2)) transitions. The former emissions show large linear pressure coefficients of -11.3 cm(-1)/GPa and -8.8 cm(-1)/GPa, while the latter show high thermal sensitivity in the low temperature range. Thus this garnet crystal can be considered a potential optical pressure and/or temperature sensor in high pressure and temperature experiments up to 12 GPa and below room temperature, used in diamond anvil cells and excited with different UV and visible commercial laser due to the multiple Cr(3+) and Nd(3+) absorption bands.

Structural and luminescence properties of Ho(3+)/Yb(3+)-doped Lu3Ga5O12 nano-garnets for phosphor applications.

Lu3Ga5O12 nano-garnet powders doped with Ho(3+)/Yb(3+) ions have been prepared using a citrate sol-gel technique. The structural and morphological properties have been investigated by X-ray diffraction, scanning electron microscopy and Fourier transform infrared spectroscopy. The materials are found to exist in single phase of cubic garnet structure with an average particle size of around 45 nm. The Ho(3+)/Yb(3+)-doped Lu3Ga5O12 nano-garnet powders give rise to an intense green and weak red emission of Ho3+ ions under 457.5 nm direct excitation. Moreover, when the Yb3+ ions are excited at 950 nm a very bright green luminescence of the Ho3+ ions is observed by the naked eyes even for such low laser power as 10 mW and the intensity of the red emission have been increased compared to that found under direct excitation of the Ho3+ ions. The power dependency and dynamics of the infrared-to-visible upconverted luminescence confirm the existence of different two-photon energy transfer processes. All these results have been compared with those obtained for other garnets doped with similar lanthanide ions which suggest that the Lu3Ga5O12 nano-garnets are potential materials for light emitting devices.

Experimental and theoretical study of α-Eu2(MoO4)3 under compression.

The compression process in the α-phase of europium trimolybdate was revised employing several experimental techniques. X-ray diffraction (using synchrotron and laboratory radiation sources), Raman scattering and photoluminescence experiments were performed up to a maximum pressure of 21 GPa. In addition, the crystal structure and Raman mode frequencies have been studied by means of first-principles density functional based methods. Results suggest that the compression process of α-Eu2(MoO4)3 can be described by three stages. Below 8 GPa, the α-phase suffers an isotropic contraction of the crystal structure. Between 8 and 12 GPa, the compound undergoes an anisotropic compression due to distortion and rotation of the MoO4 tetrahedra. At pressures above 12 GPa, the amorphization process starts without any previous occurrence of a crystalline-crystalline phase transition in the whole range of pressure. This behavior clearly differs from the process of compression and amorphization in trimolybdates with [Formula: see text]-phase and tritungstates with α-phase.

Health-seeking norms for tuberculosis symptoms in southern Angola: implications for behaviour change communications.

SETTING: A passive case-finding strategy as present in the DOTS strategy presupposes a patient's willingness to seek care. This requires awareness of tuberculosis (TB) symptoms and the diagnostic process, and positive attitudes towards access and probability of cure. OBJECTIVE: To measure parameters of health-seeking intention in Southern Angola and to inform the design of context-specific interventions to improve case detection. DESIGN: A survey in four communities based on the cough-to-cure pathway represented by five domains with either one or two proxy measures. These were assessed for association with appropriate health-seeking behaviour (visiting a medical institution or service). RESULTS: In total, 805 individuals were included in the study. Appropriate health-seeking behaviour was positively associated with knowing the disease (OR 3.1, 95%CI 1.4-6.8), knowing key symptoms (OR 1.4, 95%CI 1.0-1.9), perceived curability (OR 1.3, 95%CI 1.0-1.6), and the perception that TB services were free of charge (OR 1.9, 95%CI 1.4-2.7). Respondents who perceived a personal risk for TB were less likely to have an appropriate intended health-seeking behaviour (OR 0.7, 95%CI 0.5-0.9). CONCLUSION: Knowledge about TB should include key symptoms, perceived curability and information on access to services when designing interventions to improve case detection. The study highlights the importance of advocacy, social mobilisation and communication strategies.