Preparation of carnation-like Ag-ZnO composites for enhanced photocatalysis under visible light.

Carnation-like ZnO was synthesized by the facile precipitation method (at room temperature and in 120 min) to decompose dyes in an aqueous medium. The carnation-like ZnO had a stratified porous structure with a size of about 2-3µm, its petals had a smooth surface with a thickness of 5-10 nm and a width of about 300-500 nm. Ag-ZnO composites were synthesized using glucose with the assistance of PVP. The morphology of Ag-ZnO composites was almost unchanged compared to ZnO. Where, the Ag nanoparticles in the size range of 5-15 nm were uniformly dispersed on the ZnO petals, improving the catalytic ability of the composites in tartrazine (TA) degradation. The influence of Ag content on catalytic structure and performance of composite was studied. The 5Ag-ZnO sample had the highest BET surface area and pore volume and the lowest gap energy (Eg) among the as-synthesized samples. The 5Ag-ZnO sample proclaimed the degradation efficiency in 70 min of 97.8% and thekapof 0.031 min-1. The influences of catalyst content, solution pH, and concentration of dye on the photodegradation efficiency of the composite were thoroughly studied. Besides, the photocatalytic activity of the composite was demonstrated by degrading various organic substances and reusability. In addition, it was compared to a metal-semiconductor catalyst of Au-ZnO and semiconductor-semiconductor catalysts of MoS2-ZnO, Cu2O-ZnO, and SiO2-ZnO. The catalytic mechanism under visible light was proposed.

Facile Controlling of the Physical Properties of Zinc Oxide and Its Application to Enhanced Photocatalysis.

In this study, the physical properties of ZnO were facile controlled by the synthesis method with the addition of capping and precipitation agents. As-prepared ZnO samples had different morphologies such as carnation flower-like ZnO (CF-ZnO), rose-flower-like ZnO (RF-ZnO), rod-like ZnO (R-ZnO), and nanoparticle ZnO (N-ZnO) and were characterized by SEM, XRD, N2 adsorption/desorption isotherms, FT-IR, and DR/UV-vis. All samples had a crystallite structure of hexagonal wurtzite type. The CF-ZnO and RF-ZnO samples had the hierarchical structure like a carnation flower and a beautiful rose, respectively. R-ZnO was composed of many hexagonal rods and few spherical particles, while N-ZnO microstructures were made up of nanoparticles with approximately 20-30 nm, exhibiting the largest surface area, pore volume, and pore width among as-prepared samples, and their crystal size and bandgap energy were 17.8 nm and 3.207 eV, respectively. The catalytic performances of ZnO samples were evaluated by degradation of Tartrazine (TA) and Caffeine (CAF) under low UV irradiation (15 W). N-ZnO showed a high photocatalytic activity compared to other samples. Besides, the reaction kinetics was investigated by the first-order kinetic model, and the catalytic performance of ZnO was evaluated through several organic pollutants.