RESUMO
Perovskite light-emitting diodes (PeLEDs) employing CH3NH3PbBr3 as the emission layer (EML) and graphene oxide (GO) doped PEDOT:PSS as the hole transport layer (HTL) were prepared and characterized. GO doped in PEDOT:PSS can lead to the increased work function of HTL and lower the hole injection barrier at the HTL/CH3NH3PbBr3 interface, which facilitates the hole injection. Meanwhile, the optimized GO amount in PEDOT:PSS can help to reduce the quenching of luminescence occurring at the interface between HTL and perovskite. The luminance and current efficiency reach the maximum values of 3302 cd m-2 and 1.92 cd A-1 in PeLED with an optimized GO ratio (0.3), which increase by 43.3% and 73.0% in comparison with the undoped device, respectively. The enhanced luminescence of PeLEDs was caused by the combined effects of enhanced hole injection efficiency and the suppressed exciton quenching occurring at the HTL/EML interface. These results indicate that the introduction of traditional two-dimensional materials is a reasonable method for designing the structure of PeLEDs.
RESUMO
High efficiency blue fluorescent organic light-emitting diodes (OLEDs), based on 1,3-bis(carbazol-9-yl)benzene (mCP) doped with 4,4'-bis(9-ethyl-3-carbazovinylene)-1,1'-biphenyl (BCzVBi), were fabricated using four different hole transport layers (HTLs) and two different electron transport layers (ETLs). Fixing the electron transport material TPBi, four hole transport materials, including 1,1-Bis[(di-4-tolylamino)phenyl]cyclohexane (TAPC), N,N'-Di(1-naphthyl)-N,N'-diphenyl-(1,1'-biphenyl)-4'-diamine(NPB), 4,4'-Bis(N-carbazolyl)-1,1,-biphenyl (CBP) and molybdenum trioxide (MoO3), were selected to be HTLs, and the blue OLED with TAPC HTL exhibited a maximum luminance of 2955 cd/m2 and current efficiency (CE) of 5.75 cd/A at 50 mA/cm2, which are 68% and 62% higher, respectively, than those of the minimum values found in the device with MoO3 HTL. Fixing the hole transport material TAPC, the replacement of TPBi ETL with Bphen ETL can further improve the performance of the device, in which the maximum luminance can reach 3640 cd/m2 at 50 mA/cm2, which is 23% higher than that of the TPBi device. Furthermore, the lifetime of the device is also optimized by the change of ETL. These results indicate that the carrier mobility of transport materials and energy level alignment of different functional layers play important roles in the performance of the blue OLEDs. The findings suggest that selecting well-matched electron and hole transport materials is essential and beneficial for the device engineering of high-efficiency blue OLEDs.
RESUMO
High efficiency perovskite light-emitting diodes (PeLEDs) using PEDOT:PSS/MoO3-ammonia composite hole transport layers (HTLs) with different MoO3-ammonia ratios were prepared and characterized. For PeLEDs with one-step spin-coated CH3NH3PbBr3 emitter, an optimal MoO3-ammonia volume ratio (0.02) in PEDOT:PSS/MoO3-ammonia composite HTL presented a maximum luminance of 1082 cd/m2 and maximum current efficiency of 0.7 cd/A, which are 82% and 94% higher than those of the control device using pure PEDOT:PSS HTL respectively. It can be explained by that the optimized amount of MoO3-ammonia in the composite HTLs cannot only facilitate hole injection into CH3NH3PbBr3 through reducing the contact barrier, but also suppress the exciton quenching at the HTL/CH3NH3PbBr3 interface. Three-step spin coating method was further used to obtain uniform and dense CH3NH3PbBr3 films, which lead to a maximum luminance of 5044 cd/m2 and maximum current efficiency of 3.12 cd/A, showing enhancement of 750% and 767% compared with the control device respectively. The significantly improved efficiency of PeLEDs using three-step spin-coated CH3NH3PbBr3 film and an optimum PEDOT:PSS/MoO3-ammonia composite HTL can be explained by the enhanced carrier recombination through better hole injection and film morphology optimization, as well as the reduced exciton quenching at HTL/CH3NH3PbBr3 interface. These results present a promising strategy for the device engineering of high efficiency PeLEDs.