RESUMO
Ammonia (NH3) is widely used in various fields, and it is also considered a promising carbon free energy carrier, due to its high hydrogen content. The nitrogen reduction reaction (NRR), which converts nitrogen into ammonia by using protons from water as the hydrogen source, is receiving a lot of attention, since effective process optimization would make it possible to overcome the Haber-Bosch method. In this study, we used a solution-based approach to obtain functionalized porous Ni foam substrates with a small amount of gold (<0.1 mg cm-1). We investigated several deposition conditions and obtained different morphologies. The electrochemical performance of various catalysts on the hydrogen evolution reaction (HER) and NRR has been characterized. The ammonia production yield was determined by chronoamperometry experiments at several potentials, and the results showed a maximum ammonia yield rate of 20 µg h-1 mgcat-1 and a Faradaic efficiency of 5.22%. This study demonstrates the potential of gold-based catalysts for sustainable ammonia production and highlights the importance of optimizing deposition conditions to improve the selectivity toward HER.
RESUMO
The electrochemical synthesis of ammonia through the nitrogen reduction reaction (NRR) is receiving much attention, since it is considered a promising alternative to the Haber-Bosch process. In NRR experiments, a Nafion membrane is generally adopted as a separator. However, its use is controversial since ammonia can be trapped in the membrane, to some extent, or even pass through it. We systematically investigate the interaction of a Nafion membrane with ammonia and with an electrolyte and compare it with Zirfon as a possible alternative separator. We show that Nafion containing ammonia can easily release it when immersed in a 0.1 M Na2SO4 ammonia-free electrolyte, due to the cation exchange mechanism (Na+-NH4+). Since Na2SO4 is a commonly adopted electrolyte for NRR experiments, this may cause serious measurement errors and non-reproducible results. The same experiments performed using the polysulfone Zirfon separator clearly show that it is immune to interactions with ammonia, because of its different ion conduction mechanism. The findings provide a deeper understanding of the choice of membrane and electrolyte to be adopted for NRR tests, and may allow one to obtain more accurate and reliable results.
RESUMO
The morphology of gold nanoparticles (AuNPs) deposited on a (100) silicon wafer by simple immersion in a solution containing a metal salt and hydrofluoric acid (HF) is altered by HF treatment both before and after deposition. The gold clusters are characterized by the presence of flat regions and quasispherical particles consistent with the layer-by-layer or island growth modes, respectively. The cleaning procedure, including HF immersion prior to deposition, affects the predominantly occurring gold structures. Flat regions, which are of a few tens of nanometers long, are present after immersion for 10 s. The three-dimensional (3D) clusters are formed after a cleaning procedure of 4 min, which results in a large amount of spherical particles with a diameter of ≈15 nm and in a small percentage of residual square layers of a few nanometers in length. The samples were also treated with HF after the deposition and we found out a general thickening of flat regions, as revealed by TEM and AFM analysis. This result is in contrast to the coalescence observed in similar experiments performed with Ag. It is suggested that the HF dissolves the silicon oxide layer formed on top of the thin flat clusters and promotes the partial atomic rearrangement of the layered gold atoms, driven by a reduction of the surface energy. The X-ray diffraction investigation indicated changes in the crystalline orientation of the flat regions, which partially lose their initially heteroepitaxial relationship with the substrate. A postdeposition HF treatment for almost 70 s has nearly the same effect of long duration, high temperature annealing. The process presented herein could be beneficial to change the spectral response of nanoparticle arrays and to improve the conversion efficiency of hybrid photovoltaic devices.